Photopolymerization of dental resin as restorative material using an argon laser.

The effect of the 488-nm wavelength of argon laser at different power densities and irradiation times on the degree of conversion (DC), temperature rise, water sorption, solubility, flexural strength, flexural modulus, and microhardness of bisphenole A glycol dimethacrylate and triethylen glycol dimethacrylate with a mass ratio of 75:25 was studied. Camphorquinone and N,N'-dimethyl aminoethyl methacrylate were added to the monomer as a photo initiator system. The DC% of the resin was measured using Fourier transform infrared spectroscopy. The maximum DC% (50%), which was reached in 20 s, and temperature rise because of the reaction (13.5 degrees C) were both higher at 1075 than 700 mW/cm(2). Water sorption and solubility were measured according to ISO4049, which in our case were 23.7 and 2.20 microg/mm(3) at 1075 mW/cm(2), respectively. A flexural modulus of 1.1 GPa and microhardness of 19.6 kg/mm(2) were achieved above the power density. No significant difference was observed (i.e., p>0.05) for water sorption and flexural strength at 700 and 1075 mW/cm(2).

Bond strengths of two ceramic brackets using argon laser, light, and chemically cured resin systems.

The present study compared tooth-bracket bond strengths using two types of ceramic brackets and three methods of polymerization: argon laser, conventional light, and chemical. Ninety extracted human premolars were prepared for bonding with pumice and gel etchant. Using single crystal alumina brackets with silanated bases, three groups of 15 teeth were bonded with one of the three polymerization methods. Similarly, three groups of 15 teeth were bonded with polycrystal alumina brackets with nonsilanated bases. Each bonded bracket was tested on an Instron tensile testing machine in shear mode to determine shear debonding strength. Fracture sites were recorded. Results demonstrated that (1) all combinations produced shear bond strengths greater than those considered clinically acceptable, (2) the mean shear bond strengths of the single crystal alumina brackets with silanated bases were significantly higher than those of the polycrystal alumina brackets with nonsilanated bases, and (3) no enamel fractures were found on debonding the chemically cured brackets while the light and laser groups exhibited a 10% rate of enamel fracture on debonding.