INTRODUCTION: The decline in dental caries has been attributed to the widespread use of fluoride (F). Two forms of presentation are fluoridated toothpaste (FT) and mouthwash (MW), widely used by the population. MATERIALS AND METHODS: This study aimed to evaluate in vitro the effects of combining FT and MW, whether supplemented with sodium trimetaphosphate (TMP) or not, on dental enamel demineralization. Bovine enamel blocks (n = 60) were selected based on initial surface hardness (SHi) and divided into 5 experimental groups (n = 12 each): I) Placebo Toothpaste (without F/TMP); II) 1100 ppm F Toothpaste (FT); III) 1100F associated with a MW at 100 ppm F (FT + MW 100F); IV) 1100F associated with a MW at 225 ppm F (FT + MW 250F); and V) 1100F associated with a MW at 100 ppm F supplemented with 0.4 % TMP (FT + MW 100F-TMP). The blocks were treated twice a day, undergoing 5 pH cycles over 7 days. Thus, the percentage change in surface hardness (%SH), integrated subsurface hardness loss (ΔKHN), and the concentration of F, phosphorus (P), and calcium (Ca) in the enamel were determined. The data were submitted to ANOVA and Student-Newman-Keuls test (p < 0.001). RESULTS: The 1100F group was statistically inferior to the groups associated with MW for %SH, ΔKHN, and the concentration of P and Ca in the enamel (p < 0.001). Blocks treated with FT + MW 225F and FT + MW 100F-TMP showed significantly lower %SH compared to the other groups (p < 0.001). The FT + MW 100F - TMP group exhibited the lowest depth mineral loss (ΔKHN), and higher concentration de P in enamel (p < 0.001). CONCLUSION: The adjunct use of MW with FT produces a greater protective effect in inhibiting enamel demineralization, and the supplementation of TMP to the MW with 100F provides a superior effect compared to MW with 225F. CLINICAL SIGNIFICANCE: This combination of treatments could be regarded as one of several alternative fluoride supplements for subjects at elevated risk of caries.
Asunto(s)
Cariostáticos , Esmalte Dental , Fluoruros , Dureza , Antisépticos Bucales , Polifosfatos , Desmineralización Dental , Pastas de Dientes , Animales , Bovinos , Polifosfatos/uso terapéutico , Polifosfatos/farmacología , Desmineralización Dental/prevención & control , Esmalte Dental/efectos de los fármacos , Cariostáticos/uso terapéutico , Pastas de Dientes/uso terapéutico , Pastas de Dientes/química , Antisépticos Bucales/uso terapéutico , Fluoruros/uso terapéutico , Concentración de Iones de Hidrógeno , Calcio/uso terapéutico , Calcio/análisis , Ensayo de MaterialesRESUMEN
To evaluate the effect of 1100 ppm F toothpastes supplemented with micrometric or nanosized ß-CaGP (ß-CaGPm/ß-CaGPn) on artificial enamel remineralization, using a pH cycling model. Enamel blocks with artificial caries were randomly allocated into ten groups (n = 10), according to the toothpastes: without fluoride/ß-CaGPm/ß-CaGPn (negative control); 1100 ppm F (1100F); 1100F plus 0.125%, 0.25%, 0.5%, and 1.0% of ß-CaGPm or ß-CaGPn. The blocks were treated 2×/day with slurries of toothpastes. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); integrated mineral loss (ΔIMR); fluoride (F), calcium (Ca), and phosphorus (P) concentrations in the enamel; polydispersity index (PdI); and zeta potential (Zp) were determined. The data were analyzed by ANOVA (p < 0.001). For Zp/PdI, no significance was observed when comparing the means (p > 0.001). The treatment with 1100F-0.25%ß-CaGPn led to %SHR â¼57 higher when compared to the 1100F group (p < 0.001). The lowest ΔKHN was observed for the 1100F-0.25%ß-CaGPn group (p < 0.001). The ΔIMR was lower (â¼201%) for the 1100F-0.25%ß-CaGPn when compared to 1100F (p < 0.001). The association of ß-CaGPm and ß-CaGPn to 1100F did not influence its F concentration (p > 0.001). The highest increase in Ca and P was observed for 1100F-0.25%ß-CaGPn (p < 0.001). The addition of 0.25%ß-CaGPn to 1100F toothpaste was able to promote an additional remineralizing effect of artificial caries lesions.
RESUMEN
OBJECTIVES: To evaluate the anti-demineralizing effect of a mouthwash comprising pomegranate peel extract (PPE 3%), sodium trimetaphosphate (TMP 0.3%), and fluoride (F 225 ppm) in an in situ study, and to assess its irritation potential in an ex vivo study. METHODS: This double-blind crossover study was conducted in four phases with 7 days each. Twelve volunteers used palatal appliances containing enamel blocks, which were subjected to cariogenic challenges. The ETF formulation (PPE + TMP + F, pH 7.0), TF formulation (TMP + F, pH 7.0), deionized water (W, pH 7.0), and essential oil commercial mouthwash (CM, 220 ppm F, pH 4.3) were dropped onto the enamel twice daily. The percentage of surface hardness loss, integrated loss of subsurface hardness, calcium, phosphorus, and fluoride in enamel and biofilms were determined. In addition, alkali-soluble extracellular polysaccharide concentrations were analyzed in the biofilms. The irritation potential was evaluated using the hen's egg chorioallantoic membrane test through the vascular effect produced during 300-s of exposure. RESULTS: ETF was the most efficacious in preventing demineralization. It also showed the highest concentrations of calcium and phosphorus in the enamel and in the biofilm, as well as the lowest amount of extracellular polysaccharides in the biofilm. In the eggs, ETF produced light reddening, whereas CM led to hyperemia and hemorrhage. CONCLUSIONS: The addition of PPE to formulations containing TMP and F increased its anti-demineralizing property, and this formulation presented a lower irritation potential than the CM. CLINICAL RELEVANCE: ETF can be a promising alternative alcohol-free mouthwash in patients at high risk of caries.
