It was recently found that LiF:Mg,Cu,P, which is a very well-known thermoluminescent (TL) material, exhibits also quite substantial optically stimulated luminescence (OSL). In the present work a study on the influence of thermal treatment on the LiF:Mg,Cu,P OSL intensity has been performed. The results revealed that the well-known 'gold standard' of 240°C annealing is not appropriate for OSL measurements. The annealing at lower temperatures produced significantly higher OSL intensity. The highest enhancement of the OSL signal, reaching 95% (compared to the initial signal after standard annealing at 240°C/10 min) was obtained after annealing at about 190-200°C/30 min. The OSL emission spectrum of LiF:Mg,Cu,P was also measured and found to be peaked at 360 nm.