Effects of different primers and colouring solutions on orthodontic bonding: shear bond strength and colour change.

OBJECTIVES: This in vitro study evaluated the effect of different colouring solutions and primer systems used in the bonding of brackets on enamel colour change and bond strength. MATERIALS AND METHODS: 120 premolar teeth were divided into four main groups; brackets were bonded with 37% orthophosphoric acid + Transbond XT Primer in Group 1, 3 M Single Bond Universal in Group 2, Transbond Plus SEP in Group 3, and G-Premio Bond in Group 4. Each group was divided into three subgroups, and the teeth were placed in a cup containing coffee and tea mixture, in a cup containing cola and in distilled water. A bond strength test was applied to all teeth. Colour measurements of all teeth were performed at 2 different times: before bonding and after the bond strength test. RESULTS: The average bond strength of the 37% orthophosphoric acid group was higher than that of the other groups. The effect of primer and solution groups on colour change was statistically significant (p = 0.001 and p = 0.023, respectively). CONCLUSIONS: In this study, the bond strength was clinically sufficient in all primer groups. The highest colour change was observed when the tea-coffee solution and Transbond Plus SEP primer were used. CLINICAL RELEVANCE: This study has identified enamel discoloration and bond strength from different colouring solutions and primer systems used for bonding braces, which can be used to inform clinicians and patients to achieve better treatment results.

Effect of antioxidants on adhesive bond strength to bleached enamel.

OBJECTIVE: To evaluate the influence of antioxidants (ATX) resveratrol, winter's bark, green tea and yerba mate on the bond strength between bleached enamel and the nanohybrid composite resin. METHODOLOGY: Bovine incisor crowns (n = 132) were randomly divided into 22 groups (n = 6) according to the application times (5, 10, 15, 30, and 60 min) of each antioxidant. Teeth restored without previous bleaching or ATX constituted the non-bleached control group (NB Ctrl) (n = 6), and teeth restored after bleaching and without ATX represented the bleached control group (B Ctrl) (n = 6). The 35 % hydrogen peroxide was applied for 45 min (3 application of 15 min) to the buccal enamel surface. ATX was used after bleaching for the specified time of each group and removed with air-water spray. The enamel was etched with 37 % phosphoric acid (30 s) and rinsed with air-water spray. The adhesive resin was applied to the enamel dry surface. Teeth were restored using 1 mm composite resin increments (10 × 10 × 3 mm) and sectioned in test specimens of 6 mm in length and 1 mm2 in cross-sectional area submitted to microtensile bond strength test (0.5 mm/min). The load (N) at failure was recorded, and the bond strength (σt) was calculated (MPa). The fracture area was analyzed under optical microscopy, and failures were classified as cohesive, mixed, or adhesive. Data was evaluated by Kruskal-Wallis and Dunn tests (p ≤ 0.05). RESULTS: B Ctrl group presented lower σt than NB Ctrl (p < 0.001). Applying resveratrol for 5 or 10 min, winter's bark for 10 or 15 min, green tea for less than 15 min, and yerba mate for 15 min provided similar σt between bleached enamel and nanohybrid composite to the control group. CONCLUSION: Restorative procedures performed immediately after tooth bleaching compromises adhesion. Experimental antioxidants applied to bleached enamel can increase the immediate bond strength of restorations performed directly after bleaching, with similar values to those observed in unbleached enamel. CLINICAL SIGNIFICANCE: This study presents promising results to support the use of antioxidants on the recently bleached enamel to allow adhesive tooth restorations. The immediate bonding obtained using antioxidants was similar to the one achieved in non-bleached enamel in brief application times. Green tea extract and resveratrol were able to restore the bond strength to bleached enamel in a short application time of 5 min. The reduction in the required application time holds the potential to decrease the overall duration of the clinical section, offering clinical advantages and improving the feasibility of using antioxidants on the bleached enamel prior to adhesive procedures.

Particle abrasion as a pre-bonding dentin surface treatment: A scoping review.

