Toothbrushing abrasion susceptibility of enamel and dentin bleached with calcium-supplemented hydrogen peroxide gel.

UNLABELLED: The objective of this study was to evaluate enamel and dentin susceptibility to toothbrushing abrasion, after bleaching with 7.5% hydrogen peroxide (HP) gel supplemented or not with 0.5% calcium gluconate (Ca). Toothbrushing was performed immediately and 1h after bleaching, with two suspensions (high and low abrasivity). Bovine enamel and dentin specimens were divided into 12 groups (n=10) according to the bleaching gel (with and without Ca), slurry abrasivity (high or low) and elapsed time after bleaching (immediately and after 1h). As control, a group was not bleached, but abraded. The treatment cycle (7 d) consisted of bleaching (1h) and toothbrushing (135 strokes/day) immediatelly or after 1h of artificial saliva exposure. Surface roughness and surface loss (µm) were measured by profilometry and analysed by three-way ANOVA (5%). Surface roughness means were significantly influenced by slurry abrasivity (p<0.0001). For enamel loss, significant triple interaction was observed (p<0.0001). HP-bleached groups and immediately brushed with high-abrasive slurry exhibited increased loss (1.41±0.14) compared to other groups (µm). Control and HP+Ca-bleached groups brushed after 1h with low abrasive slurry presented the lowest loss (0.21±0.03/0.27±0.02). For dentin loss, significant interaction was observed for bleaching and interval factors (p<0.001). 7.5%HP-bleached groups and immediately brushed showed significantly higher loss (8.71±2.45) than the other groups. It was concluded that surface roughness increased when high abrasive was used, independently of bleaching. 7.5%HP increased enamel and dentin loss, mainly with high abrasive slurries. Calcium supplementation of bleaching gel reduced surface loss. Additionally, in order to minimize tooth wear susceptibility, it is recommended to delay brushing after bleaching. CLINICAL RELEVANCE: After bleaching gel application, postponing toothbrushing is recommended, as well as brushing with low abrasive dentifrices. Additionally, supplementation of hydrogen peroxide gel with calcium-based remineralizing agent potentially reduces tooth loss after abrasion.

Efficacy of mouth rinses and toothpaste on tooth whitening.

OBJECTIVES: People increasingly desire tooth whitening. Considering the wide range of whitening products on the market, this study evaluated the efficacy of whitening toothpastes and mouth rinses compared with the 10% carbamide peroxide (CP) whitening gel. METHODS: We obtained 120 cylindrical specimens from bovine teeth, which were darkened for 24 hours in a coffee solution. The color measurement was performed by a spectrophotometer using the CIE L*a*b* system, and specimens were divided into six groups according to the use of the following agents: group 1, conventional fluoridated toothpaste; group 2, Close Up White Now; group 3, Listerine Whitening; group 4, Colgate Plax Whitening; group 5, experimental mouth rinse with Plasdone; and group 6, 10% CP Whiteness Perfect. After the simulation of 12 weeks of treatment for groups 1 to 5 and 14 days of treatment for group 6, the specimens were subjected to a new color reading. RESULTS: Data were subjected to one-way analysis of variance (α=0.05), which showed significant differences among groups after 12 weeks for ΔE (p=0.001). Results of the Tukey test revealed that groups 3, 4, and 6 presented significantly higher color alteration than groups 1, 2, and 5. CONCLUSIONS: The whitening toothpaste Close Up White Now and the experimental mouth rinse with Plasdone showed similar color alteration as conventional toothpaste after a 12-week treatment simulation. These groups presented significantly lower color alteration compared with whitening mouth rinses Listerine and Colgate Plax Whitening, which showed similar results to those observed after 14 days of bleaching with 10% CP treatment.