RESUMEN
This study evaluated the removal of filling material with ProTaper Universal Rotary Retreatment system (PTR) combined with solvents and the influence of solvents on the bond strength (PBS) of sealer to intraradicular dentin after canal reobturation. Roots were endodontically treated and distributed to five groups (n = 12). The control group was not retreated. In the four experimental groups, canals were retreated with PTR alone or in combination with xylol, orange oil, and eucalyptol. After filling material removal, two specimens of each group were analysed by SEM and µCT to verify the presence of filling remnants on root canal walls. The other roots were reobturated and sectioned in 1-mm-thick dentin slices that were subjected to the push-out test. Data were analysed by two-way ANOVA and Tukey's test (α = 0.05). SEM and µCT analysis revealed that all retreatment techniques left filling remnants on canal walls. The control group (3.47 ± 1.21) presented significantly higher (p < 0.05) PBS than the experimental groups. The groups retreated with PTR alone (2.59 ± 0.99) or combined with xylol (2.54 ± 0.77) and orange oil (2.32 ± 0.93) presented similar bond strength (p > 0.05), and differed significantly from the group with eucalyptol (1.89 ± 0.63). The solvents reduced the PBS of the sealer to dentin and no retreatment technique promoted complete removal of filling material.
Asunto(s)
Cavidad Pulpar/efectos de los fármacos , Dentina/efectos de los fármacos , Materiales de Obturación del Conducto Radicular/química , Preparación del Conducto Radicular/métodos , Solventes/química , Análisis de Varianza , Ciclohexanoles/química , Recubrimiento Dental Adhesivo , Instrumentos Dentales , Resinas Epoxi/química , Eucaliptol , Gutapercha , Humanos , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Monoterpenos/química , Aceites de Plantas/química , Reproducibilidad de los Resultados , Retratamiento/instrumentación , Preparación del Conducto Radicular/instrumentaciónRESUMEN
Abstract This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols.
Asunto(s)
Humanos , Recubrimiento Dental Adhesivo/métodos , Dentina/efectos de los fármacos , Ácido Edético/química , Cementos de Resina/química , Hipoclorito de Sodio/química , Raíz del Diente/efectos de los fármacos , Grabado Ácido Dental/métodos , Análisis de Varianza , Fracaso de la Restauración Dental , Dentina/efectos de la radiación , Pruebas de Dureza , Ensayo de Materiales , Microscopía Confocal , Técnica de Perno Muñón , Distribución Aleatoria , Valores de Referencia , Reproducibilidad de los Resultados , Irrigantes del Conducto Radicular/química , Preparación del Conducto Radicular/métodos , Estadísticas no Paramétricas , Propiedades de Superficie/efectos de los fármacos , Raíz del Diente/efectos de la radiación , Terapia por UltrasonidoRESUMEN
Abstract This study evaluated the removal of filling material with ProTaper Universal Rotary Retreatment system (PTR) combined with solvents and the influence of solvents on the bond strength (PBS) of sealer to intraradicular dentin after canal reobturation. Roots were endodontically treated and distributed to five groups (n = 12). The control group was not retreated. In the four experimental groups, canals were retreated with PTR alone or in combination with xylol, orange oil, and eucalyptol. After filling material removal, two specimens of each group were analysed by SEM and µCT to verify the presence of filling remnants on root canal walls. The other roots were reobturated and sectioned in 1-mm-thick dentin slices that were subjected to the push-out test. Data were analysed by two-way ANOVA and Tukey’s test (α = 0.05). SEM and µCT analysis revealed that all retreatment techniques left filling remnants on canal walls. The control group (3.47 ± 1.21) presented significantly higher (p < 0.05) PBS than the experimental groups. The groups retreated with PTR alone (2.59 ± 0.99) or combined with xylol (2.54 ± 0.77) and orange oil (2.32 ± 0.93) presented similar bond strength (p > 0.05), and differed significantly from the group with eucalyptol (1.89 ± 0.63). The solvents reduced the PBS of the sealer to dentin and no retreatment technique promoted complete removal of filling material.