OBJECTIVE: This scoping review aims to assess the influence of air abrasion with aluminum oxide and bioactive glass on dentin bond strength. MATERIALS AND METHODS: An electronic search was conducted in three databases (PubMed, Cochrane Library, and Embase), on March 3rd, 2023, with previously identified MeSH Terms. A total of 1023 records were screened. Exclusion criteria include primary teeth, air abrasion of a substrate other than sound dentin, use of particles apart from aluminum oxide or bioactive glass, and studies in which bond strength was not assessed. RESULTS: Out of the 1023 records, title and abstract screening resulted in the exclusion of 895 and 67 studies, respectively, while full-text analysis excluded another 25 articles. In addition, 5 records were not included, as full texts could not be obtained after requesting the authors. Two cross-references were added. Thus, 33 studies were included in this review. It is important to emphasize the absence of standardization of air abrasion parameters. According to 63.6% of the studies, air abrasion does not influence dentin bond strength. Moreover, 30.3% suggest improving bonding performance, and 6.1% advocate a decrease. CONCLUSIONS: Air abrasion with aluminum oxide does not enhance or impair dentin bond strength. The available data on bioactive glass are limited, which hinders conclusive insights. CLINICAL SIGNIFICANCE: Dentin air abrasion is a widely applied technique nowadays, with numerous clinical applications. Despite the widespread adoption of this procedure, its potential impact on bonding performance requires a thorough analysis of the existing literature.

The effect of different mechanical retention forms on shear bond strength of rebonding of ceramic brackets.

The objective of this study is to compare the shear bond strength (SBS) and the morphological characteristics and chemical compositions of the base surface of newly bonded and rebonded ceramic brackets with different mechanical retention bases. Sixty extracted human premolars were divided into the newly bonded and rebonded groups. Ceramic brackets with patterned, laser-etched, and particle-coated patterned bases were randomly bonded to the tooth samples in each group (n=10 per base type). The rebonded brackets exhibited significantly lower SBS than the newly bonded brackets (p<0.05). The main chemical composition of the brackets in both groups was aluminum on the energy-dispersive X-ray spectroscopy. Scanning electron microscopy imaging showed the presence of regular-shaped undercuts or irregular micro-undercuts on the bracket bases which mostly remained intact even after debonding and sandblasting, while coated particles disappeared. The rebonded ceramic brackets with mechanical retention bases exhibited clinically acceptable bond strength regardless of retentive forms.

Can antioxidant treatment replace delay in bracket bonding? An in vitro study.

BACKGROUND: Deterioration in shear bond strength has been reported after immediate bracket bonding following hydrogen peroxide bleaching. This study compared the effectiveness of three antioxidant agents, namely, alpha-tocopherol, green tea extract, and sodium ascorbate, in reversing the bleaching effect and as possible alternatives to delayed bonding. METHODS: A total of 105 extracted human premolars were arbitrarily assigned to 7 groups (n = 15 each), including group 1 as the unbleached control group and six experimental groups, which were bleached with 40% hydrogen peroxide in three sessions of 15 min each. In experimental group 2, bonding was performed immediately after bleaching, whereas in groups 3 and 4, bonding was delayed for 1 and 2 weeks, respectively; meanwhile, the specimens were immersed in artificial saliva at 37 °C. Groups 5, 6, and 7 were treated immediately after bleaching with 10% of alpha-tocopherol, green tea extract, and sodium ascorbate solutions, respectively, for 15 min. Specimens were processed using 500 thermal cycles between 5 and 55 °C, with a dwell time of 30 s after 24 h of bracket bonding, and then tested for shear bond strength. The adhesive remnant index was examined to evaluate fracture mode. One-way analysis of variance, Kruskal-Wallis H, and post hoc Tukey's honestly significant difference tests were used to compare the data. Significant results were subjected to pairwise comparisons with Bonferroni's correction-adjusted of p values ≤ 0.050. RESULTS: Shear bond strength was significantly lower (p < 0.001) in the immediate bonding and 1-week delay groups than in the control group. However, no significant difference was detected among the 2-week delay, antioxidant-treated, and control groups (p > 0.05). CONCLUSIONS: Application of 10% alpha-tocopherol, green tea extract, or sodium ascorbate for 15 min could restore shear bond strength after 40% hydrogen peroxide bleaching as an alternative to delay in bracket bonding.

The Effect of Nano-Silica Surface Infiltration on Bond Strength of a Phosphate-Monomer-containing Composite Cement to Zirconia.

