Biosynthesis of Silver Nanoparticles Using Salvia pratensis L. Aerial Part and Root Extracts: Bioactivity, Biocompatibility, and Catalytic Potential.

The aim of this research was the synthesis of silver nanoparticles (SPA- and SPR-AgNPs) using the aqueous extracts of the aerial (SPA) and the root (SPR) parts of the plant Salvia pratensis L., their characterization, reaction condition optimization, and evaluation of their biological and catalytic activity. UV-Vis spectroscopy, X-ray powder diffraction (XRPD), scanning electron microscopy with EDS analysis (SEM/EDS), and dynamic light scattering (DLS) analysis were utilized to characterize the nanoparticles, while Fourier transform infrared (FTIR) spectroscopy was used to detect some functional groups of compounds present in the plant extracts and nanoparticles. The phenolic and flavonoid contents, as well as the antioxidant activity of the extracts, were determined spectrophotometrically. The synthesized nanoparticles showed twice-higher activity in neutralizing 2,2'-azino-bis(3-ethylbenzothiazoline-6-sulfonic acid) (ABTS+) compared with the respective extracts. SPR-AgNPs exhibited strong antimicrobial activity against almost all of the tested bacteria (<0.0039 mg/mL) and fungal strains, especially against the genus Penicillium (<0.0391 mg/mL). Moreover, they were fully biocompatible on all the tested eukaryotic cells, while the hemolysis of erythrocytes was not observed at the highest tested concentration of 150 µg/mL. The catalytic activity of nanoparticles toward Congo Red and 4-nitrophenol was also demonstrated. The obtained results confirm the possibility of the safe application of the synthesized nanoparticles in medicine and as a catalyst in various processes.

Green Synthesis of Silver Nanoparticles Using Salvia verticillata and Filipendula ulmaria Extracts: Optimization of Synthesis, Biological Activities, and Catalytic Properties.

The study's objective was to obtain silver nanoparticles (SVAgNP and FUAgNP) using aqueous extracts of Salvia verticillata and Filipendula ulmaria. The optimal conditions for nanoparticle synthesis were determined and obtained; nanoparticles were then characterized using UV-Vis, Fourier-transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), Dynamic Light Scattering (DLS), Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM/EDS). SVAgNP and FUAgNP possessed a crystalline structure with 48.42% and 60.41% silver weight, respectively. The highest percentage of nanoparticles in the solution had a diameter between 40 and 70 nm. In DPPH˙ and ABTS˙+ methods, FUAgNP (IC50 15.82 and 59.85 µg/mL, respectively) demonstrated a higher antioxidant capacity than SVAgNP (IC50 73.47 and 79.49 µg/mL, respectively). Obtained nanoparticles also showed pronounced antibacterial activity (MIC ˂ 39.1 µg/mL for most of the tested bacteria), as well as high biocompatibility with the human fibroblast cell line MRC-5 and significant cytotoxicity on some cancer cell lines, especially on the human colon cancer HCT-116 cells (IC50 31.50 and 66.51 µg/mL for SVAgNP and FUAgNP, respectively). The nanoparticles demonstrated high catalytic effectiveness in degrading Congo red dye with NaBH4. The results showed a rapid and low-cost methodology for the synthesis of AgNPs using S. verticillata and F. ulmaria with promising biological potential.