Asunto(s)
Antisépticos Bucales , Extractos Vegetales , Granada (Fruta) , Desmineralización Dental , Humanos , Calcio/análisis , Estudios Cruzados , Esmalte Dental , Fluoruros , Dureza , Antisépticos Bucales/química , Antisépticos Bucales/farmacología , Fósforo , Polifosfatos , Desmineralización Dental/prevención & control , Extractos Vegetales/farmacologíaRESUMEN
The aim of this study was to evaluate the effects of supplementing toothpastes containing 1100 ppm F with micrometric or nanometric [beta]-calcium glycerophosphate (ß-CaGPm/ß-CaGPn) on artificial enamel demineralization, using a pH cycling model. Bovine enamel blocks (4 mm × 4 mm, n = 120) selected using initial surface hardness were randomly allocated to ten toothpaste groups (n = 12): without fluoride or ß-CaGPm or ß-CaGPn (Negative control), 1100 ppm F (1100 F), and 1100 ppm F plus 0.125%, 0.25%, 0.5%, and 1.0% of ß-CaGPm or ß-CaGPn. Blocks were treated two times per day with toothpaste slurry and subjected to five pH cycles (demineralizing and remineralizing solutions) at 37 °C. The final surface hardness, percentage of surface hardness loss (%SH), cross-sectional hardness (ΔKHN), and profile analysis and lesion depth subsurface were analysed using polarized light microscopy (PLM). Fluoride (F), calcium (Ca), and phosphorus (P) concentrations were also measured. Data were analysed using ANOVA and Student-Newman-Keuls tests ([alpha] = 0.001). Blocks treated with 1100 F toothpaste containing 0.5%ß-CaGPm or 0.25%ß-CaGPn showed with reduced %SH values when compared with those treated with 1100 F alone (p < 0.001). Reduced lesion depths (ΔKHN and PLM) were observed for the slurry made up of 1100 F and 0.25%ß-CaGPn (p < 0.001). The addition of ß-CaGPm and ß-CaGPn did not influence the enamel F concentration, with the 1100 F/0.25%ß-CaGPn group exhibiting the highest Ca and P enamel concentrations (p < 0.001). Based on the findings of this in vitro study, we can conclude that the fluoride toothpaste produced a superior effect when combined at an appropriate ß-CaGP molar ratio. This effect was achieved with a lower proportion of ß-CaGP in the form of nanometric particles.
Asunto(s)
Fluoruros , Desmineralización Dental , Humanos , Animales , Bovinos , Fluoruros/farmacología , Fluoruros/análisis , Pastas de Dientes/farmacología , Calcio , Glicerofosfatos , Estudios Transversales , Desmineralización Dental/prevención & control , Dureza , Suplementos Dietéticos , Concentración de Iones de HidrógenoRESUMEN
OBJECTIVES: This study aimed to evaluate silver nanoparticles (AgNPs) obtained by a 'green' route associated or not to tyrosol (TYR) against Streptococcus mutans and Candida albicans in planktonic and biofilms states. METHODS: AgNPs were obtained by a 'green' route using pomegranate extract. The minimum inhibitory concentration (MIC) against S. mutans and C. albicans was determined for AgNPs and TYR combined and alone, and fractional inhibitory concentration index (FICI) was calculated. Single biofilms of C. albicans and S. mutans were cultivated for 24 h and then treated with drugs alone or in combination for 24 h. RESULTS: AgNPs and TYR were effective against C. albicans and S. mutans considering planktonic cells alone and combined. The MIC values obtained for C. albicans was 312.5 µg/mL (AgNPs) and 50 mM (TYR) and for S. mutans was 78.1 µg/mL (AgNPs) and 90 mM (TYR). The combination of these antimicrobial agents was also effective against both microorganisms: 2.44 µg/mL/0.08 mM (AgNPs/TYR) for C. albicans and 39.05 µg/mL /1.25 mM (AgNPs/TYR) for S. mutans. However, synergism was observed only for C. albicans (FICI 0.008). When biofilm was evaluated, a reduction of 4.62 log10 was observed for S. mutans biofilm cells treated with AgNPs (p < 0.05, Tukey test). However, the addition of TYR to AgNPs did not improve their action against biofilm cells (p > 0.05). AgNPs combined with TYR demonstrated a synergistic effect against C. albicans biofilms. CONCLUSIONS: These findings suggest the potential use of AgNPs with or without TYR against C. albicans and S. mutans, important oral pathogens. CLINICAL SIGNIFICANCE: AgNPs obtained by a 'green' route combined or not with TYR can be an alternative to develop several types of oral antimicrobial therapies and biomaterials.