PURPOSE: To evaluate the bonding receptiveness of zirconia treated with nano-silica surface infiltration and the bond strength of composite cement after aging. MATERIALS AND METHODS: Zirconia ceramic green bodies (Ceramill zolid, Amann Girbach) with dimensions of 10 x 10 x 4 mm were divided into three groups (n = 4): group C (control: no treatment after sintering), group S (sandblasted: 50-µm alumina airborne particle abrasion after sintering) and group N (nanosintered: infiltrated with nano-silica colloid, sintered, and then etched with hydrofluoric acid). Phase transformations were examined through X-ray diffraction (XRD). Composite resin (Filtek Z250, 3M Oral Care) was bonded to zirconia using the 10-MDP-containing composite cement Panavia F (Kuraray Noritake). The composite-cement/zirconia bond strength was immediately measured using the microtensile bond strength test (µTBS) as well as after three months of artificial aging in water (n = 20 microstick specimens/group). Failure mode patterns were examined using SEM. RESULTS: The specimens of groups C and S, as tested by XRD, exhibited almost full tetragonal phases, while a small extent of tetragonal-monoclinic phase transformation (t→m) was observed for group N. Group N achieved the highest bond strengths (41.5 ± 8.6 MPa), which was significantly higher than that measured for groups C and S (p < 0.05). There was a significant drop in µTBS after 90 days of water storage for groups C and S. SEM revealed a decrease in the percentage of cohesive failure in groups N and S after water storage. CONCLUSIONS: Infiltrating zirconia with nano-silica is a reliable method to establish a strong and stable bond to zirconia. The combination of surface infiltration with nano-silica and application of a phosphate monomer-containing composite cement can significantly improve the composite-cement/zirconia bond strength.

Influence of nanostructured alumina coating on the clinical performance of zirconia cantilevered resin-bonded fixed dental prostheses: Up to 3-year results of a prospective, randomized, controlled clinical trial.

STATEMENT OF PROBLEM: The debonding of zirconia cantilevered resin-bonded fixed dental prostheses remains a technical complication because zirconia's chemical inertness impedes adequate surface preparation for bonding. Limited clinical evidence on the performance of various pretreatment methods for the bonding surface of zirconia resin-bonded fixed dental prostheses is available. PURPOSE: The present prospective, randomized, controlled clinical trial aimed at evaluating the performance of zirconia resin-bonded fixed dental prostheses prepared with nanostructured alumina coating. MATERIAL AND METHODS: The study adopted a prospective, randomized, controlled, double-blind (patients, operator) design to compare the performance of nanostructured alumina coating with that of conventional airborne-particle abrasion. Twenty-seven healthy patients needing a replacement of a missing maxillary or mandibular central or lateral incisor were screened and rated to be eligible, and 31 zirconia cantilevered resin-bonded fixed dental prostheses were randomly allocated into 1 of 2 groups. The first group (n=15), where the restoration bonding surface was airborne-particle abraded with 50-µm alumina, served as a control group. In the second group (n=16), the restorations were pretreated with nanostructured alumina coating. Treatment and data collection were standardized. The primary outcome evaluated was the survival of the RBFDPs as defined by the restoration not debonding. The Kaplan-Meier analysis of cumulative survival was performed, and nonparametric tests were used to determine patient-specific differences between both study groups (age, sex, restored arch, tooth replaced, bonding surface area) (α=.05). Retainer wing surfaces of debonded resin-bonded fixed dental prostheses were inspected under a scanning electron microscope. RESULTS: Within a mean ±standard deviation observation period of 22.4 ±7.7 months (minimum, 8.3; maximum, 37.9 months), 3 debondings occurred, and the survival rate was 90.3%. The survival rate was 93.8% for the nanostructured alumina coating and 86.7% for the control group, with no statistically significant differences (log-rank, P=.54). No patient-specific differences were found between study groups (P>.05). As per the scanning electron micrographs, the majority of the nanostructured alumina-coated surfaces had large areas of nanostructured alumina residue, whereas the airborne-particle abraded surfaces exhibited predominantly adhesive failure with less cement residue. CONCLUSIONS: Over a mean observation period of 2 years, both zirconia pretreatments showed promising and comparable clinical results; therefore, nanostructured alumina coating could be regarded as a viable alternative pretreatment method to airborne-particle abrasion.

Physicochemical and biological characterization of silica-coated alumina particles.

