Corrosion resistance of Ti-Cu alloy / 中华口腔医学杂志
Chinese Journal of Stomatology
; (12): 565-568, 2010.
Article
Dans Zh
| WPRIM
| ID: wpr-243142
Responsable en Bibliothèque :
WPRO
ABSTRACT
<p><b>OBJECTIVE</b>to investigate the corrosion behavior of Ti-Cu alloy in 0.9%NaCl solution and in acidified 0.9%NaCl solution.</p><p><b>METHODS</b>the microstructure of Ti-Cu alloys were characterized by means of X-ray diffraction (XRD). The electrochemical behavior of Ti-Cu alloy in two solutions (namely 0.9%NaCl solution and acidified 0.9%NaCl solution) was tested. Commercial pure Ti and 316L stainless steel were used as control.</p><p><b>RESULTS</b>Ti-Cu alloys were composed by α-Ti and Ti(2)Cu intermetallic compound. After 3500 s immersion, the open circuit potential (OCP) values of pure Ti, Ti-5Cu alloy and Ti-10Cu alloy in 0.9% NaCl solution were -188, -181 and -173 mV, respectively. In 0.9% NaCl solution with lactic acid added, the OCP values were -143, -158 and -109 mV, respectively. In potentiodynamic polarization tests, the passive current densities of pure Ti and Ti-5Cu alloys were about 20 µA/cm(2). However, 316L stainless steel experienced pitting corrosion.</p><p><b>CONCLUSIONS</b>it was possible to establish the following relation for their corrosion resistances pure Ti≈Ti-5Cu > Ti-10Cu > 316L stainless steel. The addition of lactic acid in the solution did not compromise the corrosion resistance of Ti-Cu alloys.</p>
Texte intégral:
1
Indice:
WPRIM
Sujet Principal:
Acier inoxydable
/
Titane
/
Diffraction des rayons X
/
Test de matériaux
/
Corrosion
/
Alliage dentaire
/
Alliages
langue:
Zh
Texte intégral:
Chinese Journal of Stomatology
Année:
2010
Type:
Article