Asunto(s)
Antiinfecciosos , Nanopartículas del Metal , Alcohol Feniletílico , Alcohol Feniletílico/análogos & derivados , Plata/farmacología , Antiinfecciosos/farmacología , Alcohol Feniletílico/farmacología , Candida albicans , Biopelículas , Streptococcus mutansRESUMEN
OBJECTIVES: This in situ study aimed to assess the remineralizing effect of a fluoride toothpaste supplemented with ß-calcium glycerophosphate in both micro (ß-CaGPm) and nano-sized forms (ß-CaGPn). METHODS: This blind and cross-over study was performed in 4 phases, each spanning 3 days. Twelve volunteers utilized palatal appliances containing four bovine enamel blocks with artificial caries lesions. Volunteers were randomly assigned to the following treatment groups: Placebo (no F-ß-CaGPm-ß-CaGPn); 1100 ppm F alone (1100F); 1100F plus 0.5% micrometric ß-CaGP (1100F-0.5%ß-CaGPm); and 1100F plus 0.25%nano-sized ß-CaGP (1100F-0.25%ß-CaGPn). Participants were instructed to brush their natural teeth with the palatal appliances in the mouth for 1 min (3 times/day), ensuring that the enamel blocks were exposed to the natural toothpaste slurries. Following each phase, evaluations were conducted to determine the percentage of surface hardness recovery (%SHR), integrated recovery of subsurface hardness (ΔIHR), profile subsurface lesion through polarized light microscopy (PLM), as well as fluoride (F), calcium (Ca), and phosphorus (P) concentrations within the enamel. Data were analyzed by ANOVA and Student-Newman-Keuls test (p < 0.001). RESULTS: Treatment with 1100F-0.25%ß-CaGPn resulted in %SHR â¼69 % and â¼40 % higher when compared to 1100F and 1100F-0.5%ß-CaGPm (p < 0.001). The reduction in lesion body (ΔIHR; PLM) was â¼40 % higher with 1100F-0.25%ß-CaGPn (p < 0.001) compared to 1100F. The addition of ß-CaGPm and ß-CaGPn did not influence enamel F concentration (p > 0.001). Treatment with 1100F-0.25%ß-CaGPn led to an increase in the concentration of Ca and P in the enamel (p < 0.001). CONCLUSION: The addition of 0.25%ß-CaGPn into 1100F formulation increased the bioavailability of calcium and phosphate, promoting a higher remineralizing effect. CLINICAL SIGNIFICANCE: Toothpaste containing 1100F-0.25%ß-CaGPn showed a potential of higher remineralization to 1100 ppm F and 1100 ppm F micrometric ß-CaGP could be a strategy for patients at caries activity.
Asunto(s)
Fluoruros , Pastas de Dientes , Animales , Bovinos , Humanos , Calcio/farmacología , Cariostáticos/farmacología , Estudios Cruzados , Esmalte Dental , Fluoruros/farmacología , Glicerofosfatos/farmacología , Dureza , Remineralización Dental/métodos , Pastas de Dientes/farmacología , Pastas de Dientes/uso terapéuticoRESUMEN
OBJECTIVES: This study assembled and characterized a dual nanocarrier of chlorhexidine (CHX) and fluconazole (FLZ), and evaluated its antibiofilm and cytotoxic effects. METHODS: CHX and FLZ were added to iron oxide nanoparticles (IONPs) previously coated by chitosan (CS) and characterized by physical-chemical analyses. Biofilms from human saliva supplemented with Candida species were grown (72 h) on glass discs and treated (24 h) with IONPs-CS carrying CHX (at 39, 78, or 156 µg/mL) and FLZ (at 156, 312, or 624 µg/mL) in three growing associations. IONPs and CS alone, and 156 µg/mL CHX + 624 µg/mL FLZ (CHX156-FLZ624) were tested as controls. Next, microbiological analyses were performed. The viability of human oral keratinocytes (NOKsi lineage) was also determined (MTT reduction assay). Data were submitted to ANOVA or Kruskal-Wallis, followed by Fisher's LSD or Tukey's tests (α=0.05). RESULTS: Nanocarriers with spherical-like shape and diameter around 6 nm were assembled, without compromising the crystalline property and stability of IONPs. Nanocarrier at the highest concentrations was the most effective in reducing colony-forming units of Streptococcus mutans, Lactobacillus spp., Candida albicans, and Candida glabrata. The other carriers and CHX156-FLZ624 showed similar antibiofilm effects, and significantly reduced lactic acid production (p<0.001). Also, a dose-dependent cytotoxic effect against oral keratinocytes was observed for the dual nanocarrier. IONPs-CS-CHX-FLZ and CHX-FLZ significantly reduced keratinocyte viability at CHX and FLZ concentrations ≥7.8 and 31.25 µg/mL, respectively (p<0.05). CONCLUSION: The nanotherapy developed outperformed the effect of the combination CHX-FLZ on microcosm biofilms, without increasing the cytotoxic effect of the antimicrobials administered. CLINICAL SIGNIFICANCE: The dual nanocarrier is a promising topically-applied therapy for the management of oral candidiasis considering that its higher antibiofilm effects allow the use of lower concentrations of antimicrobials than those found in commercial products.
