Formation of Stable Tin Perovskites Co-crystallized with Three Halides for Carbon-Based Mesoscopic Lead-Free Perovskite Solar Cells.

We synthesized and characterized methylammonium (MA) mixed tri-halide tin perovskites (MASnIBr2-x Clx ) for carbon-based mesoscopic solar cells free of lead and hole-transporting layers. Varied SnCl2 /SnBr2 ratios yielded tin perovskites with three halides (I, Br, and Cl) co-crystallized inside the tin-perovskite. When the SnCl2 proportion was ≥50 % (x≥1), phase separation occurred to give MASnI3-y Bry and MASnCl3-z Brz in the stoichiometric proportions of their precursors, confirmed by XRD. A device with MASnIBr1.8 Cl0.2 (SnCl2 =10 %) showed the best photovoltaic performance: JSC =14.0 mA cm-2 , VOC =380 mV, FF=0.573, and PCE=3.1 %, and long-term stability. Electrochemical impedance spectra (EIS) show superior charge recombination and dielectric relaxation properties for the MASnIBr1.8 Cl0.2 cell. Transient PL decays showed the intrinsic problem of tin-based perovskites with average lifetimes less than 100 ps.

Interfacial Engineering with Cross-Linkable Fullerene Derivatives for High-Performance Perovskite Solar Cells.

Two fullerene derivatives with styryl and oxetane cross-linking groups served as interfacial materials to modify an electron-transporting layer (ETL) of TiO2, doped with Au nanoparticles, processed under low-temperature conditions to improve the performance of perovskite solar cells (PSC). The cross-linkable [6,6]-phenyl-C61-butyric styryl dendron ester was produced via thermal treatment at 160 °C for 20 min, whereas the cross-linkable [6,6]-phenyl-C61-butyric oxetane dendron ester (C-PCBOD) was obtained via UV-curing treatment for 45 s. Both cross-linked fullerenes can passivate surface-trap states of TiO2 and have also excellent surface coverage on the TiO2 layer shown in the corresponding atomic force microscopy images. To improve the crystallinity of perovskite, we propose a simple co-solvent method involving mixing dimethylformamide (DMF) and dimethyl sulfoxide (DMSO) in a specific ratio (DMF/DMSO = 90/10). The fullerene derivative layer between the ETL and perovskite layers significantly improved electron extraction and suppressed charge recombination by decreasing the density of traps at the ETL surface. A planar PSC device was fabricated with the configuration indium tin oxide/TiO2 (Au)/C-PCBOD/perovskite/spiro-OMeTAD/Au to attain a power conversion efficiency (PCE) of 15.9%. The device performance was optimized with C-PCBOD as an interfacial mediate to modify the surface of the mesoporous TiO2 ETL; the C-PCBOD-treated device attained a significantly enhanced performance, PCE 18.3%. Electrochemical impedance spectral and photoluminescence decay measurements were carried out to understand the characteristics of electron transfer and charge recombination of the perovskite/TiO2 samples with and without a fullerene interfacial layer.