Effect of Nd:YAG (1064-nm) and Diode Laser (980-nm) EDTA Agitation on Root Dentin Ultrastructure Properties.

OBJECTIVE: The purpose of this study was to analyze the effects of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with 1064 nm Nd:YAG and 980 nm diode laser on root dentin microhardness and superficial roughness (with confocal laser scanning microscopy [CLSM]). BACKGROUND DATA: Root canal irrigants are used in an attempt to minimize the negative effects of smear layer. MATERIALS AND METHODS: Twenty-five bovine roots were sectioned longitudinally and divided into five groups (n=10 each): (1) deionized water, (2) 17% EDTA, (3) 17% EDTA with 60 sec manual agitation, (4) 17% EDTA with 50 sec diode laser (2 W) agitation, and (5) 17% EDTA with 50 sec Nd:YAG (1.5 W) laser agitation. Microhardness and superficial roughness values were calculated before and after the procedures at the cervical, middle, and apical root thirds. Microhardness was statistically analyzed using two way ANOVA, paired t test, and Tukey's tests (α=0.05). Roughness was statistically analyzed using Kruskal-Wallis, paired t test, and Student-Newman-Keuls tests (α=0.05%). RESULTS: Statistically significant differences in microhardness and roughness were observed between the deionized water group and others. EDTA with 1064 nm Nd:YAG or 980 nm diode laser presented the lowest microhardness and the highest roughness values and was significantly different from EDTA with manual agitation and EDTA only (p<0.05). However, there were no differences in microhardness or dentin roughness between the root thirds (p>0.05). CLSM analysis showed that the control samples exhibited smoother surfaces than that of the EDTA groups. CONCLUSIONS: Nd:YAG 1064 nm and 980-nm diode laser EDTA agitation caused greater reduction in microhardness and increased roughness of root dentin than EDTA only or EDTA with manual agitation.

Chemical and Morphological Changes of Primary Teeth Irradiated with Nd:YAG Laser: An Ex Vivo Long-Term Analysis.

OBJECTIVE: The aim of this study was to assess any long-term chemical and morphological Nd:YAG laser modifications on irradiated primary enamel. BACKGROUND DATA: Previous studies on irradiated primary human enamel employed methodologies that evaluated the short-term effects only. METHODS: One hundred and eighty-six irradiated (with and/or without fluoride) primary enamel teeth from high-caries-risk children, which were exfoliated over a 1-year period, were collected, and the sample surface area was submitted for scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, and X-ray energy-dispersive spectrometry (EDS). The subsurface was analyzed by Knoop microhardness and light microscopy (LM). Data were analyzed by one way ANOVA and Tukey tests (α=0.05) and Kruskall-Wallis and Tukey tests (α=0.05). RESULTS: FTIR analysis revealed a higher concentration of phosphate and carbonate in the irradiated (0.987±0.064) and lower concentration in the control groups (1.477±0.310). SEM analysis showed that the control samples exhibited a slightly smoother surface than the irradiated groups. The EDS analysis did not show any differences in the amount of calcium, phosphorus, or fluoride among the groups. The microhardness analysis revealed that sealant (249.86±7.15) and laser irradiation (262.44±22.69) led to higher hardness values than the negative control group (128.35±25.19). LM indicated significantly reduced caries formation in the laser (5.35±5.38%) and the laser plus acidulated phosphate fluoride (APF) groups (10.35±0.88%) compared with the negative control group (72.56±12.86%). CONCLUSIONS: Even with the limitations of the present study, these results suggest that Nd:YAG irradiation clinically modified the chemical composition of the enamel surface regardless of fluoride concentration, which successfully inhibited demineralization of primary tooth enamel over a 1-year period without significant morphological changes.

Effect of different irrigation protocols on the radicular dentin interface and bond strength with a metacrylate-based endodontic sealer.

This study assessed the influence of different endodontic chemical substances on the adhesion of the Epiphany SE/Resilon system (with and without resinous solvent) to radicular dentin walls, using the push-out test and scanning electron microscopy (SEM). Forty-eight root canals of human canines were prepared biomechanically with ProTaper rotary files (crown-down technique) and the radicular dentin was treated with either 17% EDTA, 2% chlorhexidine gel (CHX) or 2.5% NaOCl (control). The root canals were filled with Resilon cones and Epiphany SE sealer with and without resinous solvent. Six groups of eight canals each had their roots sectioned transversally to obtain 1-mm thick slices. Data were subjected to statistical analysis by ANOVA and Tukey's tests. The specimens treated with 17% EDTA (1.59 ± 0.91) presented higher bond strength (P < 0.05) than those treated with 2.5% NaOCl (0.93 ± 0.27) and 2% CHX (0.92 ± 0.22). Significantly higher bond strength (P < 0.05) was observed when the Epiphany SE was prepared with (1.37 ± 0.78) than without (0.92 ± 0.33) solvent. Adhesive failures were predominant in all groups. SEM analysis showed greater homogeneity of the filling mass when the solvent was added to the sealer. Treatment of root canal walls with 17% EDTA, and addition of a resinous solvent to Epiphany SE produced the highest adhesion to radicular dentin.