Asunto(s)
Quitosano , Fluconazol , Humanos , Fluconazol/farmacología , Clorhexidina/farmacología , Clorhexidina/química , Candida , Candida albicans , Biopelículas , Quitosano/farmacología , Queratinocitos , Streptococcus mutansRESUMEN
OBJECTIVE: To evaluate the effects of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) on the in vitro remineralization of caries-like lesions. METHODOLOGY: Bovine enamel subsurface lesions (n=168) were selected according to their surface hardness (SH) and randomly divided into seven groups (n=24/group): Placebo (without F/TMP), 4,500 ppm F (4500F), 4500F + 2.5% TMPnano (2.5% Nano), 4500F + 5% TMPnano (5% Nano), 4500F + 5% TMPmicro (5% Micro), 9,000 ppm F (9000F), and 12,300 ppm F (Acid gel). The gels were applied in a thin layer for one minute. Half of the blocks were subjected to pH cycling for six days, whereas the remaining specimens were used for loosely- (calcium fluoride; CaF2) and firmly-bound (fluorapatite; FA) fluoride analysis. The percentage of surface hardness recovery (%SHR), area of subsurface lesion (ΔKHN), CaF2, FA, calcium (Ca), and phosphorus (P) on/in enamel were determined. Data (log10-transformed) were subjected to ANOVA and the Student-Newman-Keuls' test (p<0.05). RESULTS: We observed a dose-response relation between F concentrations in the gels without TMP for %SHR and ΔKHN. The 2.5% Nano and 5% Micro reached similar %SHR when compared with 9000F and Acid gels. For ΔKHN, Placebo and 5% Nano gels had the highest values, and 5% Micro, 2.5% Nano, 9000F, and Acid gels, the lowest. All groups had similar retained CaF2 values, except for Placebo and Acid gel. We verified observed an increase in Ca concentrations in nano-sized TMP groups. Regarding P, TMP groups showed similar formation and retention to 9000F and Acid. CONCLUSION: Adding 2.5% nano-sized or 5% micrometric TMP to low-fluoride gels lead to enhanced in vitro remineralization of artificial caries lesions.
Asunto(s)
Caries Dental , Desmineralización Dental , Animales , Bovinos , Cariostáticos , Caries Dental/tratamiento farmacológico , Susceptibilidad a Caries Dentarias , Fluoruros/farmacología , Fluoruros/análisis , Geles , Dureza , Fluoruro de Sodio , Desmineralización Dental/tratamiento farmacológico , Remineralización DentalRESUMEN
OBJECTIVE: Regular use of toothpaste with fluoride (F) concentrations of ≥ 1000 ppm has been shown to contribute to reducing caries increment. However, when used by children during the period of dental development, it can lead to dental fluorosis. In this study, we aimed to evaluate the in vitro effect of a toothpaste formulation with reduced fluoride (F) concentration (200 ppm) supplemented with sodium trimetaphosphate (TMP: 0.2%), Xylitol (X:16%), and Erythritol (E: 4%) on dental enamel demineralization. METHODOLOGY: Bovine enamel blocks were selected according to initial surface hardness (SHi) and then divided into seven experimental toothpaste groups (n=12). These groups included 1) no F-TMP-X-E (Placebo); 2) 16% Xylitol and 4% Erythritol (X-E); 3) 16% Xylitol, 4% Erythritol and 0.2%TMP (X-E-TMP); 4) 200 ppm F (no X-E-TMP: (200F)); 5) 200 ppm F and 0.2% TMP (200F-TMP); 200 ppm F, 16% Xylitol, 4% Erythritol, and 0.2% TMP (200F-X-E-TMP); and 7) 1,100 ppm F (1100F). Blocks were individually treated 2×/day with slurries of toothpastes and subjected to a pH cycling regimen for five days (DES: 6 hours and RE: 18 hours). Then, the percentage of surface hardness loss (%SH), integrated loss of subsurface hardness (ΔKHN), fluoride (F), calcium (Ca), and phosphorus (P) in enamel were determined. The data were analyzed by ANOVA (1-criterion) and the Student-Newman-Keuls test (p<0.001). RESULTS: We found that the 200F-X-E-TMP treatment reduced %SH by 43% compared to the 1100F treatments (p<0.001). The ΔKHN was ~ 65% higher with 200F-X-E-TMP compared to 1100F (p<0.001). The highest concentration of F in enamel was observed on the 1100F treatment (p<0.001). The 200F-X-E-TMP treatment promote higher increase of Ca and P concentration in the enamel (p<0.001). CONCLUSION: The association of 200F-X-E-TMP led to a significant increase of the protective effect on enamel demineralization compared to the 1100F toothpaste.
