ABSTRACT
To investigate the effect of captopril on the dentin bonding durability of self-etch adhesive. Different concentrations of captopril ethanol solutions or captopril ethanol/water solutions were prepared to pretreat dentin as primer for the self-etch adhesives. The surface morphology of the dentin was observed with scanning electron microscopy (SEM). Based on the morphology analysis, the pretreatment condition was selected and two self-etch adhesives were employed to evaluate the improvement effect of the captopril pretreatment on the dentin bonding durability. : SEM showed that the pretreatment of captopril ethanol solutions and captopril ethanol/water solutions were able to remove the smear lay and partially expose collagen matrix. According to the SEM results, the pretreating condition of captopril ethanol/water solution with the pretreating time of was selected for further dentin bonding study. For Clearfil SEBOND system, the immediate bonding strength increased from to (0.05]. For Clearfil S BOND system, there was no significant difference in the immediate bonding strength between the experimental group [(4.07) MPa] and the control group[(4.11) MPa]. But after one-year aging, the bonding strength of the experimental group was higher than that of the control group <0.05]. : The pretreatment with captopril ethanol/water solution increases the dentin bonding strength of the self-etch adhesive systems and also improves the bonding durability.
Palavras-chave
Texto completo:
1
Índice:
WPRIM
Assunto principal:
Teste de Materiais
/
Captopril
/
Microscopia Eletrônica de Varredura
/
Adesivos
/
Colagem Dentária
/
Adesivos Dentinários
/
Cimentos de Resina
/
Dentina
Idioma:
En
Revista:
Journal of Zhejiang University. Medical sciences
Ano de publicação:
2021
Tipo de documento:
Article