Evaluation of high oleic sunflower oil oleogels with beeswax, beeswax-glyceryl monopalmitate, and beeswax-Span80 in cookie preparation.

BACKGROUND: Shortening is used widely in cookie preparation to improve quality and texture. However, large amounts of saturated and trans fatty acids present in shortening have adverse effects on human health, and much effort has been made to reduce the use of shortening. The use of oleogels might be a suitable alternative. In this study, the oleogels of high oleic sunflower oil with beeswax (BW), BW-glyceryl monopalmitate (BW-GMP), and BW-Span80 (BW-S80) were prepared and their suitability to replace shortening in cookie preparation was evaluated. RESULTS: The solid fat content of BW, BW-GMP, and BW-S80 oleogels was significantly lower than that of commercial shortening when the temperature was not higher than 35 °C. However, the oil-binding capacity of these oleogels was almost similar to that of shortening. The crystals in the shortening and oleogels were ß' form mainly; however, the morphology of crystal aggregates in these oleogels was different from that of shortening. The textural and rheological properties of doughs prepared with the oleogels were similar, and clearly different from those of dough with commercial shortening. The breaking strengths of cookies made with oleogels were lower than that of cookies prepared with shortening. However, cookies containing BW-GMP and BW-S80 oleogels were similar in density and color to those prepared with shortening. CONCLUSION: The textural properties and color of cookies with BW-GMP and BW-S80 oleogels were very similar to those of the cookies containing commercial shortening. The BW-GMP and BW-S80 oleogels could act as alternatives to shortening in the preparation of cookies. © 2023 Society of Chemical Industry.

Crystal network structure and stability of beeswax-based oleogels with different polyunsaturated fatty acid oils.

The effect of different types of oils including camellia oil (CLO), sunflower oil (SFO), corn oil (CO) and linseed oil (LO) on the formation, crystal network structure and mechanical properties of 4%wt beeswax (BW) in oleogel was investigated. BW oleogels containing oils with higher contents of polyunsaturated fatty acids gelled first (1%wt), especially LO with higher contents of linolenic acid rather than CLO with higher contents of monounsaturated fatty acids. In comparison, oils with higher polyunsaturated fatty acid contents exhibited higher Db with more extensive microstructure at different cooling rates, which was related to shorter nucleation induction time of crystal and higher crystallinity. Stronger van der Waals forces were observed in oleogels with higher polyunsaturated fatty acid contents especially for LO oleogel. Rheology also showed that LO oleogel with higher content of linolenic acid had higher crystallinity and lower crystal melting interfacial tension, resulting in the formation of a more stable network structure.