Research on the Dealkalization Treatment of Bauxite Residue and Deep Extraction of Alumina.

Bauxite residue is the bulk solid waste generated by the alumina industry, and the environmental treatment of bauxite residue has always been a focus of attention. In this study, in the high calcium system, the bauxite residue was intensively digestion by the calcification-carbonation method, and the mole ratio of solution, the mass ratio of CaO/SiO2 of the digestion process were changed, so that the high-efficiency dealkalization of bauxite residue was realized and the aluminum oxide in bauxite residue was deeply extracted. The experimental results showed that the calcification process could achieve the recovery of 17.83% alumina at 260°C, reaction duration of 60 min, liquid-solid ratio = 5:1, the mass ratio of CaO/SiO2 = 3.5, and 200 g/L NaOH solution. The whole process can recover 49.61% of alumina from bauxite residue, and 94.4% of alkali in bauxite residue can be removed.

Study on Iron Extraction from High Iron Bauxite Residue by Pyrite Reduction.

A new method of solid-phase reduction magnetic separation with pyrite as a reducing agent was proposed in order to realize resource utilization of high iron bauxite residue while reducing environmental harm. FeS2 powder and high iron bauxite residue powder were uniformly blended and roasted in a closed environment. A magnetic separator was utilized to separate the magnetic iron concentrate at 2400 GS, and the recovery rates were calculated. Experimental results show that the best iron recovery was 91.5% at 1:6 roasted bauxite: residue at 800℃ for 2 h. The recovery of Fe can be improved by reducing high iron bauxite residue with pyrite, and iron in both pyrite and high iron bauxite residue can be recovered simultaneously, alleviating the pressure of iron ore resources and improving its utilization value.

Calcification-Carbonation Method for Bayer Red Mud Treatment: Carbonation Performance of Hydrogarnets.

Hydrogarnets are vital intermediate products in the calcification- carbonation method, which is designed for Bayer red mud treatment. Their carbonation performance greatly depends on SiO2 substitution. In this study, different SiO2-substituted hydrogarnets were synthesized and characterized. Then, batch experiments were performed to evaluate the potential effects of important parameters such as CO2 pressure, and SiO2 substitution degree (x) on the carbonation process. The SiO2 substitution degrees of the hydrogarnets synthesized at 60, 120, 180, and 240°C were 0.27, 0.36, 0.70, and 0.73, respectively. As the SiO2 substitution degree increased, the hydrogarnet carbonation extents gradually declined. With an increase in CO2 pressure, the hydrogarnet carbonation percentages increased gradually and rose from 80.33% to 98.19% within 120 min. The phases detected in the carbonized products were strip-like aragonite as well as some calcite; the Al-rich and Si-rich phases in the carbonized products were amorphous.

Comprehensive Application Technology of Bauxite Residue Treatment in the Ecological Environment: A Review.

The emission of bauxite residue continues to grow with the increase of alumina production capacity, along with the large amounts of bauxite residue currently stored in stockpiles. The exposed problems of high yield, strong alkalinity, low comprehensive utilization rate, and threats to the ecological environment are becoming increasingly prominent. With the strict requirements of environmental protection, improving the comprehensive utilization rate of bauxite residue and bulk consumption of bauxite residue has become an urgent issue to be solved. A large number of researchers have conducted in-depth investigations into the application of bauxite residue over a wide range, and this paper summarizes its application in the environment in recent years, providing guidance for the high value and harmless application of bauxite residue, which can help reduce environmental pollution and human life and health hazards caused by bauxite residue.