Asunto(s)
Humanos , Cavidad Pulpar/efectos de los fármacos , Dentina/efectos de los fármacos , Materiales de Obturación del Conducto Radicular/química , Preparación del Conducto Radicular/métodos , Solventes/química , Análisis de Varianza , Ciclohexanoles/química , Recubrimiento Dental Adhesivo , Instrumentos Dentales , Resinas Epoxi/química , Gutapercha , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Monoterpenos/química , Aceites de Plantas/química , Reproducibilidad de los Resultados , Retratamiento/instrumentación , Preparación del Conducto Radicular/instrumentaciónRESUMEN
This study aimed to evaluate, by means of scanning electron microscopy (SEM), the cleaning of flattened root canals, varying irrigation/aspiration protocols during biomechanical preparation. Thirdy human mandibular incisors were distributed into three groups (n = 10) according to the aspiration/irrigation protocols: conventional, conventional + brush, and apical negative pressure irrigation. Irrigation procedure was performed with 5 mL of 1% NaOCl at each change of instrument; final irrigation was conducted with 17% EDTA for 5 min. After biomechanical preparation, the roots were sectioned and prepared for SEM analysis. The images obtained were evaluated under 35× and 1,000× magnification by three calibrated examiners, following a double-blind design. All data were analyzed using Kruskal-Wallis and Dunn's post hoc tests (α = 0.05). Canals wherein the conventional method and apical negative pressure irrigation were employed revealed less debris, statistically different from the conventional + brush group (p < 0.05). Regarding the presence of smears, apical negative pressure irrigation was more effective in cleaning, showing lowest scores (p < 0.05), compared with the other tested protocols. Comparing each root canal third revealed that the apical portion was difficult to clean as all the tested protocols showed similar high scores (p > 0.05), both for the presence of debris and smear layer. In conclusion, although none of the studied irrigation/aspiration protocols have completely cleaned flattened root canals, apical negative pressure irrigation was more effective in smear layer removal, whereas the conventional + brush protocol was the least effective in removing the debris and smear layer.
Asunto(s)
Cavidad Pulpar/efectos de los fármacos , Irrigantes del Conducto Radicular/uso terapéutico , Preparación del Conducto Radicular/instrumentación , Preparación del Conducto Radicular/métodos , Desbridamiento/instrumentación , Desbridamiento/métodos , Cavidad Pulpar/anatomía & histología , Dentina/efectos de los fármacos , Desinfectantes/uso terapéutico , Ácido Edético/uso terapéutico , Humanos , Microscopía Electrónica de Rastreo , Reproducibilidad de los Resultados , Capa de Barro Dentinario/terapia , Hipoclorito de Sodio/uso terapéutico , Estadísticas no Paramétricas , Propiedades de Superficie , Factores de Tiempo , Resultado del TratamientoRESUMEN
OBJECTIVE: The purpose of this study was to analyze the effects of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with 1064 nm Nd:YAG and 980 nm diode laser on root dentin microhardness and superficial roughness (with confocal laser scanning microscopy [CLSM]). BACKGROUND DATA: Root canal irrigants are used in an attempt to minimize the negative effects of smear layer. MATERIALS AND METHODS: Twenty-five bovine roots were sectioned longitudinally and divided into five groups (n=10 each): (1) deionized water, (2) 17% EDTA, (3) 17% EDTA with 60 sec manual agitation, (4) 17% EDTA with 50 sec diode laser (2 W) agitation, and (5) 17% EDTA with 50 sec Nd:YAG (1.5 W) laser agitation. Microhardness and superficial roughness values were calculated before and after the procedures at the cervical, middle, and apical root thirds. Microhardness was statistically analyzed using two way ANOVA, paired t test, and Tukey's tests (α=0.05). Roughness was statistically analyzed using Kruskal-Wallis, paired t test, and Student-Newman-Keuls tests (α=0.05%). RESULTS: Statistically significant differences in microhardness and roughness were observed between the deionized water group and others. EDTA with 1064 nm Nd:YAG or 980 nm diode laser presented the lowest microhardness and the highest roughness values and was significantly different from EDTA with manual agitation and EDTA only (p<0.05). However, there were no differences in microhardness or dentin roughness between the root thirds (p>0.05). CLSM analysis showed that the control samples exhibited smoother surfaces than that of the EDTA groups. CONCLUSIONS: Nd:YAG 1064 nm and 980-nm diode laser EDTA agitation caused greater reduction in microhardness and increased roughness of root dentin than EDTA only or EDTA with manual agitation.
