Substitution of Copper by Magnesium in Malachite: Insights into the Synthesis and Structural Effects.

The phase width of the copper hydroxycarbonate malachite, Cu2CO3(OH)2, upon substitution with magnesium has been studied in detail. In extension of a previous study on amorphous precursors, the introduction of a hydrothermal aging step allowed the retrieval of crystalline hydroxycarbonate samples with up to 37 atom % Mg (metal content) that are suitable candidates as precursors to Cu/MgO catalysts for CO hydrogenation. Simultaneous refinements of X-ray powder diffraction and pair distribution function (PDF) data as well as complementary spectroscopic insight (X-ray absorption and infrared spectroscopy) revealed that samples with up to 18 atom % Mg are phase-pure magnesian malachites but the magnesium content can be increased beyond this threshold when mcguinnessite (CuMgCO3(OH)2) is accepted as a side phase. In a complementary study, a continuous increase of the magnesium fraction was found during aging and the corresponding structural evolution was studied by means of PDF. These findings add significant insight into the aging chemistry of crystalline Cu,Mg hydroxycarbonates. Furthermore, both phase-pure magnesian malachite and mcguinnessite-containing samples with up to 37 atom % Mg have been examined by thermogravimetry, X-ray powder diffraction, and N2 physisorption and were found to be promising candidates for use as precursors for the preparation of Cu/MgO catalysts.

Structural dynamics of an iron molybdate catalyst under redox cycling conditions studied with in situ multi edge XAS and XRD.

The structural dynamics and phase transformations of an iron molybdate catalyst with excess molybdenum trioxide (Mo/Fe = 2.0) were studied during redox cycling of the catalyst using in situ multi-edge X-ray absorption spectroscopy (XAS) at the Mo K-edge (transmission mode) and Fe K-edge (fluorescence mode) in combination with X-ray diffraction (XRD). X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) analysis showed that heating under reducing conditions with methanol up to 400 °C produced MoO2 and FeMoO4. Linear combination fitting (LCF) analysis showed that iron was reduced completely, while molybdenum remained partly oxidized (60% as Mo(vi)). Complementary in situ XRD also supported the phase transformation due to reduction of Fe2(MoO4)3 and MoO3 to FeMoO4 and MoO2. Subsequent heating under oxidative conditions from 200 to 500 °C transformed the catalyst into its initial state via Fe2O3 and extra MoO3 as intermediate phases. This underlines the segregation and iron enrichment during redox cycling. MoO3 volatilization, observed under industrial reaction conditions of a methanol and oxygen containing atmosphere, causes this segregation to be permanent. Complete regeneration could only be achieved at 500 °C, which is significantly higher than industrial reaction temperatures. Overall, multi edge in situ XAS along with complementary XRD was found to be an ideal tool for tracing the different amorphous and crystalline phases present during redox cycling of the catalyst.