RESUMEN
The study involved numerical FEA (finite element analysis) of dental implants. Based on this, fatigue tests were conducted according to the PN-EN 14801 standard required for the certification of dental products. Thanks to the research methodology developed by the authors, it was possible to conduct a thorough analysis of the impact of external and internal factors such as material, geometry, loading, and assembly of the dental system on the achieved value of fatigue strength limit in the examined object. For this purpose, FEM studies were based on identifying potential sites of fatigue crack initiation in reference to the results of the test conducted on a real model. The actions described in the study helped in the final evaluation of the dental system design process named by the manufacturer as INTEGRA OPTIMA 3.35. The objective of the research was to identify potential sites for fatigue crack initiation in a selected dental system built on the INTEGRA OPTIMA 3.35 set. The material used in the research was titanium grade 4. A map of reduced von Mises stresses was used to search for potential fatigue crack areas. The research [loading] was conducted on two mutually perpendicular planes positioned in such a way that the edge intersecting the planes coincided with the axis of the system. The research indicated that the connecting screw showed the least sensitivity (stress change) to the change in the loading plane, while the value of preload has a significant impact on the achieved fatigue strength of the system. In contrast, the endosteal implant (root) and the prosthetic connector showed the greatest sensitivity to the change in the loading plane. The method of mounting [securing] the endosteal implant using a holder, despite meeting the standards, may contribute to generating excessive stress concentration in the threaded part. Observation of the prosthetic connector in the Optima 3.35 system, cyclically loaded with a force of F ≈ 300 N in the area of the upper hexagonal peg, revealed a fatigue fracture. The observed change in stress peak in the dental connector for two different force application surfaces shows that the positioning of the dental system (setting of the socket in relation to the force action plane) is significantly decisive in estimating the limited fatigue strength.
RESUMEN
This study aimed to evaluate internal tooth-filling interfaces of composite fillings made using universal adhesives using micro-computed tomography (µCT). Sixty class V cavities were randomly assigned into six groups: Peak Universal etch and rinse (PER), Peak Universal self-etch (PSE), Adhese Universal etch and rinse (AER), and Adhese Universal self-etch (ASE). Two further adhesives considered gold standards were used as control groups: OptiBond FL (OER) for the etch and rinse technique and Clearfil SE for the self-etch technique (CSE). All teeth were subjected to thermomechanical loading and four-year water storage. Next, they were analyzed using µCT to investigate the internal tooth-filling interfaces. The proportions between the gap volume (GV) at the tooth-filling interface and the volume of applied composite filling (FV), between the gap and cavity volumes (CV), and between the gap volumes at the tooth-filling interface of the external (EGV) and internal (IGV) parts were calculated. Adhese Universal achieved the significantly lowest gap-to-filling- and gap-to-cavity-volume ratios for both types of etching techniques comparing to those of the Peak Universal and control groups. Significant differences between the gaps in external and internal parts of the tooth-filling interface were only noted in the control groups. Internal gap formation and development at the tooth-filling interface depend on the material as well as the type of its application.
RESUMEN
The aim of this study was to evaluate gap formation after using two universal adhesives, Peak Universal Bond (P), which contains chlorhexidine and Adhese Universal (A), which contains 10-MDP monomer, and to compare them with two gold standard adhesives. The adhesives were tested in different etching modes, etch-and-rinse (ER) or self-etch (SE), and under thermomechanical loading (TML). Two identical Class V cavities were prepared in each of 30 human third molar teeth, and resin-composite restorations were made. Before and after TML, replicas of the restorations were prepared. Gap formation and their frequency according to the modified classification of Blunck and Zaslansky and the width of the maximum marginal gap (MG) were separately evaluated in enamel and dentin. Gap frequency did not differ significantly only in the enamel before TML, despite the use of different adhesives or etching modes. At both timepoints, the highest MG values were obtained with the Peak Universal Bond self-etch (PSE) group in enamel (6.2 µm before TML, 12.2 µm after TML) and the Peak Universal Bond etch-and-rinse (PER) group in dentine (21.3 µm before TML, 35.5 µm after TML). After TML, there was a significant increase of gap frequency for Adhese universal self-etch (ASE) group and MG values for PER, PSE, ASE groups at the resin-enamel interface, and gap frequency and MG values for all groups at the resin-dentin interface. Universal adhesive with 10-MDP monomer have beneficial effect on the resin-dentin interface, while chlorhexidine may reduce the resistance of the universal adhesive system to oral cavity conditions.