Pickering emulsions of thyme oil in water using oxidized cellulose nanofibers: Towards bio-based active packaging.

The antioxidant and antimicrobial properties of thyme essential oil (TEO) are useful for active food packaging, but its poor aqueous solubility restricts its applications. This work involves anionic cellulose nanofibers (CNFs) as the sole stabilizing agent for TEO-in-water emulsions, with oil concentrations ranging from 10 mL/L to 300 mL/L. A double mechanism was proposed: the adsorption of CNFs at oil/water interfaces restricted coalescence to a limited extent, while thickening (rheological stabilization) was required to avoid the buoyance of large droplets (>10 µm). Thickening effects comprised both higher viscosity (over 0.1 Pa·s at 10 s-1) and yield stress (approximately 0.9 Pa). Dilute emulsions had good film-forming capabilities, whereas concentrated emulsions were suitable for paper coating. Regarding antimicrobial activity, CNF-stabilized TEO-in-water emulsions successfully inhibited the growth of both Gram-negative (E. coli, S. typhimurium) and Gram-positive bacteria (L. monocytogenes). As for the antioxidant properties, approximately 50 mg of paper or 3-5 mg of film per mL of food simulant D1 were required to attain 50 % inhibition in radical scavenging tests. Nonetheless, despite the stability and the active properties of these bio-based hydrocolloids, providing this antioxidant and antimicrobial activity was incompatible with maintaining the organoleptic properties of the foodstuff unaltered.

Valorization of Hemp Core Residues: Impact of NaOH Treatment on the Flexural Strength of PP Composites and Intrinsic Flexural Strength of Hemp Core Fibers.

Hemp core is a lignocellulosic residue in the production chain of hemp strands. Huge amounts of hemp core are gathered annually in Europe (43,000 tons) with no major application end. Such lignocellulosic wastes have potential as filling or reinforcing material to replace synthetic fibers and wood fibers in polymer composites. In this study, hemp core biomass was treated under different NaOH concentrations and then defibrated by means of Sprout Waldron equipment to obtain single fibers. Polypropylene matrix was reinforced up to 50 wt.% and the resulting hemp core fibers and the flexural properties were investigated. The results show that the flexural strength of composites increased with the intensity of NaOH treatment. The effect of NaOH was attributed to the removal of extractives and lignin in the fiber cell wall leading to improved interfacial adhesion characteristics. Besides, a methodology was established for the estimation of the intrinsic flexural strength of hemp core fibers. The intrinsic flexural strength of hemp core fibers was calculated to be 940 MPa for fibers treated at 10 wt.% of NaOH. In addition, a relationship between the lignin content and the intrinsic strength of the fibers was established.