Thermoresponsive starch-based particle-stabilized Pickering high internal phase emulsions as nutraceutical containers for controlled release.

Pickering high internal phase emulsions (HIPEs) stabilized solely by bioderived starch-based particles hold potential for application in the food and pharmaceutical fields. This paper reports the use of a thermoresponsive 2-hydroxy-3-butoxypropyl starch (HBPS) particle as a representative natural biocompatible material for use as an effective stabilizer for HIPE formation. HBPS is synthesized by using butyl glycidyl ether as a hydrophobic reagent to change the hydrophobic-hydrophilic balance of starch, and then starch-based particles are fabricated by a simple nanoprecipitation procedure. The size of particles increased with an increase in temperature, and the particles are essentially monodisperse with a PDI of about 0.1 when the temperature was above 15 °C. These HBPS particles were subsequently used as an effective stabilizer to fabricate stable oil-in-water (o/w) Pickering HIPEs with an internal phase volume of 80% at different stabilizer concentrations. The results demonstrated that increasing the particle concentration is conducive to the formation of stable Pickering HIPEs with greater stiffnesses. In addition, the nutraceutical material (ß-carotene) was encapsulated into HIPEs and in vitro release experiments revealed that the release in this system can be controlled by adjusting the temperature.

A novel poly(acrylic acid-co-acrylamide)/diatomite composite flocculant with outstanding flocculation performance.

Series of anionic flocculants with outstanding flocculation performance, poly(acrylic acid-co-acrylamide)/diatomite composite flocculants (PAAD) were successfully prepared through aqueous solution copolymerization and applied to flocculate from oil-field fracturing waste-water. The structure of PAAD was characterized by Fourier transform infra-red spectroscopy, (13)C nuclear magnetic resonance and X-ray diffraction tests, and its properties were systematically evaluated by viscometer, thermogravimetry analysis and flocculation measurements. Furthermore, the influences of various reaction parameters on the apparent viscosity of flocculant solution were studied, and the optimum synthesis condition was determined. The novel composite flocculants exhibited outstanding flocculation properties. Specifically, the dosage of composite flocculants that could make the transmittance of treated wastewater exceed 90% was only approximately 12-35 ppm, which was far lower than that of conventional flocculants. Meanwhile, the settling time was lower than 5 s, which was similar to that of conventional flocculants. This was because PAAD flocculants had a higher absorption capacity, and larger chain extending space than conventional linear flocculants, which could refrain from the entanglement of linear polymer chains and significantly improve flocculation capacity.