RESUMEN
esumen Objetivo:
Comparar la microdureza de dos materiales endodónticos a base de silicato de calcio MTA Densell Endo Sealer y TotalFill BC Sealer. Materiales ymétodos:
Se evaluó la microdureza de los selladores MTA Densell Endo Sealer (Grupo 1, n=5) y To- talFill BC Sealer (Grupo 2, n=5) contenidos en cilindros de dentina de vacuno a los 14 días posteriores a su fraguado. La medición se realizó a temperatura ambiente mediante la prue- ba de indentación Vickers. Se realizaron cinco indentaciones por probeta con una carga de 100 g durante 10 s cada una. Las mediciones se convirtieron a valores de dureza Vickers (HV) y los promedios de los valores HV de cada grupo se compararon por medio de la prueba t de Student con un nivel de significación de P <0,05.Resultados:
A los 14 días, luego del fraguado, la mi- crodureza de MTA Densell Endo Sealer fue significativamen- te mayor (P=0,001) que la de TotalFill BC Sealer.Conclusiones:
Los resultados sugieren que a causa de su dureza la remoción de MTA Densell Endo Sealer puede resultar dificultosa cuando está indicado un retratamiento (AU)ABSTRACT
Aim:
To compare the microhardness of two silicate-based endodontic materials MTA Densell Endo Sealer and Total Fill BC Sealer. Materials andmethods:
Samples of MTA Densell Endo Sealer (Group 1, n=5) and Total Fill BC Sealer (Group 2, n=5) contained into cow dentine cylinders were subjected to the Vickers Microhardness Indentation test at room temper- ature and 14 days after setting. Five indentations per sample were performed under a load of 100 g for 10 s. The indenta- tion measurements were converted into hardness values (HV). Mean HV values of each group were compared using the Stu- dent t test at a significance level of P <0,05.Results:
14 days after setting, the microhardness of MTA Densell Endo Sealer was significantly greater (P=0,001) than that of Total Fill BC Sealer.Conclusions:
The results of this study suggest that due to its hardness the removal of MTA Densell Endo Sealer could be difficult to perform when a root canal retreatment is indicated (AU)Key words
النص الكامل:
1
الفهرس:
LILACS
الموضوع الرئيسي:
Root Canal Filling Materials
/
Silicate Cement
/
Hardness Tests
اللغة:
Es
مجلة:
Rev. Asoc. Odontol. Argent
موضوع المجلة:
ODONTOLOGIA
السنة:
2021
نوع:
Article