Synthesis and characterization of monodispersed water dispersible Fe3O4 nanoparticles and in vitro studies on human breast carcinoma cell line under hyperthermia condition.

Monodispersed Fe3O4 magnetic nanoparticles (MNPs) having size of 7 nm have been prepared from iron oleate and made water dispersible by functionalization for biomedical applications. Three different reactions employing thioglycolic acid, aspartic acid and aminophosphonate were performed on oleic acid coated Fe3O4. In order to achieve a control on particle size, the pristine nanoparticles were heated in presence of ferric oleate which led to increase in size from 7 to 11 nm. Reaction parameters such as rate of heating, reaction temperature and duration of heating have been studied. Shape of particles was found to change from spherical to cuboid. The cuboid shape in turn enhances magneto-crystalline anisotropy (Ku). Heating efficacy of these nanoparticles for hyperthermia was also evaluated for different shapes and sizes. We demonstrate heat generation from these MNPs for hyperthermia application under alternating current (AC) magnetic field and optimized heating efficiency by controlling morphology of particles. We have also studied intra-cellular uptake and localization of nanoparticles and cytotoxicity under AC magnetic field in human breast carcinoma cell line.

Covalent bridging of surface functionalized Fe3O4 and YPO4:Eu nanostructures for simultaneous imaging and therapy.

Magnetic luminescent hybrid nanostructures (MLHN) have received a great deal of attention due to their potential biomedical applications such as thermal therapy, magnetic resonance imaging, drug delivery and intracellular imaging. We report the development of bifunctional Fe3O4 decorated YPO4:Eu hybrid nanostructures by covalent bridging of carboxyl PEGylated Fe3O4 and amine functionalized YPO4:Eu particles. The surface functionalization of individual nanoparticulates as well as their successful conjugation was evident from Fourier transform infrared (FTIR) spectroscopy, dynamic light scattering (DLS), zeta-potential and transmission electron microscopy (TEM) studies. X-ray diffraction (XRD) analysis reveals the formation of highly crystalline hybrid nanostructures. TEM micrographs clearly show the binding/anchoring of 10 nm Fe3O4 nanoparticles onto the surface of 100-150 nm rice grain shaped YPO4:Eu nanostructures. These MLHN show good colloidal stability, magnetic field responsivity and self-heating capacity under an external AC magnetic field. The induction heating studies confirmed localized heating of MLHN under an AC magnetic field with a high specific absorption rate. Photoluminescence spectroscopy and fluorescence microscopy results show optical imaging capability of MLHN. Furthermore, successful internalization of these MLHN in the cells and their cellular imaging ability are confirmed from confocal microscopy imaging. Specifically, the hybrid nanostructure provides an excellent platform to integrate luminescent and magnetic materials into one single entity that can be used as a potential tool for hyperthermia treatment of cancer and cellular imaging.

Bi-functional properties of Fe3O4@YPO4:Eu hybrid nanoparticles: hyperthermia application.

Magnetic nanoparticles based hyperthermia therapy is a possible low cost and effective technique for killing cancer tissues in the human body. Fe3O4 and Fe3O4@YPO4:5Eu hybrid magnetic nanoparticles are prepared by co-precipitation method and their average particle sizes are found to be ∼10 and 25 nm, respectively. The particles are spherical, non-agglomerated and highly dispersible in water. The crystallinity of as-prepared YPO4:5Eu sample is more than Fe3O4@YPO4:5Eu hybrid magnetic nanoparticles. The chemical bonds interaction between Fe3O4 and YPO4:5Eu is confirmed through FeO-P. The magnetization of hybrid nanocomposite shows magnetization Ms = 11.1 emu g(-1) with zero coercivity (measured at 2 × 10(-4) Oe) at room temperature indicating superparamagnetic behaviour. They attain hyperthermia temperature (~42 °C) under AC magnetic field showing characteristic induction heating of the prepared nanohybrid and they will be potential material for biological application. Samples produce the red emission peaks at 618 nm and 695 nm, which are in range of biological window. The quantum yield of YPO4:5Eu sample is found to be 12%. Eu(3+) present on surface and core could be distinguished from luminescence decay study. Very high specific absorption rate up to 100 W g(-1) could be achieved. The intracellular uptake of nanocomposites is found in mouse fibrosarcoma (Wehi 164) tumor cells by Prussian blue staining.

Multicolored and white-light phosphors based on doped GdF3 nanoparticles and their potential bio-applications.

Rare-earth-doped gadolinium fluoride nanocrystals were synthesized by a single step synthesis employing ethylene glycol as solvent. Based on X-ray diffraction studies, stabilization of hexagonal modification of GdF(3) has been inferred. The microscopic studies show formation of uniformly distributed nanocrystals (~15 nm). The nanoparticles are readily dispersible in water and show bright luminescence in colloidal solution. The luminescence properties have been investigated as a function of activator concentrations, and enhanced optical properties have been attributed to efficient energy transfer from the Gd(3+) to the activator RE(3+) ions, which has further been confirmed by steady-state and time-resolved optical studies. It has been demonstrated that on doping appropriate amount of activators in host GdF(3), a novel white-light-emitting phosphor is obtained with CIE co-ordinates and correlated color temperature (CCT) very close to broad daylight. This can have promising applications as phosphor for white-light ultraviolet-light-emitting diodes (UV-LEDs). Our experiments showed efficient labeling of human breast carcinoma cells (MCF-7) by Tb(3+)-doped GdF(3) nanoparticles. The fluorescence intensity was found to be dependent on the surface modifying/coating agent, and the results were validated using confocal microscopy in terms of localization of these functionalized nanoparticles.