In vitro characterization of a novel resin-based restorative material containing alkaline fillers
J. appl. oral sci
; 32: e20230219, 2024. tab, graf
Article
em En
|
LILACS-Express
| LILACS
| ID: biblio-1528890
Biblioteca responsável:
BR1.1
ABSTRACT
Abstract Objective:
In this study, a comparative evaluation of the physicochemical properties of Cention N and other direct restorative materials was performed. Three restorative materials—a resin-modified glass ionomer (Fuji II LC), an alkasite-based resinous material (Cention N), and a resin composite (Tetric N Ceram)—were characterized in terms of degree of conversion, Knoop hardness number (KHN) ratio, flexural strength, elastic modulus, water sorption, water solubility, microshear bond strength to dentin, immediate microleakage, and radiopacity.Methodology:
The microshear bond strength to dentin and microleakage of Cention N were evaluated with and without the application of an adhesive system (Tetric N Bond Universal). A one-way ANOVA test was used to analyze the data in terms of degree of conversion, KHN ratio, water sorption, water solubility, microshear bond strength to dentin, and radiopacity. A two-way ANOVA test (carried out considering the material type and ethanol aging as factors) was used to analyze the data in terms of flexural strength and elastic modulus. The Kruskal-Wallis test was used to statistically analyze the data on microleakage. A significance level of α=0.05 was used for all tests.Results:
Fuji II LC was found to have the highest degree of conversion, water sorption, and microleakage, as well as the lowest flexural strength. Cention N had the highest solubility; when used with an adhesive system, it achieved bond strength and microleakage similar to those of the Tetric N Ceram composite. Tetric N Ceram had the highest degree of conversion, KHN ratio, and radiopacity.Conclusion:
The properties of Cention N validate its efficacy as an alternative direct restorative material when used in conjunction with an adhesive system.