Bioaccessibility of nickel and cobalt in powders and massive forms of stainless steel, nickel- or cobalt-based alloys, and nickel and cobalt metals in artificial sweat.

Nickel (Ni) and cobalt (Co) are the most common metal allergens upon skin contact at occupational settings and during consumer handling of metals and alloys. A standardized test (EN, 1811) exists to assess Ni release from articles of metals and alloys in massive forms intended for direct and prolonged skin contact, but no corresponding test exists for other materials such as powders or massive forms of alloys placed on the market or to determine the release of Co, for which only limited data is available. Differences in Ni and Co release from massive forms of a range of common stainless steels and some high-alloyed grades compared to Ni and Co metals were therefore assessed in artificial sweat for 1 week at 30 °C according to EN 1811. A comparable modified test procedure was elaborated and used for powders and some selected massive alloys. All alloys investigated released significantly less amount of Ni (100-5000-fold) and Co (200-400,000-fold) compared with Ni and Co metal, respectively. Almost all alloys showed a lower bioaccessible concentration (0.007-6.8 wt% Ni and 0.00003-0.6 wt% Co) when compared to corresponding bulk alloy contents (0.1-53 wt% Ni, 0.02-65 wt% Co). Observed differences are, among other factors, related to differences in bulk composition and to surface oxide characteristics. For the powders, less Ni and Co were released per surface area, but more per mass, compared to the corresponding massive forms.

Surface passivity largely governs the bioaccessibility of nickel-based powder particles at human exposure conditions.

The European chemical framework REACH requires that hazards and risks posed by chemicals, including alloys and metals, are identified and proven safe for humans and the environment. Therefore, differences in bioaccessibility in terms of released metals in synthetic biological fluids (different pH (1.5-7.4) and composition) that are relevant for different human exposure routes (inhalation, ingestion, and dermal contact) have been assessed for powder particles of an alloy containing high levels of nickel (Inconel 718, 57 wt% nickel). This powder is compared with the bioaccessibility of two nickel-containing stainless steel powders (AISI 316L, 10-12% nickel) and with powders representing their main pure alloy constituents: two nickel metal powders (100% nickel), two iron metal powders and two chromium metal powders. X-ray photoelectron spectroscopy, microscopy, light scattering, and nitrogen absorption were employed for the particle and surface oxide characterization. Atomic absorption spectroscopy was used to quantify released amounts of metals in solution. Cytotoxicity (Alamar blue assay) and DNA damage (comet assay) of the Inconel powder were assessed following exposure of the human lung cell line A549, as well as its ability to generate reactive oxygen species (DCFH-DA assay). Despite its high nickel content, the Inconel alloy powder did not release any significant amounts of metals and did not induce any toxic response. It is concluded, that this is related to the high surface passivity of the Inconel powder governed by its chromium-rich surface oxide. Read-across from the pure metal constituents is hence not recommended either for this or any other passive alloy.

Adsorption of lysozyme on silver and its influence on silver release.

Silver is increasingly used in antimicrobial coatings of biomedical devices and implants to hinder infections. As proteins have been shown to largely influence the extent of released metals from various metal surfaces at biological conditions, silver may also be influenced in the same way. The aim of this study is to relate the structure of adsorbed lysozyme (LSZ) to the release of silver from metallic silver surfaces. Simultaneous adsorption measurements were performed in real time on the same surface using combined ellipsometry and quartz crystal microbalance with dissipation monitoring measurements to provide a more comprehensive understanding on the adsorption kinetics and the layer structures. The concentration of LSZ in 0.15 M NaNO3 solution (pH 7, 25 °C) influences the structure of the adsorbed layer. Monolayer coverage is obtained at concentrations ≤0.1 g/L, while a bilayer structure with a rigid inner layer and a relatively loosely adsorbed outer layer is formed at 1 g/L. The inner layer of LSZ is assumed to bind firmly to silver via disulfide bridges, which makes it irreversibly adsorbed with respect to dilution. The amount of released silver is further influenced by the structure of the LSZ layer. At low LSZ concentrations (≤0.1 g/L) the amount of released silver is not significantly different compared with non-protein-containing NaNO3 solutions; however, noticeable reduction was observed at higher concentrations (1 g/L). This reduction in silver release has several possible explanations, including (i) surface complexation between LSZ and silver ions that may result in the incorporation of silver in the irreversible adsorbed layer and, hence, reduce the amount of released silver into solution, and (ii) net charge reversal at the protein/solution interface to slightly positive surface potentials. Any release of silver will therefore exhibit an electrostatic repulsion during transportation through the protein layer results in a reduced amount of silver in solution.

Critical review: Copper runoff from outdoor copper surfaces at atmospheric conditions.

