The effect of medicaments used in endodontic regeneration on root fracture and microhardness of radicular dentine.

AIM: To investigate the effect of medicaments used in endodontic regeneration on root fracture resistance and microhardness of radicular dentine. METHODOLOGY: The root canals of mandibular premolars (n = 180) were instrumented and randomized into three treatment groups and an untreated control group. Each treatment group received either triple antibiotic paste (TAP), double antibiotic paste (DAP) or calcium hydroxide paste [Ca(OH)2] intracanal medicament. Teeth were kept in saline for 1 week, 1 month or 3 months. After each time-point, 15 teeth were randomly selected from each group and two root cylinders were obtained from each tooth. One cylinder was subjected to a fracture resistance test, and the other cylinder was used for a microhardness test. Two-way ANOVA and Tukey's pairwise comparisons were used for statistical analysis. RESULTS: For the microhardness test, the two-way interaction between group and time was significant (P < 0.001). The intracanal application of TAP and DAP caused significant and continuous decrease in root dentine microhardness after one (P < 0.05) and 3 months (P < 0.001), respectively. The three-month intracanal application of Ca(OH)2 significantly increased the microhardness of root dentine (P < 0.05). The time factor had a significant effect on fracture resistance (P < 0.001). The three intracanal medicaments caused significant decreases in fracture resistance ranging between 19% and 30% after 3-month application compared to 1-week application. CONCLUSION: In this laboratory study, the 3-month application of triple antibiotic paste, double antibiotic paste or calcium hydroxide paste medicaments significantly reduced the root fracture resistance of extracted teeth compared to a 1-week application.

The effect of nonsetting calcium hydroxide on root fracture and mechanical properties of radicular dentine: a systematic review.

The aim of this review was to identify and analyse all studies related to the effect of nonsetting calcium hydroxide [Ca(OH)(2)] on root fracture and various mechanical properties of radicular dentine. A PubMed search was conducted using the keywords 'calcium hydroxide' and 'dentistry' combined with MeSH terms 'tooth fractures' or 'mechanical phenomena' or 'compressive strength'. The search was expanded by including Embase and Web of Science databases, using the keywords 'calcium hydroxide' and 'root' and 'fracture'. The search was supplemented by checking the reference lists from each selected article. Each study had to meet the following criteria to be selected for review: (i) Inclusion of at least one experimental group with root or radicular dentine either filled with or exposed to nonsetting Ca(OH)(2); (ii) inclusion of at least one appropriate control group; and (iii) a minimum of five samples per experimental group. Only articles written in English were included. Of the 16 studies selected initially, 12 in vitro studies fulfilled the selection criteria for inclusion in the final review. No clinical studies that directly supported the correlation between Ca(OH)(2) intracanal dressing and root fracture were found in the literature. However, the majority of in vitro studies showed reduction in the mechanical properties of radicular dentine after exposure to Ca(OH)(2) for 5 weeks or longer. Conversely, the data were inconclusive regarding whether Ca(OH)(2) exposure for 1 month or less had a negative effect on the mechanical properties of radicular dentine.