OBJECTIVES: A tribochemical silica-coating (TSC) method has been developed to improve the adhesion of dental resin composites to various substrates. The method utilizes airborne-particle abrasion using particles having a silica surface and an alumina core. The impact of the TSC method has been extensively studied but less attention has been paid to the characterization of the silica-modified alumina particles. Due to the role of silicate ions in cell biology, e.g. osteoblast function and bone mineralization, silica-modified alumina particles could also be potentially used as a biomaterial in scaffolds of tissue regeneration. Thus, we carried out detailed physicochemical characterization of the silica-modified alumina particles. METHODS: Silica-modified alumina particles (Rocatec, 3 M-ESPE) of an average particle size of 30 µm were studied for the phase composition, spectroscopic properties, surface morphology, dissolution, and the capability to modify the pH of an immersion solution. The control material was alumina without silica modification. Pre-osteoblastic MC3T3-E1 cells were used to assess cell viability in the presence of the particles. Cell viability was tested at 1, 3, 7 and 10 days of culture with various particle quantities. Multivariate ANOVA was used for statistical analyses. RESULTS: Minor quantities of silica enrichment was verified on the surface of alumina particles and the silica did not evenly cover the alumina surface. In the dissolution test, no change in the pH of the immersion solution was observed in the presence of the particles. Minor quantities of silicate ions were dissolved from the particles to the cell culture medium but no major differences were observed in the viability of pre-osteoblastic cells, whether the cells were cultured with silica-modified or plain alumina particles. SIGNIFICANCE: Characterization of silica-modified alumina particles demonstrated differences in the particle surface structure compared to control alumina. Dissolution of silica layer in Tris buffer or SBF solution varied from that of cell culture medium: minor quantities of dissolved Si were observed in cell culture test medium. The cell viability test did not shown significant differences between control alumina and its silica-modified counterpart.

Effects of Surface Pretreatments on Bond Strength and Morphology of Aprismatic Enamel.

PURPOSE: To evaluate the effect of different pretreatment protocols and adhesives on the shear bond strength and surface morphology of aprismatic enamel. MATERIALS AND METHODS: Human maxillary incisors (N = 120) were assigned to five different groups according to pretreatment: 1) no treatment; 2) glycine; 3) sodium bicarbonate; 4) Al2O3 and 5) extra-fine bur. Then the teeth were divided into three subgroups, according to the adhesive applied: 3-step etch-and-rinse (ER), universal adhesive in ER mode, and universal adhesive in self-etch (SE) mode. Shear bond strength (SBS) testing was performed with a universal testing machine. For SEM observation, fifteen human molars were collected and analyzed after pretreatment with/without etching with 37% H3PO4 for 30s. RESULTS: Al2O3 showed higher SBS than all other groups considered. Comparable SBS values were obtained for other pretreatments. Universal adhesive in E&R mode performed better than did 3-step E&R and universal adhesive in SE mode. SEM images showed visible differences in enamel surface roughness. CONCLUSIONS: Airborne-particle abrasion with Al2O3 followed by etching with H3PO4 increased SBS on aprismatic enamel. The combination of airborne-particle abrasion with alumina powder followed by 15 s of H3PO4 etching and application of a universal adhesive in E&R mode proved to be the most effective adhesive protocol.

Effect of Sandblasting with Fluorapatite Glass-ceramic Powder and Chemical Primers/Adhesives on Shear Bond Strength of Indirect Repairing Composite to Zirconia.

OBJECTIVE: To investigate the effect of sandblasting with fluorapatite glass-ceramic (FGC) powder on zirconia surface roughness, crystallinity, and shear bond strength (SBS) of indirect repairing composite to zirconia using different primers/adhesives. METHODS: Zirconia blocks were treated as follows: no treatment (control group), blasting with 30-µm silica-coated alumina (CoJet group), and blasting with FGC powder (FGC group). The surface topography, silica content, roughness, and crystallinity of treated zirconia surfaces were analyzed by a scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), an optical profilometer, and X-ray diffraction (XRD), respectively. Four primers/adhesives (Monobond Plus, Calibra Silane, Futurabond M+, and Scotchbond Universal) were compared to bond precured resin composite to zirconia groups using Multilink Automix resin cement. Bonded specimens were thermocycled for 10,000 cycles and tested in SBS and the modes of failure were recorded. The effect of different surface treatments and primers/adhesives on SBS results were statistically analyzed using two-way ANOVA and Bonferroni post-hoc tests (α=0.05). RESULTS: Both CoJet and FGC groups showed rough surfaces with a higher content of silica in FGC, but less monoclinic crystals, compared to the CoJet group. The highest mean SBS was found in the FGC group treated with Monobond Plus compared to CoJet and Control groups. Adhesive failure was predominant in control groups, while combined failure was found in the CoJet and FGC groups regardless of the primers/adhesives employed. CONCLUSION: Sandblasting zirconia with FGC powder increased SBS of resin composite to zirconia with lower monoclinic phase transformation compared to CoJet sand. Monobond Plus reported the highest means of SBS values compared to other primers/adhesives.

