Tensile behaviors of Ti3C2Tx (MXene) films.

As the most representative member of a new emerging family of 2D material, titanium carbides or nitrides (MXenes), Ti3C2Tx and its 2D assembly format, Ti3C2Tx film, have displayed outstanding performance in a broad range of practical applications. However the mechanical behaviors of Ti3C2Tx films are rarely reported. We report a systematic study of the tensile behavior of Ti3C2Tx films. Ti3C2Tx films with various thicknesses (2-17 µm) were prepared by the vacuum filtration method. Quasi-static tension and cyclic tension tests were performed to investigate the deformation and fracture mechanism of Ti3C2Tx films. It was found that: (1) the relative sliding between Ti3C2Tx flakes is the dominant deformation mechanism of Ti3C2Tx films. Cyclic loading-releasing in tension suppresses the inter-layer sliding of Ti3C2Tx flakes effectively and thus the tensile strength of thicker Ti3C2Tx film (5 µm) film improves from 57 MPa to 67 MPa. (2) The mechanical properties of Ti3C2Tx films are found to be thickness dependent. When the film thickness increases from 2.3 to 17 µm, the tensile strength and elastic modulus drop from 61 to 36 MPa and from 17 to 8 GPa, respectively. This is interpreted as more structural defects presented in the through-the-thickness direction as film thickness is increased. (3) Moderate ultrasonication pretreatment (30 min) reduces the Ti3C2Tx flake size significantly while improving the compactness of the Ti3C2Tx film; and the resulting Ti3C2Tx film shows a linear stress-strain relationship without plastic-like deformation. As a result, the tensile strength of 5 µm thick Ti3C2Tx film is enhanced to 85 MPa; (4) Structural defects of the Ti3C2Tx film have significant effects on both the brittle-like fracture behavior and the distribution of tensile strength.

Electrochemical real-time sensor for the detection of Pb(II) ions based on Ti3C2Tx MXene.

Lead ions are especially harmful to human health, causing significant developmental and behavioral abnormalities even at small concentrations. In real-life samples, lead ions are present in mixtures with other metal ions, creating a challenge to detect it selectively at low quantities. To address these challenges, we prepared an electrochemical sensor based on delaminated Ti3C2Tx MXene, which can selectively detect low concentrations of Pb2+ in a solution containing other common metal ions. Cyclic voltammetry was applied as an electrochemical detection method. The proposed reaction mechanism involves a reversible transition between Pb2+ ions and PbO at the MXene-based layer. The sensitivity of the sensor towards Pb2+ ions and a limit of detection were determined. The sensor, as prepared, had a linear response range within 0.15-1.0 µM, with a sensitivity of 26.7 µA/µM and LOD value of 48.7 nM, which meets the requirements set by the World Health Organization.

MXene-Polydopamine-antiCEACAM1 Antibody Complex as a Strategy for Targeted Ablation of Melanoma.

Photothermal therapy (PTT) is a method for eradicating tumor tissues through the use of photothermal materials and photosensitizing agents that absorb light energy from laser sources and convert it into heat, which selectively targets and destroys cancer cells while sparing healthy tissue. MXenes have been intensively investigated as photosensitizing agents for PTT. However, achieving the selectivity of MXenes to the tumor cells remains a challenge. Specific antibodies (Ab) against tumor antigens can achieve homing of the photosensitizing agents toward tumor cells, but their immobilization on MXene received little attention. Here, we offer a strategy for the selective ablation of melanoma cells using MXene-polydopamine-antiCEACAM1 Ab complexes. We coated Ti3C2Tx MXene with polydopamine (PDA), a natural compound that attaches Ab to the MXene surface, followed by conjugation with an anti-CEACAM1 Ab. Our experiments confirm the biocompatibility of the Ti3C2Tx-PDA and Ti3C2Tx-PDA-antiCEACAM1 Ab complexes across various cell types. We also established a protocol for the selective ablation of CEACAM1-positive melanoma cells using near-infrared irradiation. The obtained complexes exhibit high selectivity and efficiency in targeting and eliminating CEACAM1-positive melanoma cells while sparing CEACAM1-negative cells. These results demonstrate the potential of MXene-PDA-Ab complexes for cancer therapy. They underline the critical role of targeted therapies in oncology, offering a promising avenue for the precise and safe treatment of melanoma and possibly other cancers characterized by specific biomarkers. Future research will aim to refine these complexes for clinical use, paving the way for new strategies for cancer treatment.

Polycaprolactone-MXene Nanofibrous Scaffolds for Tissue Engineering.

