Facile construction of lamellar-like phosphorus-based triazole-zinc complex for high-performance epoxy resins.

Epoxy resins (EP) possessing superior flame retardancy, mechanical properties and glass transition temperature are urgently needed to meet the ever-increasing requirement of high performance for the practical application of EP. Herein, lamellar-like phosphorus-based triazole-zinc complex (Zn-PT) was firstly constructed through coordination reaction in a facile condition to address the above issue. The results revealed that Zn-PT was well dispersed in epoxy matrix, and with 3 wt% Zn-PT, the tensile strength, flexural strength and modulus of epoxy composites were remarkably increased from 71, 112 and 2982 MPa of neat epoxy resin (EP) to 80, 162 and 3482 MPa respectively. The glass transition temperature was higher than EP. Besides, the limiting oxygen index (LOI) increased to 28.3%, and UL-94V-1 level was available. Meanwhile, the cone calorimeter test (CCT) results showed that epoxy composites displayed less heat release and smoke production. Generally, this work provides a feasible strategy to prepare high-performance epoxy composites, which has the potential to satisfy the requirement of epoxy in the practical application.

From herbicide to flame retardant: The lamellar-like phosphorus-bridged amitrole toward high fire safety epoxy resin with light smoke and low toxicity.

In an attempt to alleviate the harmful impact of the flammability of epoxy resin on the environment, amitrole, a herbicide, has been converted to a novel flame retardant (PBA) with lamellar morphology through organophosphorus modification. This material has been utilized to fabricate fire safe epoxy thermosets (EP). EP containing 7.5 wt% PBA undergoes quick self-extinguishment upon ignition. This blend displays a high limiting oxygen index (LOI) value of 34%. More importantly, hazardous products (heat, smoke, toxic gases including CO/CO2) released during combustion of EP, are strongly suppressed in the presence of PBA. The mechanical properties of EP-PBA blends are comparable to those of virgin EP. The tensile strength of EP containing PBA is 90% of that of unmodified EP. The flexural strength of PBA blends is somewhat greater than that for EP containing no additive. A tactful strategy for the transformation of amitrole, a potential environmental contaminant to a benign flame retardant for polymers has been developed.