A Bridge-Linked Phosphorus-Containing Flame Retardant for Endowing Vinyl Ester Resin with Low Fire Hazard.

The high flammability of vinyl ester resin (VE) significantly limits its widespread application in the fields of electronics and aerospace. A new phosphorus-based flame retardant 6,6'-(1-phenylethane-1,2 diyl) bis (dibenzo[c,e][1,2]oxaphosphinine 6-oxide) (PBDOO), was synthesized using 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and acetophenone. The synthesized PBDOO was further incorporated with VE to form the VE/PBDOO composites, which displayed an improved flame retardancy with higher thermal stability. The structure of PBDOO was investigated using Fourier transformed infrared spectrometry (FTIR) and nuclear magnetic resonances (NMR). The thermal stability and flame retardancy of VE/PBDOO composites were investigated by thermogravimetric analysis (TGA), vertical burn test (UL-94), limiting oxygen index (LOI), and cone calorimetry. The impacts of PBDOO weight percentage (wt%) on the flame-retardant properties of the formed VE/PBDOO composites were also examined. When applying 15 wt% PBDOO, the formed VE composites can meet the UL-94 V-0 rating with a high LOI value of 31.5%. The peak heat release rate (PHRR) and the total heat release (THR) of VE loaded 15 wt% of PBDOO decreased by 76.71% and 40.63%, respectively, compared with that of untreated VE. In addition, the flame-retardant mechanism of PBDOO was proposed by analyzing pyrolysis behavior and residual carbon of VE/PBDOO composites. This work is expected to provide an efficient method to enhance the fire safety of VE.

Natural antioxidant functionalization for fabricating ambient-stable black phosphorus nanosheets toward enhancing flame retardancy and toxic gases suppression of polyurethane.

Herein, as a natural antioxidant, tannin (TA) is firstly used to functionalize black phosphorous (BP) nanosheets to improve the ambient stability and toxic suppression, thus decreasing the fire hazards of polymer materials. Compared to pure BP nanosheets, higher temperature for thermal oxidation decomposition is achieved for TA-BP nanosheets, directly confirming the ambient stability of TA-BP nanosheets. Meanwhile, from high resolution TEM and XPS results, TA-BP nanosheets after being exposed at air for 10 days present well-organized crystal structure and low POx bonds content. Cone calorimeter results illustrate that the incorporation of 2.0 wt% TA-BP nanosheets significantly decreases the peak value of heat release rate (-56.5 %), total heat release (-43.0 %), CO2 concentration (-57.3 %) of TPU composite. Meanwhile, with addition of low to 1.5 wt%, the release of highly-toxic CO gas is significantly suppressed, confirmed by lower peak value (0.52 mg/m3) and decreased total release amount (-55.1 %). The obviously enlarged tensile strength (36.7 MPa) and desirable elongation at break (622 %) are also observed. This strategy not only firstly adopts bio-based antioxidant to impart excellent environmental stability for BP nanosheets, but also promotes the promising potentials of BP nanosheets in the fire safety application of polymer composites.