New conductive materials for tissue engineering are needed for the development of regenerative strategies for nervous, muscular, and heart tissues. Polycaprolactone (PCL) is used to obtain biocompatible and biodegradable nanofiber scaffolds by electrospinning. MXenes, a large class of biocompatible 2D nanomaterials, can make polymer scaffolds conductive and hydrophilic. However, an understanding of how their physical properties affect potential biomedical applications is still lacking. We immobilized Ti3C2Tx MXene in several layers on the electrospun PCL membranes and used positron annihilation analysis combined with other techniques to elucidate the defect structure and porosity of nanofiber scaffolds. The polymer base was characterized by the presence of nanopores. The MXene surface layers had abundant vacancies at temperatures of 305-355 K, and a voltage resonance at 8 × 104 Hz with the relaxation time of 6.5 × 106 s was found in the 20-355 K temperature interval. The appearance of a long-lived component of the positron lifetime was observed, which was dependent on the annealing temperature. The study of conductivity of the composite scaffolds in a wide temperature range, including its inductive and capacity components, showed the possibility of the use of MXene-coated PCL membranes as conductive biomaterials. The electronic structure of MXene and the defects formed in its layers were correlated with the biological properties of the scaffolds in vitro and in bacterial adhesion tests. Double and triple MXene coatings formed an appropriate environment for cell attachment and proliferation with mild antibacterial effects. A combination of structural, chemical, electrical, and biological properties of the PCL-MXene composite demonstrated its advantage over the existing conductive scaffolds for tissue engineering.

MXene nanoflakes decorating ZnO tetrapods for enhanced performance of skin-attachable stretchable enzymatic electrochemical glucose sensor.

Continuous painless glucose monitoring is the greatest desire of more than 422 million diabetics worldwide. Therefore, new non-invasive and convenient approaches to glucose monitoring are more in demand than other tests for microanalytical diagnostic tools. Besides, blood glucose detection can be replaced by continuous glucose monitoring of other human biological fluids (e.g. sweat) collected non-invasively. In this study, a skin-attachable and stretchable electrochemical enzymatic sensor based on ZnO tetrapods (TPs) and a new class of 2D materials - transition metal carbides, known as MXene, was developed and their electroanalytical behavior was tailored for continuous detection glucose in sweat. The high specific area of ZnO TPs and superior electrical conductivity of MXene (Ti3C2Tx) nanoflakes enabled to produce enzymatic electrochemical glucose biosensor with enhanced sensitivity in sweat sample (29 µA mM-1 cm-2), low limit of detection (LOD ≈ 17 µM), broad linear detection range (LDR = 0.05-0.7 mM) that satisfices glucose detection application in human sweat, and advanced mechanical stability (up to 30% stretching) of the template. The developed skin-attachable stretchable electrochemical electrodes allowed to monitor the level of glucose in sweat while sugar uptake and during physical activity. Continuous in vivo monitoring of glucose in sweat obtained during 60 min correlated well with data collected by a conventional amperometric blood glucometer in vitro mode. Our findings demonstrate the high potential of developed ZnO/MXene skin-attachable stretchable sensors for biomedical applications on a daily basis.

MXene-Assisted Ablation of Cells with a Pulsed Near-Infrared Laser.

Innovative therapies are urgently needed to combat cancer. Thermal ablation of tumor cells is a promising minimally invasive treatment option. Infrared light can penetrate human tissues and reach superficial malignancies. MXenes are a class of 2D materials that consist of carbides/nitrides of transition metals. The transverse surface plasmons of MXenes allow for efficient light absorption and light-to-heat conversion, making MXenes promising agents for photothermal therapy (PTT). To date, near-infrared (NIR) light lasers have been used in PTT studies explicitly in a continuous mode. We hypothesized that pulsed NIR lasers have certain advantages for the development of tailored PTT treatment targeting tumor cells. The pulsed lasers offer a wide range of controllable parameters, such as power density, duration of pulses, pulse frequency, and so on. Consequently, they can lower the total energy applied and enable the ablation of tumor cells while sparing adjacent healthy tissues. We show for the first time that a pulsed 1064 nm laser could be employed for selective ablation of cells loaded with Ti3C2Tx MXene. We demonstrate both low toxicity and good biocompatibility of this MXene in vitro, as well as a favorable safety profile based on the experiments in vivo. Furthermore, we analyze the interaction of MXene with cells in several cell lines and discuss possible artifacts of commonly used cellular metabolic assays in experiments with MXenes. Overall, these studies provide a basis for the development of efficient and safe protocols for minimally invasive therapies for certain tumors.

MXenes-A New Class of Two-Dimensional Materials: Structure, Properties and Potential Applications.

A new class of two-dimensional nanomaterials, MXenes, which are carbides/nitrides/carbonitrides of transition and refractory metals, has been critically analyzed. Since the synthesis of the first family member in 2011 by Yury Gogotsi and colleagues, MXenes have quickly become attractive for a variety of research fields due to their exceptional properties. Despite the fact that this new family of 2D materials was discovered only about ten years ago, the number of scientific publications related to MXene almost doubles every year. Thus, in 2021 alone, more than 2000 papers are expected to be published, which indicates the relevance and prospects of MXenes. The current paper critically analyzes the structural features, properties, and methods of synthesis of MXenes based on recent available research data. We demonstrate the recent trends of MXene applications in various fields, such as environmental pollution removal and water desalination, energy storage and harvesting, quantum dots, sensors, electrodes, and optical devices. We focus on the most important medical applications: photo-thermal cancer therapy, diagnostics, and antibacterial treatment. The first results on obtaining and studying the structure of high-entropy MXenes are also presented.