Asunto(s)
Ácido Edético , Láseres de Semiconductores , Láseres de Estado Sólido , Terapia por Luz de Baja Intensidad , Raíz del Diente/efectos de la radiación , Raíz del Diente/ultraestructura , Animales , Bovinos , Dureza/efectos de la radiación , Microscopía Electrónica de Rastreo , Irrigantes del Conducto Radicular , Técnicas de Cultivo de TejidosRESUMEN
This study aimed to evaluate, by means of scanning electron microscopy (SEM), the cleaning of flattened root canals, varying irrigation/aspiration protocols during biomechanical preparation. Thirdy human mandibular incisors were distributed into three groups (n = 10) according to the aspiration/irrigation protocols: conventional, conventional + brush, and apical negative pressure irrigation. Irrigation procedure was performed with 5 mL of 1% NaOCl at each change of instrument; final irrigation was conducted with 17% EDTA for 5 min. After biomechanical preparation, the roots were sectioned and prepared for SEM analysis. The images obtained were evaluated under 35× and 1,000× magnification by three calibrated examiners, following a double-blind design. All data were analyzed using Kruskal–Wallis and Dunn’s post hoctests (α = 0.05). Canals wherein the conventional method and apical negative pressure irrigation were employed revealed less debris, statistically different from the conventional + brush group (p < 0.05). Regarding the presence of smears, apical negative pressure irrigation was more effective in cleaning, showing lowest scores (p < 0.05), compared with the other tested protocols. Comparing each root canal third revealed that the apical portion was difficult to clean as all the tested protocols showed similar high scores (p > 0.05), both for the presence of debris and smear layer. In conclusion, although none of the studied irrigation/aspiration protocols have completely cleaned flattened root canals, apical negative pressure irrigation was more effective in smear layer removal, whereas the conventional + brush protocol was the least effective in removing the debris and smear layer.
Asunto(s)
Humanos , Cavidad Pulpar/efectos de los fármacos , Irrigantes del Conducto Radicular/uso terapéutico , Preparación del Conducto Radicular/instrumentación , Preparación del Conducto Radicular/métodos , Desbridamiento/instrumentación , Desbridamiento/métodos , Cavidad Pulpar/anatomía & histología , Dentina/efectos de los fármacos , Desinfectantes/uso terapéutico , Ácido Edético/uso terapéutico , Microscopía Electrónica de Rastreo , Reproducibilidad de los Resultados , Estadísticas no Paramétricas , Propiedades de Superficie , Capa de Barro Dentinario/terapia , Hipoclorito de Sodio/uso terapéutico , Factores de Tiempo , Resultado del TratamientoRESUMEN
The aim of this study was to assess the influence of surface pretreatments of fiber-reinforced posts on flexural strength (FS), modulus of elasticity (ME) and morphology of these posts, as well as the bond strength (BS) between posts and core material. Fifty-two fiber posts (smooth and serrated) were assigned to 4 groups (n=13): no treatment (control), 10% hydrogen peroxide (HP) for 10 min (HP-10), 24% HP for 1 min (HP-24) and airborne-particle abrasion (Al(2)O(3)). To evaluate FS and ME, a 3-point bending test was performed. Three posts of each group were examined by scanning electron microscopy. Composite resin was used as the core build-up and samples were sectioned to obtain microtensile sticks. Data were analyzed by ANOVA and Tukey's test (α=0.05). For FS, significant differences were observed between posts type and surface pretreatment (p<0.05), with the highest means for the smooth posts. Al2O3 provided higher FS than HP-24. Al(2)O(3) promoted higher ME than HP-24 and control. SEM images revealed partial dissolution of the resin matrix in all treated groups. The smooth posts had higher BS and FS than serrated posts (p<0.05). Mechanical properties of the glass fiber posts and the bond strength between posts and composite material were not altered by the surface treatments, except for airborne-particle abrasion that increased the post elastic modulus.
