Facemasks and ferrous metallurgy: improving gasification reactivity of low-volatile coals using waste COVID-19 facemasks for ironmaking application.

The global pandemic response to COVID-19 has led to the generation of huge volumes of unrecyclable plastic waste from single use disposable face coverings. Rotary hearth furnaces can be used to recover Zn and Fe from non-recyclable steelmaking by-product dusts, and waste plastic material such as facemasks could be utilized as a supplementary reductant for the rotary hearth furnace (RHF), but their fibrous form makes milling and processing to appropriate sizing for RHF application extremely challenging. A scalable method of grinding facemasks to powder by melting and mixing with Welsh coal dust reported herein provides a solution to both environmental challenges. The melt-blended PPE/coal dust shows a dramatically improved CO2 gasification reactivity (Ea = 133-159 kJmol-1) when compared to the untreated coal (Ea = 183-246 kJmol-1), because of improved pore development in the coal during the pyrolysis stage of heating and the catalytic activity of the CaO based ash present in the facemask plastic. The results are promising for the application of waste facemasks in recycling steelmaking by-product dusts in rotary hearth furnaces and may also be suitable for direct injection to the blast furnace subject to further study.

Water-structuring molecules and nanomaterials enhance radiofrequency heating in biologically relevant solutions.

For potential applications in nano-mediated radiofrequency cancer hyperthermia, the nanomaterial under investigation must increase the heating of any aqueous solution in which it is suspended when exposed to radiofrequency electric fields. This should also be true for a broad range of solution conductivities, especially those that artificially mimic the ionic environment of biological systems. Herein we demonstrate enhanced heating of biologically relevant aqueous solutions using kosmotropes and a hexamalonoserinolamide fullerene.

Alumoxane/ferroxane nanoparticles for the removal of viral pathogens: the importance of surface functionality to nanoparticle activity.

A bi-functional nano-composite coating has been created on a porous Nomex® fabric support as a trap for aspirated virus contaminated water. Nomex® fabric was successively dip-coated in solutions containing cysteic acid functionalized alumina (alumoxane) nanoparticles and cysteic acid functionalized iron oxide (ferroxane) nanoparticles to form a nanoparticle coated Nomex® (NPN) fabric. From SEM and EDX the nanoparticle coating of the Nomex® fibers is uniform, continuous, and conformal. The NPN was used as a filter for aspirated bacteriophage MS2 viruses using end-on filtration. All measurements were repeated to give statistical reliability. The NPN fabrics show a large decrease as compared to Nomex® alone or alumoxane coated Nomex®. An increase in the ferroxane content results in an equivalent increase in virus retention. This suggests that it is the ferroxane that has an active role in deactivating and/or binding the virus. Heating the NPN to 160 °C results in the loss of cysteic acid functional groups (without loss of the iron nanoparticle's core structure) and the resulting fabric behaves similar to that of untreated Nomex®, showing that the surface functionalization of the nanoparticles is vital for the surface collapse of aspirated water droplets and the absorption and immobilization of the MS2 viruses. Thus, for virus immobilization, it is not sufficient to have iron oxide nanoparticles per se, but the surface functionality of a nanoparticle is vitally important in ensuring efficacy.

Wet catalyst-support films for production of vertically aligned carbon nanotubes.

A procedure for vertically aligned carbon nanotube (VA-CNT) production has been developed through liquid-phase deposition of alumoxanes (aluminum oxide hydroxides, boehmite) as a catalyst support. Through a simple spin-coating of alumoxane nanoparticles, uniform centimer-square thin film surfaces were coated and used as supports for subsequent deposition of metal catalyst. Uniform VA-CNTs are observed to grow from this film following deposition of both conventional evaporated Fe catalyst, as well as premade Fe nanoparticles drop-dried from the liquid phase. The quality and uniformity of the VA-CNTs are comparable to growth from conventional evaporated layers of Al(2)O(3). The combined use of alumoxane and Fe nanoparticles to coat surfaces represents an inexpensive and scalable approach to large-scale VA-CNT production that makes chemical vapor deposition significantly more competitive when compared to other CNT production techniques.