This review on copper runoff dispersed from unsheltered naturally patinated copper used for roofing and facades summarizes and discusses influencing factors, available literature, and predictive models, and the importance of fate and speciation for environmental risk assessment. Copper runoff from outdoor surfaces is predominantly governed by electrochemical and chemical reactions and is highly dependent on given exposure conditions (size, inclination, geometry, degree of sheltering, and orientation), surface parameters (age, patina composition, and thickness), and site-specific environmental conditions (gaseous pollutants, chlorides, rainfall characteristics (amount, intensity, pH), wind direction, temperature, time of wetness, season). The corrosion rate cannot be used to assess the runoff rate. The extent of released copper varies largely between different rain events and is related to dry and wet periods, dry deposition prior to the rain event and prevailing rain and patina characteristics. Interpretation and use of copper runoff data for environmental risk assessment and management need therefore to consider site-specific factors and focus on average data of long-term studies (several years). Risk assessments require furthermore that changes in copper speciation, bioavailability aspects, and potential irreversible retention on solid surfaces are considered, factors that determine the environmental fate of copper runoff from outdoor surfaces.

Inter-laboratory validation of bioaccessibility testing for metals.

Bioelution assays are fast, simple alternatives to in vivo testing. In this study, the intra- and inter-laboratory variability in bioaccessibility data generated by bioelution tests were evaluated in synthetic fluids relevant to oral, inhalation, and dermal exposure. Using one defined protocol, five laboratories measured metal release from cobalt oxide, cobalt powder, copper concentrate, Inconel alloy, leaded brass alloy, and nickel sulfate hexahydrate. Standard deviations of repeatability (sr) and reproducibility (sR) were used to evaluate the intra- and inter-laboratory variability, respectively. Examination of the sR:sr ratios demonstrated that, while gastric and lysosomal fluids had reasonably good reproducibility, other fluids did not show as good concordance between laboratories. Relative standard deviation (RSD) analysis showed more favorable reproducibility outcomes for some data sets; overall results varied more between- than within-laboratories. RSD analysis of sr showed good within-laboratory variability for all conditions except some metals in interstitial fluid. In general, these findings indicate that absolute bioaccessibility results in some biological fluids may vary between different laboratories. However, for most applications, measures of relative bioaccessibility are needed, diminishing the requirement for high inter-laboratory reproducibility in absolute metal releases. The inter-laboratory exercise suggests that the degrees of freedom within the protocol need to be addressed.

New UK nickel-plated steel coins constitute an increased allergy and eczema risk.

BACKGROUND: Nickel-plated steel coins have recently been introduced in the United Kingdom. OBJECTIVES: To compare the performance and allergy risk of the new nickel-plated coins (five and ten pence) with those of the cupro-nickel coins being replaced. MATERIALS AND METHODS: Coin handling studies with assessment of skin exposure and metal release in artificial sweat were performed. Six volunteers participated. RESULTS: The amount of nickel deposited onto skin during the handling of nickel-plated coins for 1 hr was 7.5 µg/cm(2) , four times higher than that from cupro-nickel coins. The nickel content in the oxidized surface of nickel-plated coins was higher, explaining the higher skin dose. Initial nickel release rates were 10-27 times higher than 1-week rates, emphasizing that brief and repeated contact results in significant nickel exposure. CONCLUSIONS: Nickel-plated coins deposit higher levels of nickel onto skin than cupro-nickel coins, and hence pose an increased allergy risk. One-week release in artificial sweat is not suitable for determining the risk of handling items with high nickel release that come into short, repeated contact with the skin. The nickel skin dose is recommended for risk assessment. UK citizens are now, because of this change in coinage, unnecessarily exposed to higher levels of nickel on the skin. This is of public health concern.

Characterization and Toxic Potency of Airborne Particles Formed upon Waste from Electrical and Electronic Equipment Waste Recycling: A Case Study.

Manual dismantling, shredding, and mechanical grinding of waste from electrical and electronic equipment (WEEE) at recycling facilities inevitably lead to the accidental formation and release of both coarse and fine particle aerosols, primarily into the ambient air. Since diffuse emissions to air of such WEEE particles are not regulated, their dispersion from the recycling plants into the adjacent environment is possible. The aim of this interdisciplinary project was to collect and characterize airborne WEEE particles smaller than 1 µm generated at a Nordic open waste recycling facility from a particle concentration, shape, and bulk and surface composition perspective. Since dispersed airborne particles eventually may reach rivers, lakes, and possibly oceans, the aim was also to assess whether such particles may pose any adverse effects on aquatic organisms. The results show that WEEE particles only exerted a weak tendency toward cytotoxic effects on fish gill cell lines, although the exposure resulted in ROS formation that may induce adverse effects. On the contrary, the WEEE particles were toxic toward the crustacean zooplankter Daphnia magna, showing strong effects on survival of the animals in a concentration-dependent way.