Effect of cigarette smoke on aesthetic brackets: an in vitro study.

OBJECTIVE: The objective of this study was to evaluate the effect of cigarette smoke (CS) on physical and mechanical properties of ceramic, polycarbonate and alumina ceramic brackets. The null hypothesis tested was that aesthetic brackets would not be influenced by CS. METHODS: Ninety aesthetic brackets were allocated to three groups (n = 30): ceramic (GCE), polycarbonate (GCO) and alumina ceramic (GPS). Ten samples of each group were assigned to color and surface roughness analysis, performed before (T0) and after (T1) exposure to CS; and twenty samples were allocated into control and experimental groups (n = 10) (not exposed and exposed to CS, respectively) for shear bond strength test (SBS). Exposure to CS followed an adaptation of the method described by Le Mesurier. Colorimetric reading, surface morphology and roughness, SBS and adhesive remnant index (ARI) were assessed. Statistical analysis comprised independent and paired t-tests, ANOVA/Tukey and Fisher's exact tests (α = 0.05). RESULTS: Changes were observed in brackets' color (NBS: GCE = 2.4; GCO = 1.9; GPS = 2.1), surface roughness (ΔRa: GCE = 1.1 ± 0.8 µm; GCO = 1.9 ± 1.5µm; GPS = -0.3 ± 0.1 µm / ΔRz: GCE = 1.4 ± 1.0 nm; GPS = -0.5 ± 0.1 nm); and SBS (GPS - experimental = 221.8 ± 48.6 N) after exposure to CS (p< 0.05). CONCLUSIONS: Exposure, in vitro, of aesthetic brackets to CS resulted in changes of color to darker and more opaque shades, surface roughness alterations, and higher SBS values. ARI scores were not associated with exposure to CS.

Which Zirconia Surface-cleaning Strategy Improves Adhesion of Resin Composite Cement after Saliva Contamination? A Systematic Review and Meta-Analysis.

PURPOSE: To identify the most effective cleaning method for saliva-contaminated zirconia surface before adhesive cementation through a systematic review and meta-analysis. MATERIALS AND METHODS: PubMed, Scopus, and Web of Science databases were searched to select in vitro studies published through October 2021. Studies that did not perform aging methods, had a sample size less than 5 per group, or did not present a group with zirconia contaminated only with saliva were excluded. Data were extracted and risk of bias was assessed. Statistical analysis comparing the cleaning methods was conducted, and the standardized mean difference was assessed using the R software program. RESULTS: Among 804 potentially eligible studies, 36 were selected for full-text reading, of which 13 were included in qualitative analysis, and 11 of these were subsequently included in the quantitative analysis. A meta-analysis revealed a significant difference in the bond strength between the cleaning methods. Sandblasting with Al2O3  showed a higher bond strength than cleaning solution (Ivoclean, Ivoclar Vivadent) (p < 0.01, I2 = 65%), and both methods promoted higher resin-bond strength to zirconia than water cleaning. In addition, there was no significant difference in the bond strength between alcohol (p = 0.35, I2 = 79%), phosphoric acid (p < 0.23, I2 = 90%), and water cleaning. CONCLUSION: Sandblasting with Al2O3 seems to be the best method for zirconia surface cleaning before adhesive luting, promoting better resin-bond strength to zirconia.

MDP Salts: A New Bonding Strategy for Zirconia.

Durable resin-ceramic adhesion may influence the clinical success of ceramic restorations, which has been one of the challenging issues in dentistry. The present study assessed the bond strength and chemical interaction of 10-methacryloxydecyl dihydrogen phosphate (MDP), MDP+silane, and MDP-salt primers to alumina-blasted zirconia ceramic by tensile bond strength test, surface elemental composition with x-ray photoelectron spectroscopy analysis, contact angle measurement, surface morphology with scanning electron microscopy, and surface topography with 3-dimensional confocal laser scanning microscope analyses. MDP-salt showed the highest tensile bond strength before and after thermocycling when compared with MDP and MDP+silane (P < 0.05). The measured contact angle values differed significantly (P < 0.001) in the order of MDP-salt > control (no chemical pretreatment) > MDP+silane > MDP. There was no difference in surface roughness (P = 0.317) and surface topography among all tested groups. Zirconia treated with MDP-salt showed phosphorus peaks in addition to zirconia and alumina peaks. MDP-salt has zirconia priming properties, which improves bonding performance to resin cement.

