Biodegradable L-lysine-modified amino black phosphorus/poly(l-lactide-coε-caprolactone) nanofibers with enhancements in hydrophilicity, shape recovery and osteodifferentiation properties.

Biodegradable poly-(lactide-coε-caprolactone) (PLCL) scaffolds have opened new perspectives for tissue engineering due to their nontoxic and fascinating functionality. Herein, a black phosphorus-based biodegradable material with a combination of promising enhanced hydrophilicity, shape recovery and osteodifferentiation properties was proposed. First, amino black phosphorous (BP-NH2) was prepared by a simple ball milling method. Then, L-lysine-modified black phosphorous (L-NH-BP) was formed by hydrogen bonding between L-lysine and amino BP and integrated into PLCL to form PLCL/L-NH-BP composite fibers. The scaffolds had excellent shape recovery and shape fixity properties. Moreover, based on gene expression and protein level assessment, the scaffolds could enhance the expression of alkaline phosphatase (ALP) and bone morphogenetic protein 2 (BMP2), simultaneously improving the mineralization ability of bone mesenchymal stem cells. Specifically, this new composite material was experimentally verified to be degradable under mild conditions. This strategy provided new insight into the design of multifunctional materials for diverse applications.

Natural antioxidant functionalization for fabricating ambient-stable black phosphorus nanosheets toward enhancing flame retardancy and toxic gases suppression of polyurethane.

Herein, as a natural antioxidant, tannin (TA) is firstly used to functionalize black phosphorous (BP) nanosheets to improve the ambient stability and toxic suppression, thus decreasing the fire hazards of polymer materials. Compared to pure BP nanosheets, higher temperature for thermal oxidation decomposition is achieved for TA-BP nanosheets, directly confirming the ambient stability of TA-BP nanosheets. Meanwhile, from high resolution TEM and XPS results, TA-BP nanosheets after being exposed at air for 10 days present well-organized crystal structure and low POx bonds content. Cone calorimeter results illustrate that the incorporation of 2.0 wt% TA-BP nanosheets significantly decreases the peak value of heat release rate (-56.5 %), total heat release (-43.0 %), CO2 concentration (-57.3 %) of TPU composite. Meanwhile, with addition of low to 1.5 wt%, the release of highly-toxic CO gas is significantly suppressed, confirmed by lower peak value (0.52 mg/m3) and decreased total release amount (-55.1 %). The obviously enlarged tensile strength (36.7 MPa) and desirable elongation at break (622 %) are also observed. This strategy not only firstly adopts bio-based antioxidant to impart excellent environmental stability for BP nanosheets, but also promotes the promising potentials of BP nanosheets in the fire safety application of polymer composites.