Effects of different concentrations of bromelain and papain enzymes on shear bond strength of composite resin to deep dentin using an etch-and-rinse adhesive system.

BACKGROUND: The dentin substrate can be modified by proteolytic agents, which may affect the bonding strength of adhesive systems to the treated dentin surface. Papain, a cysteine protease enzyme with antibacterial and anti-inflammatory properties, can be used for deproteinization of dentin. An alternative deproteinizing enzyme is bromelain. OBJECTIVES: This study aimed to evaluate the impact of deproteinization on the shear bond strength (SBS) of composite resin to deep dentin using different concentrations of bromelain and papain. MATERIAL AND METHODS: Sixty upper premolars were extracted and randomly divided into 5 groups (n = 12 per group). In all groups, the dentin surface was etched with 37% phosphoric acid. Group 1 did not receive any enzyme treatment, group 2 was treated with a 10% papain solution, group 3 was treated with a 15% papain solution, group 4 was treated with a 6% bromelain solution, and group 5 was treated with a 10% bromelain solution. After applying an etch-and-rinse adhesive system, the specimens were restored with composite resin and the SBS was measured. RESULTS: Statistically significant differences were found between groups 2 and 3 (10% papain and 15% papain, p = 0.004), groups 2 and 4 (10% papain and 6% bromelain, p = 0.017), groups 4 and 5 (6% bromelain and 10% bromelain, p = 0.021), and groups 3 and 5 (15% papain and 10% bromelain, p = 0.005). CONCLUSIONS: Deproteinization with papain and bromelain at different concentrations after acid etching did not affect the SBS of composite resin to deep dentin when using an etch-and-rinse adhesive system. However, the group deproteinized with 15% papain demonstrated a higher SBS than the group deproteinized with 10% papain, and the group deproteinized with 6% bromelain showed a higher SBS compared to the group deproteinized with 10% bromelain.

Evaluation of the Effects of Bromelain and Papain Enzymes on Shear Bond Strength of Composite Resin to Enamel.

AIM: This study aimed to evaluate the effects of 6% bromelain and 10% papain enzymes on shear bond strength (SBS) of composite resin to enamel compared to conventional 37% phosphoric acid etching. MATERIALS AND METHODS: 50 human maxillary premolar teeth were randomly divided into 5 groups (G1-G5/n = 10). In G1 and G2, after etching enamel with 37% phosphoric acid for 15 seconds and washing the surface, 10% papain and 6% bromelain enzymes were used, respectively. In G3 and G4, 6% bromelain or 10% papain enzymes were applied on enamel. In G5, the enamel surface was etched with 37% phosphoric acid for 15 seconds. A two-step etch-and-rinse adhesive system (Adper Single Bond 2) was applied. A nanohybrid composite (Z350) was placed using Teflon molds. All the samples were then subjected to the SBS test using a universal testing machine. Data analysis was performed using a one-way ANOVA test followed by the Tukey test. p values less than 0.05 were considered significant. RESULTS: Comparison of the mean SBS between G1, G2, and G5 shows no significant differences (p > 0.05); however, they had higher mean SBS compared with G3 and G4 (p < 0.0001). CONCLUSIONS: The shear bond strength of composite to enamel was not affected significantly using either 6% bromelain or 10% papain enzymes after 37% phosphoric acid application. Moreover, 6% bromelain and 10% papain enzymes were not as effective as 37% phosphoric acid alone.