RESUMEN
Surface modification of superparamagnetic Fe3O4 nanoparticles using polymers (polyaniline/polypyrrole) was done by radio frequency (r.f.) plasma polymerization technique and characterized by XRD, TEM, TG/DTA and VSM. Surface-passivated Fe3O4 nanoparticles with polymers were having spherical/rod-shaped structures with superparamagnetic properties. Broad visible photoluminescence emission bands were observed at 445 and 580 nm for polyaniline-coated Fe3O4 and at 488 nm for polypyrrole-coated Fe3O4. These samples exhibit good fluorescence emissions with L929 cellular assay and were non-toxic. Magnetic hyperthermia response of Fe3O4 and polymer (polyaniline/polypyrrole)-coated Fe3O4 was evaluated and all the samples exhibit hyperthermia activity in the range of 42-45 °C. Specific loss power (SLP) values of polyaniline and polypyrrole-coated Fe3O4 nanoparticles (5 and 10 mg/ml) exhibit a controlled heat generation with an increase in the magnetic field.
Asunto(s)
Compuestos de Anilina/química , Diagnóstico por Imagen/métodos , Hipertermia Inducida/métodos , Nanopartículas de Magnetita/química , Polímeros/química , Pirroles/química , Compuestos de Anilina/efectos de la radiación , Línea Celular Tumoral , Supervivencia Celular/efectos de los fármacos , Compuestos Férricos/síntesis química , Compuestos Férricos/química , Compuestos Férricos/efectos de la radiación , Humanos , Campos Magnéticos , Magnetismo/métodos , Nanopartículas de Magnetita/efectos de la radiación , Nanopartículas de Magnetita/uso terapéutico , Ensayo de Materiales , Gases em Plasma/química , Polímeros/efectos de la radiación , Pirroles/efectos de la radiación , Ondas de Radio , Propiedades de Superficie/efectos de la radiación , Difracción de Rayos XRESUMEN
Ferrofluid-based manganese (Mn(2+)) substituted superparamagnetic iron oxide nanoparticles stabilized by surface coating with trisodium citrate (MnIOTCs) were synthesized for enhanced hyperthermic activity and use as negative magnetic resonance imaging (MRI) contrast media intended for applications in theranostics. The synthesized MnIOTC materials were characterized based on their physicochemical and biological features. The crystal size and the particle size at the nano level were studied using XRD and TEM. The presence of citrate molecules on the crystal surface of the iron oxide was established by FTIR, TGA, DLS and zeta potential measurements. The superparamagnetic property of MnIOTCs was measured using a vibrating sample magnetometer. Superparamagnetic iron oxide substituted with Mn(2+) with a 3:1 molar concentration of Mn(2+) to Fe(2+) and surface modified with trisodium citrate (MnIO75TC) that exhibited a high T2 relaxivity of 184.6mM(-1)s(-1) and showed excellent signal intensity variation in vitro. Hyperthermia via application of an alternating magnetic field to MnIO75TC in a HeLa cell population induced apoptosis, which was further confirmed by FACS and cLSM observations. The morphological features of the cells were highly disrupted after the hyperthermia experiment, as evidenced from E-SEM images. Biocompatibility evaluation was performed using an alamar blue assay and hemolysis studies, and the results indicated good cytocompatibility and hemocompatibility for the synthesized particles. In the current study, the potential of MnIO75TC as a negative MRI contrast agent and a hyperthermia agent was demonstrated to confirm its utility in the burgeoning field of theranostics.