The effects of different silicatization and silanization protocols on the bond durability of resin cements to new high-translucent zirconia.

OBJECTIVE: The aim of this study was to assess the influence of different silicatization protocols with various silane treatment methods on the bond performance to high-translucent zirconia. MATERIALS AND METHODS: High-translucent zirconia specimens were assigned to five groups according to mechanical surface pretreatment: as-sintered (Con), 0.2 MPa alumina sandblasting (AB2), tribochemical silica coating (TSC), 0.2 and 0.4 MPa glass bead air abrasion (GB2) and (GB4). Each group was subjected to 4 different cementation protocols: Panavia SA Universal (SAU), Panavia SA plus (SAP), silane + SAP (S-SAP), and Universal adhesive + SAP (U-SAP). Tensile bond strength (TBS) was measured after 24 h and 10,000 thermocycling (TC). Surface topography, surface energy, and elemental composition of the abraded zirconia surface analyses were completed. TBS data was analyzed using the Weibull analysis method. Surface roughness and surface energy were compared by one-way ANOVA analysis of variance (α = 0.05). RESULTS: After 24 h, higher TBS was achieved with all cementation protocols in AB2 and TSC, also, in GB2 with all protocols except U-SAP, and in GB4 with SAU and S-SAP. After aging, GB4/S-SAP, GB2/S-SAP, AB2/U-SAP, and TSC/S-SAP showed the highest bond strength. GB groups showed the lowest surface roughness and highest surface energy. CONCLUSION: Glass bead abrasion achieved the durable bond strength to high-translucent zirconia using a separate silane coupling agent while altered surface chemistry, surface energy, and roughness without effect on morphology. CLINICAL RELEVANCE: Glass bead air abrasion is an alternative to alumina sandblasting and tribochemical silica coating and improves bond strength to high translucent zirconia.

Effect of Air-Particle Abrasion Protocol and Primer on The Topography and Bond Strength of a High-Translucent Zirconia Ceramic.

PURPOSE: To evaluate effect of air-particle abrasion protocol and primer on surface topography and bond strength of resin cement to high-translucent zirconia ceramics. MATERIALS AND METHODS: Two hundred disk-shaped high-translucent zirconia specimens of 5Y-PSZ were prepared. The specimens were assigned to 5 groups in terms of particle type and air-particle abrasion pressure: (1) control, (2) alumina with 0.2 MPa-air pressure [AB-0.2], (3) alumina with 0.4 MPa-air pressure [AB-0.4], (4) glass beads with 0.2 MPa-air pressure [GB-0.2], and (5) glass beads with 0.4 MPa-air pressure [GB-0.4]. Two different primers 1% MDP (Experimental) and MDP-silane primer (Clearfil Ceramic Primer Plus) was also tested. Stainless steel rods were bonded to the 5Y-PSZ specimens with PANAVIA V5. For each group, the tensile bond strength (TBS) was measured after 24-hour water storage (n = 10) and after 5000 thermal-cycling (n = 10) at crosshead speed of 2 mm/min. The data were statistically analyzed using Weibull analysis. Surface roughness (Sa) was measured using a 3D-Laser Scanning Confocal Microscope (n = 5) and analyzed by t-test with Bonferroni correction. Surface topography using scanning electron microscopy (SEM) and surface elemental analysis using energy dispersion spectroscopy (EDX), and cross-section SEM at the interface with composite cement were also investigated. RESULTS: In MDP-silane groups, the highest TBS was observed in AB-0.4 after 24 hours and GB-0.4 after thermal-cycling (p < 0.05). In MDP groups, AB groups resulted in the significantly higher TBS than GB groups (p < 0.05). AB-0.4 group showed the highest Sa value compared to all groups (p < 0.005), meanwhile GB groups did not show different Sa compared to control (p > 0.005). CONCLUSION: Air-abrasion with different particle and blasting pressure can improve bonding to zirconia with proper primer selection. Particularly, glass beads abrasion followed by MDP-silane primer and alumina abrasion followed by MDP primer alone provided stable bond strength of resin cement to high-translucent zirconia after aging. High-translucent zirconia abraded with glass beads achieves a desirable bonding performance without creating surface microcracks which may hinder zirconia's mechanical properties.

