Controlling oxygen coordination and valence of network forming cations.

Understanding the structure-property relationship of glass material is still challenging due to a lack of periodicity in disordered materials. Here, we report the properties and atomic structure of vanadium phosphate glasses characterized by reverse Monte Carlo modelling based on neutron/synchrotron X-ray diffraction and EXAFS data, supplemented by Raman and NMR spectroscopy. In vanadium-rich glass, the water durability, thermal stability and hardness improve as the amount of P2O5 increases, and the network former of the glass changes from VOx polyhedra to the interplay between VOx polyhedra and PO4 tetrahedra. We find for the first time that the coordination number of oxygen atoms around a V4+ is four, which is an unusually small coordination number, and plays an important role for water durability, thermal stability and hardness. Furthermore, we show that the similarity between glass and crystal beyond the nearest neighbour distance is important for glass properties. These results demonstrate that controlling the oxygen coordination and valence of the network-forming cation is necessary for designing the properties of glass.

Network topology for the formation of solvated electrons in binary CaO-Al2O3 composition glasses.

Glass formation in the CaO-Al2O3 system represents an important phenomenon because it does not contain typical network-forming cations. We have produced structural models of CaO-Al2O3 glasses using combined density functional theory-reverse Monte Carlo simulations and obtained structures that reproduce experiments (X-ray and neutron diffraction, extended X-ray absorption fine structure) and result in cohesive energies close to the crystalline ground states. The O-Ca and O-Al coordination numbers are similar in the eutectic 64 mol % CaO (64CaO) glass [comparable to 12CaO·7Al2O3 (C12A7)], and the glass structure comprises a topologically disordered cage network with large-sized rings. This topologically disordered network is the signature of the high glass-forming ability of 64CaO glass and high viscosity in the melt. Analysis of the electronic structure reveals that the atomic charges for Al are comparable to those for Ca, and the bond strength of Al-O is stronger than that of Ca-O, indicating that oxygen is more weakly bound by cations in CaO-rich glass. The analysis shows that the lowest unoccupied molecular orbitals occurs in cavity sites, suggesting that the C12A7 electride glass [Kim SW, Shimoyama T, Hosono H (2011) Science 333(6038):71-74] synthesized from a strongly reduced high-temperature melt can host solvated electrons and bipolarons. Calculations of 64CaO glass structures with few subtracted oxygen atoms (additional electrons) confirm this observation. The comparable atomic charges and coordination of the cations promote more efficient elemental mixing, and this is the origin of the extended cage structure and hosted solvated (trapped) electrons in the C12A7 glass.