Silorane- and high filled-based"low-shrinkage" resin composites: shrinkage, flexural strength and modulus
Brazilian Oral Research; Arrais, Cesar Augusto Galvão; Oliveira, Marcelo Tavares de; Mettenburg, Donald; Rueggeberg, Frederick Allen; Giannini, Marcelo.
Afiliação
  • Arrais, Cesar Augusto Galvão; Univ Estadual de Ponta Grossa -UEPG. Department of Operative Dentistry. Ponta Grossa. BR
  • Oliveira, Marcelo Tavares de; Univ Estadual de Ponta Grossa -UEPG. Department of Operative Dentistry. Ponta Grossa. BR
  • Mettenburg, Donald; Univ Estadual de Ponta Grossa -UEPG. Department of Operative Dentistry. Ponta Grossa. BR
  • Rueggeberg, Frederick Allen; Univ Estadual de Ponta Grossa -UEPG. Department of Operative Dentistry. Ponta Grossa. BR
  • Giannini, Marcelo; Univ Estadual de Ponta Grossa -UEPG. Department of Operative Dentistry. Ponta Grossa. BR
Braz. oral res ; 27(2): 97-102, Mar-Apr/2013. tab, graf
Article em En | LILACS | ID: lil-668002
Biblioteca responsável: BR1.1
ABSTRACT
This study compared the volumetric shrinkage (VS), flexural strength (FS) and flexural modulus (FM) properties of the low-shrinkage resin composite Aelite LS (Bisco) to those of Filtek LS (3M ESPE) and two regular dimethacrylate-based resin composites, the microfilled Heliomolar (Ivoclar Vivadent) and the microhybrid Aelite Universal (Bisco). The composites (n = 5) were placed on the Teflon pedestal of a video-imaging device, and VS was recorded every minute for 5 min after 40 s of light exposure. For the FS and FM tests, resin discs (0.6 mm in thickness and 6.0 mm in diameter) were obtained (n = 12) and submitted to a piston-ring biaxial test in a universal testing machine. VS, FS, and FM data were submitted to two-way repeated measures and one-way ANOVA, respectively, followed by Tukey's post-hoc test (a = 5%). Filtek LS showed lower VS than did Aelite LS, which in turn showed lower shrinkage than did the other composites. Aelite Universal and Filtek LS exhibited higher FS than did Heliomolar and Aelite LS, both of which exhibited the highest FM. No significant difference in FM was noted between Filtek LS and Aelite Universal, while Heliomolar exhibited the lowest values. Aelite LS was not as effective as Filtek LS regarding shrinkage, although both low-shrinkage composites showed lower VS than did the other composites. Only Filtek LS exhibited FS and FM comparable to those of the regular microhybrid dimethacrylate-based resin composite.
Assuntos
Palavras-chave

Texto completo: 1 Índice: LILACS Assunto principal: Poliuretanos / Resinas Acrílicas / Resinas Compostas / Resinas de Silorano / Metacrilatos Limite: Humans Idioma: En Revista: Braz. oral res Assunto da revista: ODONTOLOGIA Ano de publicação: 2013 Tipo de documento: Article / Project document

Texto completo: 1 Índice: LILACS Assunto principal: Poliuretanos / Resinas Acrílicas / Resinas Compostas / Resinas de Silorano / Metacrilatos Limite: Humans Idioma: En Revista: Braz. oral res Assunto da revista: ODONTOLOGIA Ano de publicação: 2013 Tipo de documento: Article / Project document