Mechanistic insight on the combined effect of albumin and hydrogen peroxide on surface oxide composition and extent of metal release from Ti6Al4V.

The titanium-aluminium (6 wt%)-vanadium (4 wt%) (Ti6Al4V) alloy is widely used as an orthopedic and dental implant material due to its high corrosion resistance in such environments. The corrosion resistance is usually determined by means of electrochemical methods, which may not be able to detect other chemical surface reactions. Literature findings report a synergistic effect of the combination of the abundant protein albumin and hydrogen peroxide (H2 O2 ) on the extent of metal release and corrosion of Ti6Al4V. The objectives of this study were to gain further mechanistic insight on the interplay of H2 O2 and albumin on the metal release process of Ti6Al4V with special focus on (1) kinetics and (2) H2 O2 and albumin concentrations. This was accomplished mainly by metal release and surface oxide composition investigations, which confirmed the combined effect of H2 O2 and albumin on the metal release process, although not detectable by electrochemical open circuit potential measurements. A concentration of 30 mM H2 O2 induced substantial changes in the surface oxide characteristics, an oxide which became thicker and enriched in aluminum. Bovine serum albumin (BSA) seemed to be able to deplete this aluminum content from the outermost surface or at least to delay its surface enrichment. This effect increased with increased BSA concentration, and for time periods longer than 24 h. This study hence suggests that short-term (accelerated) corrosion resistance measurements are not sufficient to predict potential health effects of Ti6Al4V alloys since also chemical dissolution mechanisms play a large role for metal release, possibly in a synergistic way. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 855-867, 2019.

Corrosion-induced release of the main alloying constituents of manganese-chromium stainless steels in different media.

The main focus of this paper is the assessment of release rates of chromium, nickel, iron and manganese from manganese-chromium stainless steel grades of low nickel content. The manganese content varied between 9.7 and 1.5 wt% and the corresponding nickel content between 1 and 5 wt%. All grades were exposed to artificial rain and two were immersed in a synthetic body fluid of similar pH but of different composition and exposure conditions. Surface compositional studies were performed using X-ray photoelectron spectroscopy (XPS) in parallel to correlate the metal release process with changes in surface oxide properties. All grades, independent of media, revealed a time-dependent metal release process with a preferential low release of iron and manganese compared to nickel and chromium while the chromium content of the surface oxide increased slightly. Manganese was detected in the surface oxide of all grades, except the grade of the lowest manganese bulk content. No nickel was observed in the outermost surface oxide. Stainless steel grades of the lowest chromium content (approximately 16 wt%) and highest manganese content (approximately 7-9 wt%), released the highest quantity of alloy constituents in total, and vice versa. No correlation was observed between the release rate of manganese and the alloy composition. Released main alloy constituents were neither proportional to the bulk alloy composition nor to the surface oxide composition.

Surface-rain interactions: differences in copper runoff for copper sheet of different inclination, orientation, and atmospheric exposure conditions.

Predictions of the diffuse dispersion of metals from outdoor constructions such as roofs and facades are necessary for environmental risk assessment and management. An existing predictive model has been compared with measured data of copper runoff from copper sheets exposed at four different inclinations facing four orientations at two different urban sites (Stockholm, Sweden, and Milan, Italy) during a 4-year period. Its applicability has also been investigated for copper sheet exposed at two marine sites(Cadiz, Spain, for 5 years, and Brest, France, for 9 years). Generally the model can be used for all given conditions. However, vertical surfaces should be considered as surfaces inclined 60-80 due to wind driven effects. The most important parameters that influence copper runoff, and not already included in the model, are the wind and rain characteristics that influence the actual rainfall volume impinging the surface of interest.

Release of Si from silicon, a ferrosilicon (FeSi) alloy and a synthetic silicate mineral in simulated biological media.