Asunto(s)
Fluoruros , Desmineralización Dental , Niño , Animales , Bovinos , Humanos , Fluoruros/farmacología , Pastas de Dientes/uso terapéutico , Xilitol/farmacología , Xilitol/uso terapéutico , Desmineralización Dental/tratamiento farmacológico , Esmalte Dental , Dureza , Calcio/farmacología , Cariostáticos/farmacología , Fluoruro de Sodio/farmacologíaRESUMEN
Abstract Regular use of toothpaste with fluoride (F) concentrations of ≥ 1000 ppm has been shown to contribute to reducing caries increment. However, when used by children during the period of dental development, it can lead to dental fluorosis. Objective: In this study, we aimed to evaluate the in vitro effect of a toothpaste formulation with reduced fluoride (F) concentration (200 ppm) supplemented with sodium trimetaphosphate (TMP: 0.2%), Xylitol (X:16%), and Erythritol (E: 4%) on dental enamel demineralization. Methodology: Bovine enamel blocks were selected according to initial surface hardness (SHi) and then divided into seven experimental toothpaste groups (n=12). These groups included 1) no F-TMP-X-E (Placebo); 2) 16% Xylitol and 4% Erythritol (X-E); 3) 16% Xylitol, 4% Erythritol and 0.2%TMP (X-E-TMP); 4) 200 ppm F (no X-E-TMP: (200F)); 5) 200 ppm F and 0.2% TMP (200F-TMP); 200 ppm F, 16% Xylitol, 4% Erythritol, and 0.2% TMP (200F-X-E-TMP); and 7) 1,100 ppm F (1100F). Blocks were individually treated 2×/day with slurries of toothpastes and subjected to a pH cycling regimen for five days (DES: 6 hours and RE: 18 hours). Then, the percentage of surface hardness loss (%SH), integrated loss of subsurface hardness (ΔKHN), fluoride (F), calcium (Ca), and phosphorus (P) in enamel were determined. The data were analyzed by ANOVA (1-criterion) and the Student-Newman-Keuls test (p<0.001). Results: We found that the 200F-X-E-TMP treatment reduced %SH by 43% compared to the 1100F treatments (p<0.001). The ΔKHN was ~ 65% higher with 200F-X-E-TMP compared to 1100F (p<0.001). The highest concentration of F in enamel was observed on the 1100F treatment (p<0.001). The 200F-X-E-TMP treatment promote higher increase of Ca and P concentration in the enamel (p<0.001). Conclusion: The association of 200F-X-E-TMP led to a significant increase of the protective effect on enamel demineralization compared to the 1100F toothpaste.
RESUMEN
Abstract Objective To evaluate the effects of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) on the in vitro remineralization of caries-like lesions. Methodology Bovine enamel subsurface lesions (n=168) were selected according to their surface hardness (SH) and randomly divided into seven groups (n=24/group): Placebo (without F/TMP), 4,500 ppm F (4500F), 4500F + 2.5% TMPnano (2.5% Nano), 4500F + 5% TMPnano (5% Nano), 4500F + 5% TMPmicro (5% Micro), 9,000 ppm F (9000F), and 12,300 ppm F (Acid gel). The gels were applied in a thin layer for one minute. Half of the blocks were subjected to pH cycling for six days, whereas the remaining specimens were used for loosely- (calcium fluoride; CaF2) and firmly-bound (fluorapatite; FA) fluoride analysis. The percentage of surface hardness recovery (%SHR), area of subsurface lesion (ΔKHN), CaF2, FA, calcium (Ca), and phosphorus (P) on/in enamel were determined. Data (log10-transformed) were subjected to ANOVA and the Student-Newman-Keuls' test (p<0.05). Results We observed a dose-response relation between F concentrations in the gels without TMP for %SHR and ΔKHN. The 2.5% Nano and 5% Micro reached similar %SHR when compared with 9000F and Acid gels. For ΔKHN, Placebo and 5% Nano gels had the highest values, and 5% Micro, 2.5% Nano, 9000F, and Acid gels, the lowest. All groups had similar retained CaF2 values, except for Placebo and Acid gel. We verified observed an increase in Ca concentrations in nano-sized TMP groups. Regarding P, TMP groups showed similar formation and retention to 9000F and Acid. Conclusion Adding 2.5% nano-sized or 5% micrometric TMP to low-fluoride gels lead to enhanced in vitro remineralization of artificial caries lesions.
RESUMEN
In order to improve the anticaries effects of fluoridated products, the supplementation of these products has been considered a promising alternative for caries control. This study evaluated the effects of sodium hexametaphosphate (HMP) and/or fluoride (F) on the inorganic components and pH of Streptococcus mutans and Candida albicans dual-species biofilms. The biofilms were treated 72, 78, and 96 h after the beginning of their formation with 0.25, 0.5, or 1% HMP-containing solutions with or without F (500 ppm, as sodium fluoride). F-containing solutions (500 ppm and 1100 ppm) and artificial saliva were used as controls. The biofilms were exposed to a 20% sucrose solution after the third treatment. Along with the biofilm pH, the concentrations of F, calcium, phosphorus (P), and HMP were determined. HMP, combined with F, increased F levels and decreased P levels in the biofilm fluid compared to that of the solution with 500 ppm F. Exposure to sucrose decreased the concentrations of all ions in the biomass, except for HMP; 1% HMP, combined with F, promoted the highest pH. It can be concluded that HMP affected the inorganic composition of the biofilm and exerted a buffering effect on the biofilm pH.