Does the bonding effectiveness of a fiber post/resin composite benefit from mechanical or chemical treatment? Seven methods for saliva-contaminated surfaces.

PURPOSE: This study examined four cleaning methods and three chemical treatments for artificial saliva-contaminated fiber posts in terms of bonding durability to resin composite core materials. METHODS: Non-contaminated fiber posts (Tokuyama FR Post, Tokuyama Dental) and those contaminated (GC Fiber Post, GC) with artificial saliva (Saliveht Aerosol, Teijin Pharma) were used. Washing and drying (WD), alcohol cleaning (AlC), H3PO4 etching (P/WD), alumina blasting (B/D) for decontamination and silanization (Clearfil Ceramic Primer Plus, Kuraray Noritake Dental, Si), resin priming (HC Primer, Shofu, MMA), and bonding resin application (Clearfil Universal Bond Quick, Kuraray Noritake Dental, BR) for chemical treatment were performed. The treated fiber post was planted inside a cylindrical tube and filled with resin composite (DC Core Automix ONE, Kuraray Noritake Dental). The specimen was sectioned, and a push-out test was performed after 24 h, 1 month, and 3 months. The fracture surface was observed using a scanning electron microscope (SEM). RESULTS: Adhesion between the non-contaminated fiber post and resin composite did not improve by silanization and decreased by alumina blasting. SEM observations revealed a fractured glass fiber by alumina blasting. Saliva contamination decreased the bond strength between the fiber post and resin composite; however, recovery was achieved by WD, Alc, P/WD, and B/D. Compared to Si, BR (P = 0.009) was effective in restraining the long-term durability of bonding, whereas MMA (P = 0.99) was not. CONCLUSION: The application of bonding resin after alcohol cleaning is the most convenient and effective clinical procedure for fiber post surface treatment.

Shear bond strength of an acrylic resin to a ceria-stabilized zirconia-alumina nanocomposite.

STATEMENT OF PROBLEM: Ceria-stabilized zirconia-alumina nanocomposite (Ce-TZP-Al2O3) has properties that may be suitable for partial denture frameworks. However, studies on its adhesion strength and durability with denture base resin are lacking. PURPOSE: The purpose of this in vitro study was to determine the optimal surface treatment for Ce-TZP-Al2O3 to secure a durable bond with an acrylic resin. MATERIAL AND METHODS: The surface of Ce-TZP-Al2O3 test specimens was alumina airborne-particle abraded (Group APA) and then treated with 10-methacryloyloxydecyl dihydrogen phosphate (MDP) (Group MDP) and 2 silica coating methods: the flame spraying method (Group SLP) and the tribochemical treatment (110 µm: Group TRB-P, 30 µm: Group TRB-S). TRB-P and TBR-S were further treated by MDP (Group CBT-P and CBT-S). Autopolymerizing acrylic resin was bonded to the specimens, and the shear bond strength was tested after thermocycling (5 °C and 60 °C, 10 000 cycles). The area of the resin remaining on the fractured surfaces was also measured. To evaluate the effect of the surface treatment condition on shear bond strength and the resin remaining, 1-way analysis of variance (ANOVA) was conducted, followed by the Tukey multiple comparison post hoc test. Additionally, the effect of thermocycling on the specimens was evaluated by the Student t test. RESULTS: After placement in deionized water for 24 hours, the shear bond strengths of Group MDP and 2 types of combination treatment (Groups CBT-P and CBT-S) were significantly higher than those of Groups SLP, TRB-P, and TRB-S (P<.05). Moreover, the fractured surface of all the treatment conditions except Group APA showed cohesive failure. The shear bond strength as a result of all treatment conditions decreased significantly after thermocycling (P<.05). Group CBT-S showed the highest shear bond strength; however, no significant differences were found between Groups CBT-S and MDP (P=.908). In particular, the area of resin remaining on the fractured surfaces of Group CBT-S was 100% (cohesive failure). CONCLUSIONS: The combined surface treatment of alumina airborne-particle abrasion and tribochemical treatment, along with primer treatment using silane coupling and an MDP monomer, improved the adhesion strength and adhesion durability between base resins and Ce-TZP-Al2O3.

