Improvement of performance for flexible film dosimeter by incorporating additive agents.

Objective.To evaluate the reduction in energy dependence and aging effect of the lithium salt of pentacosa-10,-12-diynoic acid (LiPCDA) films with additives including aluminum oxide (Al2O3), propyl gallate (PG), and disodium ethylenediaminetetracetate (EDTA).Approach. LiPCDA films exhibited energy dependence on kilovoltage (kV) and megavoltage (MV) photon energies and experienced deterioration over time. Evaluations were conducted with added Al2O3and antioxidants to mitigate these issues, and films were produced with and without Al2O3to assess energy dependence. The films were irradiated at doses of 0, 3, 6, and 12 cGy at photon energies of 75 kV, 105 kV, 6 MV, 10 MV, and 15 MV. For the energy range of 75 kV to 15 MV, the mean and standard deviation (std) were calculated and compared for the values normalized to the net optical density (netOD) at 6 MV, corresponding to identical dose levels. To evaluate the aging effect, PG and disodium EDTA were incorporated into the films: sample C with 1% PG, sample D with 2% PG, sample E with 0.62% disodium EDTA added to sample D, and sample F with 1.23% disodium EDTA added to sample D.Main results. Films containing Al2O3demonstrated a maximum 15.8% increase in mean normalized values and a 15.1% reduction in std, reflecting a greater netOD reduction at kV than MV energies, which indicates less energy dependence in these films. When the OD of sample 1-4 depending on the addition of PG and disodium EDTA, was observed for 20 weeks, the transmission mode decreased by 8.7%, 8.3%, 29.3%, and 27.3%, respectively, while the reflection mode was 5.4%, 3.0%, 37.0%, and 34.5%, respectively.Significance. Al2O3effectively reduced the voltage and MV energy dependence. PG was more effective than disodium EDTA in preventing the deterioration of film performance owing to the aging effect.

Absorbed dose distributions from ophthalmic 106 Ru/106 Rh plaques measured in water with radiochromic film.

PURPOSE: Brachytherapy with 106 Ru/106 Rh plaques offers good outcomes for small-to-medium choroidal melanomas and retinoblastomas. The dose measurement of the plaques is challenging, due to the small range of the emitted beta particles and steep dose gradients involved. The scarce publications on film dosimetry of 106 Ru/106 Rh plaques used solid phantoms. This work aims to develop a practical method for measuring the absorbed dose distribution in water produced by 106 Ru/106 Rh plaques using EBT3 radiochromic film. METHODS: Experimental setups were developed to determine the dose distribution at a plane perpendicular to the symmetry axis of the plaque and at a plane containing the symmetry axis. One CCA and two CCX plaques were studied. The dose maps were obtained with the FilmQA Pro 2015 software, using the triple-channel dosimetry method. The measured dose distributions were compared to published Monte Carlo simulation and experimental data. RESULTS: A good agreement was found between measurements and simulations, improving upon published data. Measured reference dose rates agreed within the experimental uncertainty with data obtained by the manufacturer using a scintillation detector, with typical differences below 5%. The attained experimental uncertainty was 4.1% (k = 1) for the perpendicular setup, and 7.9% (k = 1) for the parallel setup. These values are similar or smaller than those obtained by the manufacturer and other authors, without the need of solid phantoms that are not available to most users. CONCLUSIONS: The proposed method may be useful to the users to perform quality assurance preclinical tests of 106 Ru/106 Rh plaques.