Fabrication and release property of self-assembled garlic essential oil-amylose inclusion complex by pre-gelatinization coupling with high-speed shear.

Our aim was to investigate the preparation of self-assembled garlic essential oil-amylose inclusion complexes (SGAs) using garlic essential oil (GEO) and corn starch (CS), and evaluated their release properties. SGAs were fabricated by pre-gelatinization coupling with high-speed shear at different GEO-CS mass ratios. When the mass ratio of GEO to pre-gelatinized corn starch was set at 15 % (SGA-15 %), with a fixed shear rate of 9000 rpm and a shear time of 30 min, the allicin content was 0.573 ± 0.023 mg/g. X-ray diffraction (XRD) results revealed a starch V-type crystalline structure in SGAs with peaks at 13.0°, 18.0°, and 20.0° (2θ). Fourier Transform Infrared (FTIR) spectra of SGAs displayed a shift in the characteristic peak of diallyl trisulfide from 987.51 cm-1 to 991.45 cm-1. Scanning electron microscope (SEM) images revealed that SGAs exhibited lamellar structures covered with small granules. SGAs exhibited higher residual mass (approximately 12 %) than other samples. The resistant starch content of SGAs increased from 10.1 % to 18.4 % as GEO contents varied from 5 % to 15 %. In vitro digestion tests showed that about 53.21 % of allicin remained in SGA-15 % after 8 h. Therefore, this dual treatment can be a new method for fabricating controlled-release inclusion complexes of guest molecules.