RESUMEN
OBJECTIVES: This study evaluated the effects of sodium hexametaphosphate microparticles (HMPmicro) or nanoparticles (HMPnano) on the growth of saliva-derived microcosm biofilms MATERIALS AND METHODS: Saliva-derived biofilms were formed on glass coverslips for 24 h. Thereafter, Streptococcus mutans (C180-2) was incorporated or not into the biofilms. From that time point onwards, solutions containing 0.2% HMPmicro or HMPnano, combined or not with 220 ppm F, were constantly present in the culture medium. In addition, 220 ppm F alone (220F) and McBain medium without any compound were also tested as positive and negative controls (CTL), respectively. After 96 h, the biofilms were plated on anaerobic blood agar or sucrose agar bacitracin for total and S. mutans CFU-counting, respectively. Biofilms' lactic acid production was analysed spectrophotometrically. Data were submitted to ANOVA or Kruskal-Wallis' tests, followed by Student-Newman-Keuls' test (p<0.05; n=12). RESULTS: HMPmicro or HMPnano led to significantly lower lactic acid production, and significant reductions in total CFU-counting in microcosm biofilms, supplemented or not with S. mutans, in comparison to both controls, with significant differences between 220F and CTL. No significant differences were observed among the groups treated with HMPmicro or HMPnano (with or without F). The same trend was seen for S. mutans CFU-counting, in biofilms supplemented with S. mutans. CONCLUSIONS: HMP significantly reduced total and S. mutans CFU counts, as well as lactic acid production by saliva-derived microcosm biofilms. CLINICAL RELEVANCE: These findings in saliva-derived microcosm biofilms suggest that HMP stands as a promising alternative for the control of cariogenic biofilms.
Asunto(s)
Nanopartículas , Saliva , Agar/farmacología , Biopelículas , Humanos , Ácido Láctico/farmacología , Fosfatos , Streptococcus mutansRESUMEN
OBJECTIVE: To evaluate the effect of treatment with fluoridated toothpaste supplemented with a combination of sodium trimetaphosphate (TMP) and casein phosphopeptide-amorphous calcium phosphate (MI Paste Plus®) on the demineralization of dental enamel. METHODS: Bovine enamel blocks selected by initial surface hardness (SHi) were randomly allocated into six groups (n = 12), according to the test toothpastes: (1) without F-TMP-MI Paste Plus® (Placebo); (2) 1100 ppm F (1100F); (3) MI Paste Plus®; (4) 1100F + MI Paste Plus® (1100F-MI Paste Plus), (5) 1100F + 3 % TMP (1100F-TMP); and (6) 1100F-TMP + MI Paste Plus® (1100F-TMP-MI Paste Plus). Blocks were treated two times per day with slurries of toothpaste (1 min), and groups 4 and 6 received an application of MI Paste Plus (3 min). Next, the samples were subjected to five pH cycles (demineralizing/remineralizing solutions) at 37 °C, to produce subsurface enamel lesions.Thereafter, the blocks were maintained for 2 days in fresh remineralizing solution. After pH cycling, the following were obtained: percentage of surface hardness loss (%SH); integrated loss of subsurface hardness (ΔKHN); profile analysis and lesion depth subsurface through polarized light microscopy (PLM); scanning electron microscopy (SEM); and fluoride (F), calcium (Ca), and phosphorus (P) in the enamel. The data were subjected to ANOVA (1-criterion), followed by the Student-Newman-Keuls test (p < 0.001). RESULTS: The 1100F-TMP-MI Paste Plus group showed better results for SHR, ΔKHN, and PLM (p < 0.001). The F concentration was similar among all groups (p > 0.001). The 1100F-TMP-MI Paste Plus group showed the highest concentration of Ca and P in the enamel (p < 0.001). CONCLUSION: The application of 1100F-TMP-MI Paste Plus promoted a higher inhibitory effect against enamel demineralization. CLINICAL SIGNIFICANCE: The combination of treatments with F, TMP, and MI Paste Plus® can be an effective alternative to improve the oral health of individuals, especially those with high activity of dental caries and at high risk for its development.
Asunto(s)
Caries Dental , Desmineralización Dental , Animales , Fosfatos de Calcio , Cariostáticos , Caseínas/farmacología , Bovinos , Esmalte Dental , Fluoruros , Dureza , Humanos , Fosfopéptidos , Polifosfatos , Remineralización Dental , Pastas de Dientes/farmacologíaRESUMEN
OBJECTIVE: To evaluate the effects of combination of treatments with fluoridated toothpastes supplemented with sodium trimetaphosphate (TMP) and casein phosphopeptide-amorphous calcium phosphate (MI Paste Plus®), on the remineralization of dental enamel. DESIGN: Enamel blocks with artificial caries were randomly allocated into six groups (n = 12), according to the toothpastes: 1) without F-TMP-MI Paste Plus® (Placebo); 2) 1100 ppm F (1100 F), 3) MI Paste Plus®, 4) 1100 F + MI Paste Plus® (1100 F-MI Paste Plus®), 5) 1100 F + 3% TMP (1100 F-TMP) and 6) 1100 F-TMP + MI Paste Plus® (1100 F-TMP-MI Paste Plus®). Blocks were treated 2×/day with slurries of toothpastes (1 min). Furthermore, groups 4 and 6 received the application of MI Paste Plus® for 3 min. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); profile analysis and lesion depth subsurface through polarized light microscopy (PLM), confocal laser scanning microscopy (LSCM), scanning electron microscopy (SEM), fluoride (F), calcium (Ca), phosphorus (P) concentrations in the enamel were determined. The data were analyzed by ANOVA (1-criterion) and Student-Newman-Keuls test (p < 0.001). RESULTS: 1100 F-TMP-MI Paste Plus® group showed the best results of %SHR, ΔKHN and PLM (p < 0.001). F concentration was similar between the 1100 F, 1100 F-MI Paste Plus®, and 1100 F-TMP-MI Paste Plus® groups (p > 0.001). 1100 F-TMP-MI Paste Plus® group showed the highest concentration of Ca and P in the enamel (p < 0.001). CONCLUSION: The association of 1100 F-TMP and MI Paste Plus® led to a significant increase in the remineralization of initial carious lesions.
