Structural Features of Alkaline Dioxane Lignin and Residual Lignin from Eucalyptus grandis × E. urophylla.

In the present study, lignin from eucalyptus was extracted with 80% alkaline dioxane (0.05 M NaOH) from ball-milled wood and subsequently fractionated by gradient acid precipitation from the filtrate. Meanwhile, the residual lignin was prepared by a double enzymatic hydrolysis process. The yield of the lignin extracted by alkaline dioxane (LA-2) was 29.5%. The carbohydrate contents and molecular weights of the gradient acid precipitated lignin fractions gradually decreased from 4.90 to 1.36% and from 7770 to 5510 g/mol, respectively, with the decline of the pH value from 6 to 2. Results from two-dimensional heteronuclear single quantum coherence nuclear magnetic resonance (NMR) and 31P NMR spectroscopy showed an evident reduction of ß- O-4 ' linkages with the pH value decrease, while the contents of aliphatic -OH, phenolic -OH, and carboxylic groups displayed an increasing trend. Moreover, the residual lignin exhibited the highest molecular weight (11690 g/mol), the most abundant ß- O-4 ' linkages (71.1%), and the highest S/G ratio (4.68).

Structural features and antioxidant activities of lignins from steam-exploded bamboo (Phyllostachys pubescens).

An environmentally friendly steam explosion process of bamboo, followed by alkali and alkaline ethanol delignification, was developed to fractionate lignins. Results showed that after steam explosion the lignins isolated showed relatively low carbohydrate contents (0.55-1.76%) and molecular weights (780-1050 g/mol). For each steam-exploded sample, alkali-extracted lignins presented higher phenolic OH values (1.41-1.82 mmol/g), p-coumaric acid to ferulic acid ratios (pCA/FA ratios 4.5-14.1), and syringyl to guaiacyl ratios (S/G ratios 5.0-8.5) than those from alkaline ethanol-extracted lignins (phenolic OH 0.85-1.35 mmol/g, pCA/FA ratios 1.6-5.2, and S/G ratios 3.5-4.8). The lignins obtained consisted mainly of ß-O-4' linkages combined with small amounts of ß-ß', ß-5', and α-O-4/ß-O-4 linkages. Antioxidant activities of the lignins obtained were tested by the 2,2-diphenyl-1-picrylhydrazyl, 2,2'-azobis(3-ethylbenzothiazoline-6-sulfonic acid), and ferric reducing activity power methods. It was found that alkali-extracted lignins obtained during the initial extraction process had higher antioxidant activities than alkaline ethanol-extracted lignins obtained during the second extraction process.

Microwave-induced synthesis of carboxymethyl hemicelluloses and their rheological properties.

In this article, a facile, rapid, and efficient method was developed for the preparation of carboxymethyl hemicelluloses using microwave-induced organic reaction enhancement chemistry. The influences of the factors including reaction time, temperature, and the amount of sodium monochloroacetate and sodium hydroxide on the degree of substitution (DS) of the products were investigated. The rheological properties and the chemical structure of the resulting polymers were also studied. It was found that microwave irradiation could significantly promote the chemical reaction efficiency and accelerate the carboxymethylation of hemicelluloses with sodium monochloroacetate. Therefore, carboxymethyl hemicelluloses with higher DS of 1.02 could be obtained in much shorter time scales as compared to the conventional heating method. Results from rheological analysis indicated that carboxymethyl hemicellulose solutions exhibited shear-thinning behavior in the range of shear rates tested and showed lower viscosity and modulus in comparison with those of the native hemicelluloses due to lower molecular weight and the role of carboxymethyl groups in reducing the entanglements between hemicelluloses chains.