RESUMEN
Several parameters, including specific surface area, morphology, crystal size, and dopant concentration, play a significant role in improving the photocatalytic performance of ZnO. However, it is still unclear which of these parameters play a significant role in enhancing the photocatalytic activity. Herein, undoped and Mn-, Co-, and Cu-doped platelet-like zinc oxide (ZnO) nanostructures were synthesized via a facile microwave synthetic route, and their ultraviolet (UV) and visible-light-induced photocatalytic activities, by monitoring the gaseous acetaldehyde (CH3CHO) degradation, were systematically investigated. Both the pure and doped ZnO nanostructures were found to be UV-active, as the CH3CHO oxidation photocatalysts with the Cu-doped ZnO one being the most UV-efficient photocatalyst. However, upon visible light exposure, all ZnO-nanostructured samples displayed no photocatalytic activity except the Co-doped ZnO, which showed a measurable photocatalytic activity. The latter suggests that Co-doped ZnO nanostructures are potent candidates for several indoor photocatalytic applications. Various complementary techniques were utilized to improve the understanding of the influence of Mn-/Co-/Cu-doping on the photocatalytic performance of the ZnO nanostructures. Results showed that the synergetic effects of variation in morphology, surface defects, that is, VO, high specific surface areas, and porosity played a significant role in modulating the photocatalytic activity of ZnO nanostructures.
RESUMEN
Single layers of MgF2 and LaF3 were deposited upon superpolished fused-silica and CaF2 substrates by ion-beam sputtering (IBS) as well as by boat and electron beam (e-beam) evaporation and were characterized by a variety of complementary analytical techniques. Besides undergoing photometric and ellipsometric inspection, the samples were investigated at 193 and 633 nm by an optical scatter measurement facility. The structural properties were assessed with atomic-force microscopy, x-ray diffraction, TEM techniques that involved conventional thinning methods for the layers. For measurement of mechanical stress in the coatings, special silicon substrates were coated and analyzed. The dispersion behavior of both deposition materials, which was determined on the basis of various independent photometric measurements and data reduction techniques, is in good agreement with that published in the literature and with the bulk properties of the materials. The refractive indices of the MgF2 coatings ranged from 1.415 to 1.440 for the wavelength of the ArF excimer laser (193 nm) and from 1.435 to 1.465 for the wavelength of the F2 excimer laser (157 nm). For single layers of LaF3 the refractive indices extended from 1.67 to 1.70 at 193 nm to approximately 1.80 at 157 nm. The IBS process achieves the best homogeneity and the lowest surface roughness values (close to 1 nm(rms)) of the processes compared in the joint experiment. In contrast to MgF2 boat and e-beam evaporated coatings, which exhibit tensile mechanical stress ranging from 300 to 400 MPa, IBS coatings exhibit high compressive stress of as much as 910 MPa. A similar tendency was found for coating stress in LaF3 single layers. Experimental results are discussed with respect to the microstructural and compositional properties as well as to the surface topography of the coatings.