RESUMEN
Sorption capacity of four plants (Funaria hygrometrica, Musa acuminata, Brassica juncea and Helianthus annuus) extracts/fractions for uranium, a radionuclide was investigated by EDXRF and tracer studies. The maximum sorption capacity, i.e., 100% (complete sorption) was observed in case of Musa acuminata extract and fractions. Carbohydrate, proteins, phenolics and flavonoids contents in the active fraction (having maximum sorption capacity) were also determined. Further purification of the most active fraction provided three pure molecules, mannitol, sorbitol and oxo-linked potassium oxalate. The characterization of isolated molecules was achieved by using FTIR, NMR, GC-MS, MS-MS, and by single crystal-XRD analysis. Of three molecules, oxo-linked potassium oxalate was observed to have 100% sorption activity. Possible binding mechanism of active molecule with the uranyl cation has been purposed.
Asunto(s)
Plantas/metabolismo , Contaminantes Radiactivos del Suelo/metabolismo , Uranio/metabolismo , Adsorción , Biodegradación Ambiental , Bryopsida/metabolismo , Helianthus/metabolismo , Musa/metabolismo , Planta de la Mostaza/metabolismoRESUMEN
Adsorptive sorbent for bio-aggressive natural aqueous media like seawater was developed by one pot simultaneous synthesis of silver nanoparticles (Ag nps) and poly(ethylene glycol methacrylate phosphate) (PEGMP) by UV-initiator induced photo-polymerization. The photo-polymerization was carried out by irradiating N,N'-dimethylformamide (DMF) solution containing appropriate amounts of the functional monomer (ethylene glycol methacrylate phosphate), UV initiator (α,α'-dimethoxy-α-phenyl acetophenone), and Ag(+) ions with 365 nm UV light in a multilamps photoreactor. To increase mechanical strength, nano-composite sorbent (Ag@PEGMP) was also reinforced with thermally bonded non-woven poly(propylene) fibrous sheet. Transmission electron microscopy (TEM) of the nano-composite sorbent showed uniform distribution of spherical Ag nanoparticles with particles size ranging from 3 to 6 nm. The maximum amount of Ag(0) that could be anchored in the form of nanoparticles were 5±1 and 10±1 wt.% in self-supported PEGMP and poly(propylene) reinforced PEGMP matrices, respectively. Ag@PEGMP sorbent was found to be stable under ambient conditions for a period of six months. Ag@PEGMP composite sorbent did not exhibit growth at all after incubation with pre-grown Escherichia coli cells, and showed non-adherence of this bacteria to the composite. This indicated that composite sorbent has the bio-resistivity due to bacterial repulsion and bactericidal properties of Ag nanoparticles embedded in the PEGMP. Sorption of U(VI) in PEGMP and Ag@PEGMP nano-composite sorbents from well-stirred seawater was studied to explore the possibility of using it for uranium preconcentration from bio-aggressive aqueous streams. The nano-composite sorbent was used to preconcentrate U(VI) from a process aqueous waste stream.