ABSTRACT
The utilization of lignin, an abundant and renewable bio-aromatic source, is of significant importance. In this study, lignin oxidation was examined at different temperatures with zirconium oxide (ZrO2)-supported nickel (Ni), cobalt (Co) and bimetallic Ni-Co metal catalysts under different solvents and oxygen pressure. Non-catalytic oxidation reaction produced maximum bio-oil (35.3 wt%), while catalytic oxidation significantly increased the bio-oil yield. The bimetallic catalyst Ni-Co/ZrO2 produced the highest bio-oil yield (67.4 wt%) compared to the monometallic catalyst Ni/ZrO2 (59.3 wt%) and Co/ZrO2 (54.0 wt%). The selectively higher percentage of vanillin, 2-methoxy phenol, acetovanillone, acetosyringone and vanillic acid compounds are found in the catalytic bio-oil. Moreover, it has been observed that the bimetallic Co-Ni/ZrO2 produced a higher amount of vanillin (43.7% and 13.30 wt%) compound. These results demonstrate that the bimetallic Ni-Co/ZrO2 catalyst promotes the selective cleavage of the ether ß-O-4 bond in lignin, leading to a higher yield of phenolic monomer compounds.
Subject(s)
Benzaldehydes , Cobalt , Nickel , Oxides , Plant Oils , Polyphenols , Zirconium , Lignin , PhenolsABSTRACT
The size-dependent dissolution of nanoscale hematite (8 and 40 nm α-Fe(2)O(3)) was examined across a broad range of pH (pH 1-7) and mechanisms including proton- and ligand- (oxalate-) promoted dissolution and dark (ascorbic acid) and photochemical (oxalate) reductive dissolution. Empirical relationships between dissolution rate and pH revealed that suspensions of 8 nm hematite exhibit between 3.3- and 10-fold greater reactivity per unit mass than suspensions of 40 nm particles across all dissolution modes and pH, including circumneutral. Complementary suspension characterization (i.e., sedimentation studies and dynamic light scattering) indicated extensive aggregation, with steady-state aggregate sizes increasing with pH but being roughly equivalent for both primary particles. Thus, while the reactivity difference between 8 and 40 nm suspensions is generally greater than expected from specific surface areas measured via N(2)-BET or estimated from primary particle geometry, loss of reactive surface area during aggregation limits the certainty of such comparisons. We propose that the relative reactivity of 8 and 40 nm hematite suspensions is best explained by differences in the fraction of aggregate surface area that is reactive. This scenario is consistent with TEM images revealing uniform dissolution of aggregated 8 nm particles, whereas 40 nm particles within aggregates undergo preferential etching at edges and structural defects. Ultimately, we show that comparably sized hematite aggregates can exhibit vastly different dissolution activity depending on the nature of the primary nanoparticles from which they are constructed, a result with wide-ranging implications for iron redox cycling.
Subject(s)
Ferric Compounds/chemistry , Nanoparticles/chemistry , Ascorbic Acid/chemistry , Hydrogen-Ion Concentration , Oxalates/chemistry , Particle Size , Solubility , Solutions , Surface PropertiesABSTRACT
Stereocontrolled Mn-mediated addition of alkyl iodides to chiral N-acylhydrazones enables strategic C-C bond constructions at the stereogenic centers of chiral amines. Applying this strategy to quinine suggested complementary synthetic approaches to construct C-C bonds attached at the nitrogen-bearing stereogenic center using multifunctional alkyl iodides 6a-d as radical precursors, or using multifunctional chiral N-acylhydrazones 26a-d as radical acceptors. These were included among Mn-mediated radical additions of various alkyl iodides to a range of chiral N-acylhydrazone radical acceptors, leading to the discovery that pyridine and alkene functionalities are incompatible. In a revised strategy, these functionalities are avoided during the Mn-mediated radical addition of 6d to chiral N-acylhydrazone 22b, which generated a key C-C bond with complete stereochemical control at the chiral amine carbon of quinine. Subsequent elaboration included two sequential cyclizations to complete the azabicyclo[2.2.2]octane ring system. Group selectivity between two 2-iodoethyl groups during the second cyclization favored an undesired azabicyclo[3.2.1]octane ring system, an outcome that was found to be consistent with transition state calculations at the B3LYP/6-31G(d) level. Group differentiation at an earlier stage enabled an alternative regioconvergent pathway; this furnished the desired azabicyclo[2.2.2]octane ring system and afforded quincorine (21b), completing a formal synthesis of quinine.
Subject(s)
Hydrazones/chemistry , Manganese/chemistry , Quinine/chemistry , Quinine/chemical synthesis , Molecular Structure , StereoisomerismABSTRACT
Water adsorption on kaolinite, illite, and montmorillonite clays was studied as a function of relative humidity (RH) at room temperature (298 K) using horizontal attenuated total reflectance (HATR) Fourier transform infrared (FTIR) spectroscopy equipped with a flow cell. The water content as a function of RH was modeled using the Brunauer, Emmett, and Teller (BET) and Freundlich adsorption isotherm models to provide complementary multilayer adsorption analysis of water uptake on the clays. A detailed analysis of model fit integrity is reported. From the BET fit to the experimental data, the water content on each of the three clays at monolayer (ML) water coverage was determined and found to agree with previously reported gravimetric data. However, BET analysis failed to adequately describe adsorption phenomena at RH values greater than 80%, 50%, and 70% RH for kaolinite, illite, and montmorillonite clays, respectively. The Freundlich adsorption model was found to fit the data well over the entire range of RH values studied and revealed two distinct water adsorption regimes. Data obtained from the Freundlich model showed that montmorillonite has the highest water adsorption strength and highest adsorption capacity at RH values greater than 19% (i.e., above ML water adsorption) relative to the kaolinite and illite clays. The difference in the observed water adsorption behavior between the three clays was attributed to different water uptake mechanisms based on a distribution of available adsorption sites. It is suggested that different properties drive water adsorption under different adsorption regimes resulting in the broad variability of water uptake mechanisms.