Asunto(s)
Recubrimiento Dental Adhesivo , Grabado Dental/métodos , Materiales Dentales/química , Vidrio/química , Técnica de Perno Muñón/instrumentación , Óxido de Aluminio/química , Resinas Compuestas/química , Diseño de Prótesis Dental , Análisis del Estrés Dental/instrumentación , Módulo de Elasticidad , Resinas Epoxi/química , Humanos , Peróxido de Hidrógeno/química , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Oxidantes/química , Docilidad , Silanos/química , Solubilidad , Estrés Mecánico , Propiedades de Superficie , Temperatura , Resistencia a la Tracción , Factores de Tiempo , Agua/químicaRESUMEN
The aim of this study was to assess the influence of surface pretreatments of fiber-reinforced posts on flexural strength (FS), modulus of elasticity (ME) and morphology of these posts, as well as the bond strength (BS) between posts and core material. Fifty-two fiber posts (smooth and serrated) were assigned to 4 groups (n=13): no treatment (control), 10% hydrogen peroxide (HP) for 10 min (HP-10), 24% HP for 1 min (HP-24) and airborne-particle abrasion (Al2O3). To evaluate FS and ME, a 3-point bending test was performed. Three posts of each group were examined by scanning electron microscopy. Composite resin was used as the core build-up and samples were sectioned to obtain microtensile sticks. Data were analyzed by ANOVA and Tukey's test (α=0.05). For FS, significant differences were observed between posts type and surface pretreatment (p<0.05), with the highest means for the smooth posts. Al2O3 provided higher FS than HP-24. Al2O3 promoted higher ME than HP-24 and control. SEM images revealed partial dissolution of the resin matrix in all treated groups. The smooth posts had higher BS and FS than serrated posts (p<0.05). Mechanical properties of the glass fiber posts and the bond strength between posts and composite material were not altered by the surface treatments, except for airborne-particle abrasion that increased the post elastic modulus.
O objetivo deste estudo foi avaliar a influência do pré-tratamento de superfície dos pinos de fibra de vidro na resistência à flexão (RF), módulo de elasticidade (ME) e morfologia, bem como a resistência de união (RU) entre os pinos e o núcleo de preenchimento. Cinqüenta e dois pinos de fibra de vidro (lisos e serrilhados) foram divididos em 4 grupos (n=13): sem tratamento (controle), peróxido de hidrogênio a 10% por 10 min (HP-10), peróxido de hidrogênio 24% por 1 min (HP-24) e jato de óxido de alumínio (Al2O3). Para avaliar a RF e ME, o ensaio de flexão de 3 pontos foi realizado. Três pinos de cada grupo foram examinados em MEV. Resina composta foi utilizada como núcleo de preenchimento e as amostras foram seccionadas para obter palitos de microtração. Os dados foram analisados por ANOVA e teste de Tukey (α=0,05). Na RF, observou-se diferença estatisticamente significante entre os pinos e tipo de pré-tratamento de superfície (p<0,05), com as maiores médias para os pinos lisos. Al2O3 proporcionou maior RF que HP-24. Al2O3 promoveu maior ME que HP-24 e grupo controle. MEV revelou dissolução parcial da matriz de resina em todos os grupos tratados. Os pinos lisos tiveram a maior RU (p<0,05). Os pinos lisos apresentaram RF e RU superior aos pinos serrilhados (p<0,05). As propriedades mecânicas dos pinos de fibra de vidro e a resistência de união entre os pinos e o material resinoso não foram alterados pelos tratamentos de superfície, com exceção do jato de óxido de alumínio que aumentou o módulo de elasticidade dos pinos.