Staining and bleaching susceptibility of zirconia-reinforced lithium silicate glass-ceramics with different thicknesses, translucencies, and fabrication methods.

STATEMENT OF PROBLEM: The influence of different thicknesses, translucencies, and fabrication methods on the spectrophotometric and topographical properties of zirconia-reinforced lithium silicate glass-ceramics (ZLSs) for dental restorations remains unclear. PURPOSE: The purpose of this in vitro study was to investigate the effect of thicknesses, translucencies, and fabrication methods on the color stability, translucency parameter, opalescence parameter, whiteness stability, transmitted irradiance, light transmittance, opacity, gloss, and roughness of ZLSs exposed to coffee staining and bleaching treatments. MATERIAL AND METHODS: Two pressable ZLSs (VITA AMBRIA, VA and Celtra Press, CP) and 2 machinable ZLSs (VITA Suprinity, VS and Celtra Duo, CD) were examined at high translucency (HT) and low translucency (LT) levels in 2 thicknesses (n=160). The specimens were evaluated at baseline, after coffee staining, and after bleaching. The color stability (ΔE2000), translucency parameter (TP), opalescence parameter (OP), whiteness index (WID), and whiteness stability (ΔWID) were measured with a spectrophotometer. Transmitted irradiance (It), light transmission (T), and opacity (O) were obtained from a light-polymerizing unit and a polymerization light collection device. Roughness stability (ΔSa%) was determined with an optical profilometer, and gloss stability (ΔGU%) was recorded with a gloss meter. Data of ΔCIE2000, ΔWID, ΔSa%, and ΔGU% were analyzed by 4-way ANOVA, and data of the TP, OP, WID, It, T, and O were analyzed by repeated 4-way ANOVA (α=.05). RESULTS: VS-HT exceeded the ΔCIE2000 acceptability threshold after coffee staining and bleaching protocols. Pressable ZLSs exhibited greater color stability than machinable ZLSs. The 1-mm-thick VA, CP, and CD materials exceeded the ΔWID perceptibility threshold after bleaching. The highest TP and OP was displayed by the 1-mm-thick CP after bleaching. ΔGU increased after water storage and decreased after coffee staining and bleaching. ΔSa% significantly increased after bleaching (P<.05). CONCLUSIONS: The color stability and other spectrophotometric properties of ZLSs depended on material thickness. The effects of ZLS fabrication methods and translucency levels on their measured properties were inconsistent. Subjecting 1-mm-thick ZLS materials to acidic media adversely impacted their stainability and surface texture.

Microhardness and Gloss of a New CAD/CAM Hybrid Material Following Accelerated Aging and Coffee Immersion.

PURPOSE: To evaluate and compare the effect of accelerated aging and coffee immersion on the microhardness and gloss of a new computer-aided design and computer-aided manufacturing (CAD/CAM) hybrid material (Crystal Ultra) to those of contemporary restorative materials. MATERIALS AND METHODS: A total of 160 specimens (12 × 14 × 1 mm ± 0.05 mm) were obtained from IPS e.max (IPS), VITA Enamic (VE), Crystal Ultra (CU), Lava Ultimate (LU), and CeraSmart (CS) high-translucency CAD/CAM blocks. The Vickers microhardness and gloss of the specimens were determined after thermocycling and coffee immersion. Data analysis was performed using SPSS (α = .05). RESULTS: IPS and CS specimens exhibited the highest (572.66 ± 11.30) and lowest (61.92 ± 3.91) microhardness, respectively. The highest gloss was observed with IPS specimens (3.31 ± 0.32), and LU specimens showed the lowest gloss (2.33 ± 0.06). A significant difference in gloss was observed between the materials at all measurement intervals (P < .01), except at T0 (P = .43). IPS specimens showed no significant changes in either group at any measurement interval. CONCLUSIONS: The microhardness and gloss of the new CU material were comparable to those of the tested contemporary hybrid restorative materials. Glass-ceramic showed superior hardness and gloss compared to hybrid restorative materials. Accelerated aging with thermocycling and staining significantly affected the microhardness and gloss of all tested CAD/CAM materials.