Asunto(s)
Fosfatos de Calcio/farmacología , Cariostáticos/farmacología , Esmalte Dental/efectos de los fármacos , Fluoruros/farmacología , Polifosfatos/farmacología , Remineralización Dental , Caseínas/farmacología , Caries Dental/tratamiento farmacológico , Humanos , Técnicas In Vitro , Fosfopéptidos/farmacología , Distribución Aleatoria , Pastas de Dientes/farmacologíaRESUMEN
OBJECTIVES: To evaluate in vitro the effect of neutral pH topical gels with reduced fluoride concentration (F), supplemented or not with sodium hexametaphosphate (HMP) on the remineralization of dental enamel, using a pH-cycling model. Materials and methods Bovine enamel blocks with caries-like lesions were randomly treated with five gels (nâ¯=â¯24/group): without F/HMP (Placebo); 4500â¯ppm F (4500F), 4500F plus 9% HMP (4500Fâ¯+â¯HMP); 9000â¯ppm F (9000F); and 12,300â¯ppm F (Acid gel). After pH-cycling, the percentage of surface hardness recovery (%SHR), integrated loss of subsurface hardness (ΔKHN), and concentrations of loosely- (CaF2) and firmly-bound (FA) fluoride formed and retained in/on enamel were determined. The results were analyzed by ANOVA followed by the Student-Newman-Keuls test (pâ¯<â¯0.001). RESULTS: The 4500Fâ¯+â¯HMP gel promoted the highest %SHR among all groups; the lowest ΔKHN was achieved by 4500Fâ¯+â¯HMP and Acid gel, without significant differences between these. The Acid gel group presented the highest CaF2 and FA formed and retained on/in enamel (pâ¯<â¯0.001). CONCLUSION: Based on the present results, the addition of 9% sodium hexametaphosphate to a gel with reduced fluoride concentration (4500F) was able to significantly enhance the remineralization of artificial carious lesions in vitro when compared to 4500F, reaching protective levels similar to an acidic formulation with â¼3-fold higher fluoride concentration.
Asunto(s)
Esmalte Dental/efectos de los fármacos , Fluoruros Tópicos/farmacología , Fluoruros/farmacología , Fosfatos/farmacología , Desmineralización Dental/prevención & control , Remineralización Dental/métodos , Animales , Fluoruro de Calcio/farmacología , Cariostáticos/farmacología , Bovinos , Caries Dental/prevención & control , Fluoruros/administración & dosificación , Fluoruros Tópicos/administración & dosificación , Geles , Dureza/efectos de los fármacos , Concentración de Iones de Hidrógeno , Técnicas In Vitro , Fosfatos/administración & dosificación , Propiedades de Superficie/efectos de los fármacosRESUMEN
OBJECTIVE: This study evaluated the effect of toothpastes containing 1100ppm F associated or not with micrometric or nano-sized sodium trimetaphosphate (TMP) on enamel demineralization in vitro, using a pH cycling model. DESIGN: Bovine enamel blocks (4mm×4mm, n=96) were randomly allocated into eight groups (n=12), according to the test toothpastes: Placebo (without fluoride or TMP); 1100ppm F (1100F); 1100F plus micrometric TMP at concentrations of 1%, 3% or 6%; and 1100F plus nanosized TMP at 1%, 3% or 6%. Blocks were treated 2×/day with slurries of toothpastes and submitted to a pH cycling regimen for five days. Next, final surface hardness (SHf), integrated hardness loss (IHL), differential profile of integrated hardness loss (ΔIHL) and enamel fluoride (F) concentrations were determined. Data were analyzed by ANOVA and Student-Newman-Keuls' test (p<0.05). RESULTS: The use of 1100F/3%TMPnano led to SHf 30% higher (p<0.001) and IHLâ¼80% lower (p<0.001) when compared to 1100F. This toothpaste also resulted in â¼64% reduction of mineral loss (ΔIHL) when compared to 1100F. Moreover, the addition of nano-sized TMP promoted increases in enamel F uptake of 90%, 160% and 100%, respectively for the concentrations of 1%, 3% and 6%, when compared to 1100F (p<0.001). CONCLUSION: The addition of nano-sized TMP at 3% to a conventional toothpaste significantly decreased enamel demineralization when compared to its counterparts without TMP or supplemented with micrometric TMP.