Unique quantitative bioaccessibility data has been generated, and the influence of surface/material and test media characteristics on the elemental release process were assessed for silicon containing materials in specific synthetic body fluids at certain time periods at a fixed loading. The metal release test protocol, elaborated by the KTH team, has previously been used for classification, ranking, and screening of different alloys and metals. Time resolved elemental release of Si, Fe and Al from particles, sized less than 50 µm, of two grades of metallurgical silicon (high purity silicon, SiHG, low purity silicon, SiLG), an alloy (ferrosilicon, FeSi) and a mineral (aluminium silicate, AlSi) has been investigated in synthetic body fluids of varying pH, composition and complexation capacity, simple models of for example dermal contact and digestion scenarios. Individual methods for analysis of released Si (as silicic acid, Si(OH)4) in synthetic body fluids using GF-AAS were developed for each fluid including optimisation of solution pH and graphite furnace parameters. The release of Si from the two metallurgical silicon grades was strongly dependent on both pH and media composition with the highest release in pH neutral media. No similar effect was observed for the FeSi alloy or the aluminium silicate mineral. Surface adsorption of phosphate and lactic acid were believed to hinder the release of Si whereas the presence of citric acid enhanced the release as a result of surface complexation. An increased presence of Al and Fe in the material (low purity metalloid, alloy or mineral) resulted in a reduced release of Si in pH neutral media. The release of Si was enhanced for all materials with Al at their outermost surface in acetic media.

Corrosion and runoff rates of Cu and three Cu-alloys in marine environments with increasing chloride deposition rate.

Bare copper sheet and three commercial Cu-based alloys, Cu15Zn, Cu4Sn and Cu5Al5Zn, have been exposed to four test sites in Brest, France, with strongly varying chloride deposition rates. The corrosion rates of all four materials decrease continuously with distance from the coast, i.e. with decreasing chloride load, and in the following order: Cu4Sn>Cu sheet>Cu15Zn>Cu5Al5Zn. The patina on all materials was composed of two main layers, Cu2O as the inner layer and Cu2(OH)3Cl as the outer layer, and with a discontinuous presence of CuCl in between. Additional minor patina constituents are SnO2 (Cu4Sn), Zn5(OH)6(CO3)2 (Cu15Zn and Cu5Al5Zn) and Zn6Al2(OH)16CO3·4H2O/Zn2Al(OH)6Cl·2H2O/Zn5Cl2(OH)8·H2O and Al2O3 (Cu5Al5Zn). The observed Zn- and Zn/Al-containing corrosion products might be important factors for the lower sensitivity of Cu15Zn and Cu5Al5Zn against chloride-induced atmospheric corrosion compared with Cu sheet and Cu4Sn. Decreasing corrosion rates with exposure time were observed for all materials and chloride loads and attributed to an improved adherence with time of the outer patina to the underlying inner oxide. Flaking of the outer patina layer was mainly observed on Cu4Sn and Cu sheet and associated with the gradual transformation of CuCl to Cu2(OH)3Cl of larger volume. After three years only Cu5Al5Zn remains lustrous because of a patina compared with the other materials that appeared brownish-reddish. Significantly lower release rates of metals compared with corresponding corrosion rates were observed for all materials. Very similar release rates of copper from all four materials were observed during the fifth year of marine exposure due to an outer surface patina that with time revealed similar constituents and solubility properties.

Risks of using membrane filtration for trace metal analysis and assessing the dissolved metal fraction of aqueous media--a study on zinc, copper and nickel.

Membrane filtration is commonly performed for solid-liquid separation of aqueous solutions prior to trace metal analysis and when assessing "dissolved" metal fractions. Potential artifacts induced by filtration such as contamination and/or adsorption of metals within the membrane have been investigated for different membrane materials, metals, applied pressures and pre-cleaning steps. Measurements have been conducted on aqueous solutions including well-defined metal standards, ultrapure water, and on runoff water from corroded samples. Filtration using both non-cleaned and pre-cleaned filters revealed contamination and adsorption effects, in particular pronounced for zinc, evident for copper but non-significant for nickel. The results clearly show these artifacts to be non-systematic both for non-cleaned and pre-cleaned membranes. The applied pressure was of minor importance. Measurements of the labile fraction by means of stripping voltammetry clearly elucidate that membrane filtration followed by total metal analysis cannot accurately assess the labile or the dissolved metal fraction.

Corrosion-induced release of Cu and Zn into rainwater from brass, bronze and their pure metals. A 2-year field study.

A 2-year field study has been conducted in an urban environment to provide annual release rates of copper and zinc from brass (20 wt% Zn) and copper and tin from bronze (6 wt% Sn) compared to sheets of their pure alloy constituents, copper and zinc. Despite relatively low nominal bulk alloy content, substantially more zinc was released from brass compared to copper. Both metals were released at a significantly slower rate from the brass alloy, compared to the pure metals. The proportion of release rates of copper and zinc from the alloy differed significantly from their proportions in the bulk alloy. Bronze showed relatively constant release rates of copper, being similar to that of pure copper sheet. The release of tin from bronze was negligible. The results clearly show that alloys and the pure metals behave very differently when exposed to rainwater. Accordingly, release rates from pure metals cannot be used to predict release rates of individual constituents from their alloys. Generated data are of importance within REACH, the new chemical policy of the European commission, where metal alloys erroneously are being treated as mixtures of chemical substances.