ABSTRACT
There is growing emphasis on developing green composites as a substitute for oil-based materials. In the pursuit of studying and enhancing the mechanical properties of these composites, tensile tests are predominantly employed, often overlooking the flexural properties. This study focuses on researching the flexural properties of abaca-fiber-reinforced bio-based high-density polyethylene (BioPE) composites. Specifically, composites containing 30 wt% of abaca fiber (AF) were treated with a coupling agent based on polyethylene functionalized with maleic acid (MAPE). The test results indicate that incorporating 8 wt% of the coupling agent significantly improved the flexural strength of the composites. Thereafter, composites with AF content ranging from 20 to 50 wt% were produced and subjected to flexural testing. It was observed that flexural strength was positively correlated with AF content. A micromechanics analysis was conducted to evaluate the contributions of the phases. This analysis involved assessing the mechanical properties of both the reinforcement and matrix to facilitate the modeling of flexural strength. The findings of this study demonstrate the feasibility of replacing oil-based matrices, such as high-density polyethylene (HDPE), with fully bio-based composites that exhibit comparable flexural properties to their oil-based counterparts.
ABSTRACT
Composites from polypropylene (PP) reinforced with hemp strands (HS) are prepared in the current work with the aim of deepening on the influence of this reinforcement on the impact performance of these specific composites. Despite all the research conducted in this field, the effect of this natural reinforcement on the absorbed energy during crack formation and propagation is not fully tackled in previous research works. From the methodology and samples' geometry, the results concluded that the quality of the interface has a noticeable role in the impact resistance of these materials. The interface strength, fiber dispersion and fiber pullout are the main contributors to crack formation, whereas fiber pullout is the main one responsible for crack propagation. Maximum values of absorbed energy were found for PP composites comprising 20-30 wt% of HS and 8 wt% of the coupling agent for the un-notched samples, whereas maximum absorbed energy values corresponded to PP composites with 40 wt% of HS and 4 wt% of coupling agent for the notched samples. The water-absorption behavior in different humid environments is also examined. From the kinetic study, the water diffusion followed a Fickean behavior showing low-diffusion coefficients, increasing with fiber content. This systematic investigation represents a contribution to the analysis of the potential of reinforcing conventional polymers with natural materials, as a strategy towards more sustainable development.
ABSTRACT
Composite materials containing natural reinforcement fibers, generally called biocomposites, have attracted the interest of both researchers and manufacturers, but the most environmentally advantageous combinations include a bio-based matrix, as well. With this in mind, a poly(lactic acid) (PLA) matrix was reinforced with natural fibers from hemp, both untreated strands (UHSs) and soda-bleached fibers (SBHFs). The preparation of the subsequent fully bio-sourced, discontinuously reinforced composites involved kinetic mixing, intensive single-screw extrusion, milling, and injection molding. Up to a fiber content of 30 wt%, the tensile modulus increased linearly with the volume fraction of the dispersed phase. Differences between SBHFs (up to 7.6 Gpa) and UHSs (up to 6.9 Gpa) were hardly significant (p = 0.1), but SBHF-reinforced composites displayed higher strain at failure. In any case, for the same fiber load (30 wt%), the Young's modulus of PLA/hemp biocomposites was greater than that of glass fiber (GF)-reinforced polypropylene (5.7 GPa), albeit lower than that of PLA/GF (9.8 GPa). Considering all the measurements, the contribution of each phase was analyzed by applying the Hirsch model and the Tsai-Pagano model. As a concluding remark, although the intrinsic tensile modulus of SBHFs was lower than that of GF, the efficiency of those natural fibers as reinforcement (according to the rule of mixtures) was found to be higher.