ABSTRACT
Two-dimensional (2D) hexagonal boron-carbon-nitrogen (h-BCN) atomic layers are expected to possess interesting properties complementary to those of graphene and h-BN, enabling a rich variety of electronic structures, properties and applications. Herein, we demonstrate a novel method to synthesize 2D h-BCN atomic layers with a full range of compositions by ion beam sputtering deposition under a mixed Ar/CH4 atmosphere. The h-BCN layers have been thoroughly characterized by various techniques, aiming at the determination of their structure evolution and properties. We find that homogeneous h-BCN layers consisting of graphene and h-BN nanodomains can be obtained at an appropriate C content, whereas too high or too low C contents result in the segregation of large-sized graphene or h-BN islands. Furthermore, the band gap of h-BCN layers slightly decreases with the increasing C content, while their electric properties can be tuned from insulating to highly conducting. This work provides a novel approach for synthesizing 2D h-BCN atomic layers and paves the way for the development of h-BCN-based devices.
ABSTRACT
Ultraflexible transparent film heaters have been fabricated by embedding conductive silver (Ag) nanowires into a thin poly(vinyl alcohol) film (AgNW/PVA). A cold-pressing method was used to rationally adjust the sheet resistance of the composite films and thus the heating powers of the AgNW/PVA film heaters at certain biases. The film heaters have a favorable optical transmittance (93.1% at 26 Ω/sq) and an outstanding mechanical flexibility (no visible change in sheet resistance after 10â¯000 bending cycles and at a radius of curvature ≤1 mm). The film heaters have an environmental endurance, and there is no significant performance degradation after being kept at high temperature (80 °C) and high humidity (45 °C, 80% humidity) for half a year. The efficient Joule heating can increase the temperature of the film heaters (20 Ω/sq) to 74 °C in â¼20 s at a bias of 5 V. The fast-heating characteristics at low voltages (a few volts) associated with its transparent and flexibility properties make the poly(dimethylsiloxane)/AgNW/PVA composite film a potential candidate in medical thermotherapy pads.