Asunto(s)
Fluoruros/farmacología , Polifosfatos/farmacología , Desmineralización Dental/tratamiento farmacológico , Pastas de Dientes/farmacología , Animales , Bovinos , Concentración de Iones de Hidrógeno , Técnicas In Vitro , Ensayo de Materiales , Nanoestructuras , Propiedades de Superficie , Pastas de Dientes/químicaRESUMEN
OBJECTIVES: The present study evaluated fluoride (F) and calcium (Ca) concentrations in the biofilm fluid formed in situ under cariogenic challenge after using F dentifrices supplemented or not with sodium trimetaphosphate (TMP) or calcium glycerophosphate (CaGP). METHODS: Volunteers (n = 12) were randomly divided into 5 groups according to the toothpastes used: placebo (without F, CaGP or TMP), 1100 ppm F (1100F) and low-fluoride dentifrice (LFD, 550 ppm F) with no supplementation (550F) or supplemented with 1 % TMP (550F-TMP) or 0.25 % CaGP (550F-CaGP). In each phase, volunteers wore palatal appliances containing 4 bovine enamel blocks. Cariogenic challenge was performed with 30 % sucrose solution, 6 times/day. On the morning of the eigth day, biofilm samples were collected 12 h and 1 h after brushing and cariogenic challenge. F and Ca analyses in the biofilm fluid were performed with the inverted electrode after buffering with TISAB III and using the Arsenazo III method, respectively. Data were submitted to two-way ANOVA (repeated measures) and Student-Newman-Keuls test (p < 0.05). RESULTS: A dose-response relationship was verified between F concentrations in the dentifrices and in the biofilm fluid. Significant differences were observed among placebo, 550F, and 1100F only 1 h after brushing, without statistical differences among 550F, 550F-TMP, and 550F-CaGP. No defined trend was observed among the groups regarding Ca concentrations, with the highest values seen for placebo and 550F-CaGP. CONCLUSION: The anticaries effect of LFDs supplemented with CaGP or TMP cannot be related to an increased availability of F and Ca in the biofilm fluid. CLINICAL SIGNIFICANCE: The better performance of LFDs containing CaGP or TMP shown in previous studies should be attributed to their ability to interact with tooth enamel and with the biofilm, rather to their effect on the biofilm fluid.
Asunto(s)
Biopelículas/efectos de los fármacos , Calcio/análisis , Dentífricos/farmacología , Fluoruros/análisis , Glicerofosfatos/farmacología , Polifosfatos/farmacología , Adulto , Estudios Cruzados , Dentífricos/química , Relación Dosis-Respuesta a Droga , Método Doble Ciego , Femenino , Glicerofosfatos/química , Humanos , Masculino , Polifosfatos/química , Cepillado DentalRESUMEN
AIM: This study screened plants from Brazilian Pantanal for Candida albicans antibiofilm activity. MATERIAL & METHODS: Sixty extracts were obtained from ten plants using different extraction methods. Antifungal activity was assessed. Effects on biofilm inhibition and disruption and cytotoxicity were also evaluated. The most active extract was chemically characterized. RESULTS: Buchenavia tomentosa ethanolic extract showed noticeable antifungal activity and was selected for biofilm experiments. Subinhibitory concentration of extract inhibited fungal adhesion. Maximum killing reached 90% of C. albicans cells in suspension and 65% of cells in biofilms. The active extract was noncytotoxic. Chemical characterization showed the presence of phenols. Ellagic and gallic acids showed activity on C. albicans. CONCLUSION: B. tomentosa extract and its isolated compound, ellagic acid, presented antibiofilm activity and low toxicity.
Asunto(s)
Antifúngicos/farmacología , Biopelículas/efectos de los fármacos , Candida albicans/efectos de los fármacos , Extractos Vegetales/farmacología , Brasil , Células CACO-2 , Combretaceae/química , Ácido Elágico/farmacología , Ácido Gálico/farmacología , Humanos , Fenoles/farmacologíaRESUMEN
OBJECTIVE: The aim of this study was to evaluate the effect of fluoride dentifrices combined with sodium hexametaphosphate (HMP) on enamel demineralization in vitro. MATERIAL AND METHODS: Enamel bovine blocks were selected by initial surface hardness (SHi) and then divided into five experimental groups (n = 12): placebo (without fluoride and without HMP); 1100 ppm F (1100F); and 1100F associated with HMP at 0.5 % (1100HMP0.5%), 1 % (1100HMP1%), and 2 % of HMP (1100HMP2%). Blocks were submitted to five pH cycles (demineralizing/remineralizing solutions) at 37 °C. After pH cycling, final surface hardness (SHf), percentage of surface hardness loss (%SH), integrated differential hardness (ΔIH), integrated loss of subsurface hardness (ΔKHN), and enamel firmly bound fluoride (F) were determined. Data were submitted to one-way ANOVA, followed by Student-Newman-Keuls test (p < 0.05). RESULTS: Significant differences were observed among all groups regarding %SH and ΔKHN. 1100HMP1% promoted the lowest mineral loss among all groups (p < 0.001), and led to significantly lower demineralization in the deeper regions of the subsurface lesion when compared with the other HMP-containing toothpastes (p < 0.001). Significantly higher mineral loss was observed for 1100HMP2% when compared to the other fluoridated dentifrices, mainly in the outer part of the lesion (p < 0.001). Enamel F uptake was similar for 1100F and 1100HMP1% but significantly reduced for other HMP concentrations. CONCLUSION: The supplementation of a 1100-ppm F dentifrice with 1 % HMP promoted a higher inhibitory effect against enamel demineralization when compared to a dentifrice containing the same amount of fluoride in vitro. CLINICAL RELEVANCE: This dentifrice could potentially be indicated to patients at high risk of caries.