Comparación de la microfiltración apical de cuatro tipos de cementos endodónticos: Endofill, mtaFillapex, Adseal y Roeko Seal / Comparison of the Apical Microleakage of Four Types Of Endodontic Cements: Endofill, mta Fillapex, Adseal and Roeko Seal / Comparação da microinfiltração apical de quatro tipos de cimentos endodônticos: Endofill, mta Fillapex, Adseal e Roeko seal

RESUMEN

Introducción: La microfiltración apical es uno de los principales causantes de fracasos endodónticos donde hay invasión de bacterias y líquidos periapicales a la parte interna del conducto radicular y material de relleno. Materiales y Métodos: La muestra estuvo conformada por 60 dientes premolares unirradiculares que fueron seccionados en la unión amelocementaria, la instrumentación biomecánica se realizó con técnica rotatoria e irrigación con hipoclorito de sodio al 5.25% y EDTA 17%, se dividió aleatoriamente en 4 grupos (n=15) para cada tipo de cemento, la obturación se realizó con la técnica de condensación lateral, a nivel coronal se obturó con Ionómero vidrio base y resina, se colocaron en una incubadora a 37° sumergidos en NaCL 0.9% por 5 días hasta el fraguado de los cementos, para observar la microfiltración se utilizó el método filtración de tinta china y la diafanización con la técnica de Robertson. Las medidas de microfiltración apical se observaron utilizando el Estereomicroscopio. Resultados: El valor promedio fue menor para el cemento Adseal 0,33mm, seguido por los cementos Fillapex 0,87mm, Roeko seal 1,00mm y Endofill 1,30mm respectivamente. Hubo diferencias estadísticamente significativas en la microfiltración apical de los cuatro cementos endodónticos (p=0.00) Conclusiones: El cemento Adseal presentó menor microfiltración en comparación a los cementos Fillapex, Roeko seal y Endofill.

ABSTRACT

Introduction: Apical microleakage is one of the main causes of endodontic failure, either due to invasion of microorganisms or periapical fluids into the canal, and only the composition of the type of obturator cement favors its reduction. The objective of this research was to compare the apical microleakage of four types of endodontic cements Endofill, MTA Fillapex, Adseal and Roeko Seal. Materials and methods: The sample consisted of 60 single root premolar teeth that were sectioned at the cement- enamel junction, the biomechanical instrumentation was performed with a rotary technique and irrigation with sodium hypochlorite and edta, randomly divided into 4 groups (n = 15) for each type of cement, the obturation was performed with the lateral condensation technique, at the coronal level it was obturated with base glass ionomer and resin, they were placed in an incubator at 37° submerged in NaCL 0.9% for 5 days until setting. of the cements, to observe the microleakage the India ink filtration method was used and diaph-anization with the Robertson technique. Apical microleakage measurements were observed using the Stereomicroscope. Results: The average value was lower for the Adseal 0.33 mm cement, followed by the Fillapex 0.87 mm, Roeko Seal 1.00 mm and Endofill 1.30 mm cements respectively. There were sta-tistically significant differences in the apical microleakage of the four endodontic cements (p = 0.00) Conclusions: Adseal cement presented less microfiltration compared to Fillapex, Roeko Seal and Endofill cements

RESUMO

Introdução: a microinfiltração apical é uma das principais causas de falhas endodônticas onde há inva-são de microrganismos e líquidos periapicais ao interior do conducto e só a composição do tipo de cimento obturador favorece sua disminuição. O objetivo desta pesquisa foi comparar a microinfiltração apical de quatro tipos de cimentos endodônticos Endofill, MTA Fillapex, Adseal e Roeko Seal. Materiais e métodos: a amostra foi composta por 60 dentes pré-molares uniradiculares que foram seccionados na junção amelocementária. A instrumentação biomecânica foi realizada com técnica rotatória e irrigação com hipoclorito e edta, sendo dividida aleatoriamente em 4 grupos (n = 15) para cada tipo de cimento. A obturação foi realizada pela técnica de condensação lateral, no nível coronal foi obturado com base de ionômero de vidro e resina, foram colocados em incubadora a 37° submersos em NaCl 0,9% por 5 dias até a pega dos cimentos. Para observar a microfiltração utilizou-se o método de filtração em tinta nan-quim e diafanização pela técnica de Robertson. As medidas de microinfiltração apical foram observadas utilizando o estereomicroscópio. Resultados: o valor médio foi menor para o cimento Adseal (0,33 mm), seguido pelos cimentos Fillapex (0,87 mm), Roeko Seal (1,00 mm) e Endofill (1,30 mm), respectivamente. Houve diferenças estatisticamente significativas na microinfiltração apical dos quatro cimentos endo-dônticos (p = 0,00). Conclusões: o cimento Adseal apresentou menor microinfiltração comparado aos cimentos Fillapex, Roeko seal e Endofill.