Bond durability and surface states of titanium, Ti-6Al-4V alloy, and zirconia for implant materials.

PURPOSE: Screw-retained implant crowns used as dental implants comprise a zirconia coping and titanium base bonded using resin cement. These devices are prone to debonding failures. This study investigated the bond characteristics of implant materials based on shear bond strength (SBS) and surface characteristics. METHODS: Chemically pure (CP) titanium grade-4 (Ti), Ti-6Al-4V alloy (Ti-6Al-4V), and tetragonal polycrystalline zirconia (zirconia) were evaluated as adherent materials. Plates of each material were polished, primed for the respective resin cements, and cemented using either methyl methacrylate-based resin cement (Super-Bond) or composite-based resin cement (Panavia). The cemented samples were subjected to 10,000 thermocycles alternating between 5 and 55 °C, and the SBS were obtained before and after thermocycling. The sample surfaces were characterized based on surface observations, roughness, and free energy (SFE). RESULTS: The SBSs of all materials bonded using Panavia were significantly compromised during thermocycling and reached zero. Although the SBSs of Ti and Ti-6Al-4V bonded using Super-Bond were not significantly affected by thermocycling, those of zirconia decreased significantly. The bond durability between zirconia and Super-Bond was improved via alumina air-abrasion, which caused no significant loss of SBS after thermocycling. Surface analyses of the air-abraded zirconia validated these results and confirmed that its surface roughness and SFE were significantly increased. CONCLUSION: The bond durability between resin cement and zirconia was lower than that between Ti and Ti-6Al-4V. The alumina air-abrasion pretreatment of zirconia improved the SFE and surface roughness, thereby enhancing bond durability.

Alternativas de tratamiento para pacientes jóvenes con pérdida de estructura dentaria. Parte 2: caso clínico / Treatment alternatives for young patients with loss of dental structure. Part 2: a clinical case

El objetivo de este artículo es presentar una alternativa de tratamiento rehabilitador para pacientes jóvenes con gran pérdida de estructura dental, vinculada a lesiones de origen no bacteriano. Se presenta el caso clínico de un paciente de sexo masculino, de 39 años de edad, que acudió a la Cátedra de Odontología Integral Adultos de la Facultad de Odontología de la Universidad de Buenos Aires (FOUBA) relatando síntomas compatibles con hipersensibilidad dentaria y fatiga de los músculos masticadores. Al mismo tiempo, manifestó disconformidad con el aspecto estético de su sonrisa. Teniendo en cuenta la gran pérdida de sustancia en sus piezas dentarias producida por hábitos parafuncionales (bruxismo), se realizó una rehabilitación oral adhesiva con cerámicas utilizando el protocolo de abordaje terapéutico sugerido por la Cátedra. En pacientes que presentan severos desgastes (AU)

Adhesive resistance of a copaiba oil-based dentin biomodifier.

This study analyzed the effect of prior application of copaiba oil (CO) emulsions as a dentin cleaning substance on microleakage and microtensile adhesive strength. Twenty-five premolars and sixty-four molars were used for microleakage and microtensile assays. For the microleakage assays, specimens with standard class V cavities were divided (n = 5), according to the tested CO emulsions: CO10%X, CO10%Y, and CO10%Z, as well as chlorhexidine 2% (CHX) and distilled water (DW), as positive and negative controls, respectively. Restorations were performed using the Adper Single Bond® and/or Clearfil SE Bond® systems. Cervical, occlusal, distal and mesial sections were assessed for tracer penetration degree at the composite/tooth interface. For the microtensile assay, healthy molars were divided into sixteen groups, in which artificial caries were induced in half of the groups. Dentin surfaces were treated with CO10%X and CO10%Y, CHX and DW. Microtensile bond strength was measured by fixing each sample to the plate of a universal testing machine operated at a speed of 0.5 mm/minute until failure. Dentin treated with CO10%X showed a lower infiltration rate than dentin treated with the other CO emulsions, CHX2% and DW. According to the microtensile assay, both healthy and affected dentin treated with CO10%X and Adper Single Bond® adhesive system presented higher adhesive strength. CO emulsion, used as a dentin biomodifier, interfered positively in microleakage and improved adhesive strength after acid etching in the Adper Single Bond® adhesive system, or before applying the Clearfil SE Bond® self-etching system.