The adhesive strength of fiber post-to-canal dentin with Aniline green, Fotoenticine activated by PDT, green tea, and ozone as a final irrigant.

AIM: The effect of novel final disinfection protocols Malachite green (MG), Fotoenticine® (FTC), Green tea extract (GTE), and Ozonated water (OW) on the bond strength of prefabricated glass fiber posts (PGFP) adhered to canal dentin. MATERIAL AND METHOD: The canals of fifty premolars with closed apices were cleansed and obturated. The specimens were randomly assigned to one of five groups based on the final irrigant used, with the control group receiving NaOCl+EDTA and the experimental groups receiving MG, FTC, OW, and GTE. The GFP was cemented with a self-etching, dual-cure paste; the bond strength was estimated with a universal testing machine; and failure analysis was conducted with a stereomicroscope. RESULTS: The highest PBS was observed in the coronal third of Group 4 (using ozonated water as the final irrigant), whereas the lowest bond integrity was observed in the apical section of Group 2 (1.02-0.54 MPa) using Malachite green as the final irrigant. Group 1, Group 4, and Group 5 exhibited no significant difference in the bond integrity of GFP to dentin when compared to Group 2 (p>0.05). In addition, comparable bond score values were obtained for Groups 2 and 3 (p>0.05). CONCLUSION: The results of this study suggest that OW and GTE may be effective final disinfectants for root canals, as they increase the bond strength of resin-luting cement.

Influence of photodynamic therapy, different final irrigants, and ultrasonic activation on the bond strength of glass fiber posts to root dentin.

OBJECTIVE: To evaluate the influence of photodynamic therapy (PDT), different final irrigants, and ultrasonic activation (US) on the bond strength of glass fiber posts (GFP) to root dentin. METHODS: One hundred twenty bovine roots were divided into 12 groups according to PDT application, the type of final endodontic irrigant, and US. The samples were divided into 12 groups (n = 10): G1-DW(distilled water); G2-DW+US; G3-17% EDTA; G4-17% EDTA+US; G5-17% GA (glycolic acid); G6-17% GA+US; G7-PDT+DW; G8-PDT+DW+US; G9-PDT+17% EDTA; G10-PDT+17% EDTA+US; G11-PDT+17% GA; G12-PDT+17% GA+US. After cementing the glass fiber posts with resin cement, roots were sectioned into 2-mm-thick slices. One slice from the cervical third and another from the middle third were used for the push out test (PO), and the other two for the diametral compression test (DC). Thus, 10 samples were obtained per third for each mechanical test (n = 10). Kruskal-Wallis and Student-Newman-Keuls tests were used to analyze PO and DC data, and Pearson's correlation test was used to verify the relationship between the variables. Failure patterns were analyzed with chi-square test. RESULTS: Significant differences were found in the PO test among the experimental groups (p < 0.001; power=1.00). PDT improved bond strength when using EDTA. PDT and US increased bond strength when using GA. Favorable failure patterns occurred more frequently in Group GA+US. There was no correlation between data obtained with PO and DC tests (r = 0.112; p = 0.729). CONCLUSION: PDT provided the highest bond strength values of GFP to root dentin when associated with GA and US or when associated only with EDTA.

Does the bonding effectiveness of a fiber post/resin composite benefit from mechanical or chemical treatment? Seven methods for saliva-contaminated surfaces.

PURPOSE: This study examined four cleaning methods and three chemical treatments for artificial saliva-contaminated fiber posts in terms of bonding durability to resin composite core materials. METHODS: Non-contaminated fiber posts (Tokuyama FR Post, Tokuyama Dental) and those contaminated (GC Fiber Post, GC) with artificial saliva (Saliveht Aerosol, Teijin Pharma) were used. Washing and drying (WD), alcohol cleaning (AlC), H3PO4 etching (P/WD), alumina blasting (B/D) for decontamination and silanization (Clearfil Ceramic Primer Plus, Kuraray Noritake Dental, Si), resin priming (HC Primer, Shofu, MMA), and bonding resin application (Clearfil Universal Bond Quick, Kuraray Noritake Dental, BR) for chemical treatment were performed. The treated fiber post was planted inside a cylindrical tube and filled with resin composite (DC Core Automix ONE, Kuraray Noritake Dental). The specimen was sectioned, and a push-out test was performed after 24 h, 1 month, and 3 months. The fracture surface was observed using a scanning electron microscope (SEM). RESULTS: Adhesion between the non-contaminated fiber post and resin composite did not improve by silanization and decreased by alumina blasting. SEM observations revealed a fractured glass fiber by alumina blasting. Saliva contamination decreased the bond strength between the fiber post and resin composite; however, recovery was achieved by WD, Alc, P/WD, and B/D. Compared to Si, BR (P = 0.009) was effective in restraining the long-term durability of bonding, whereas MMA (P = 0.99) was not. CONCLUSION: The application of bonding resin after alcohol cleaning is the most convenient and effective clinical procedure for fiber post surface treatment.

Photodynamic therapy and gaseous ozone versus conventional post space treatment methods on the push-out bond strength of fiber posts luting with different resin cements.

BACKGROUND: The aim of this study was to compare the push-out bond strength of fiber posts by using two different resin cement after the treatments of post space with photodynamic therapy, gaseous ozone and conventional disinfection solution. METHODS: The root canal treatments of one hundred maxillary incisors were performed. The roots were randomly distributed into 5 groups (n = 20). NaOCl of 2.5% + EDTA of 17% in group 1, CHX of 2% in group 2, toluidine blue + diode laser as the photodynamic therapy (PDT) in group 3 and ozone in group 4 were applied to the post spaces. Group 5 was washed with distilled water as control group. Each group was divided into two subgroups according to the adhesive types and the posts were bonded by using RelyX and LinkForce. The bond strength was calculated using the push-out test method. Resin tag formations were photographed with SEM. The push-out bond strength was analyzed by ANOVA and Tukey tests (p = .05). RESULTS: The PDT group, which showed the highest PBS among the groups bonded with LinkForce at all levels, was significantly higher than Ozone and DW groups (p<.05). NaOCl and ozone treatments provided the highest PBS among the groups bonded with RelyX for all levels and this difference was significant according to the DW group (p < .05). CONCLUSION: Post space treatments improved the bond strength of the fiber post ​​in both types of resin cement.

Influence of two photodynamic therapy sessions and different photosensitizers on the bond strength of glass-fiber posts in different regions of intraradicular dentin.

BACKGROUND: Although photodynamic therapy associated with photosensitizers can promote microbial reduction, studies evaluating the consequences of two photodynamic therapy sessions associated with different photosensitizers on the bond strength of glass-fiber posts to endodontically treated intraradicular dentin are scarce. This in vitro study aimed to investigate the influence of two photodynamic therapy sessions using methylene blue or curcumin photosensitizers on the bond strength of glass-fiber posts to intraradicular dentin in different root thirds. METHODS: Seventy-two teeth were divided into 9 experimental groups according to photosensitizer type, concentration and light-activation: Control - deionized water; Methylene blue 50 mg/L; Methylene blue 50 mg/L + laser; Methylene blue 100 mg/L; Methylene blue 100 mg/L + laser; Curcumin 500 mg/L; Curcumin 500 mg/L + LED; Curcumin 1000 mg/L; and Curcumin 1000 mg/L + LED. Push-out bond strength of the fiber posts to endodontically treated dentin was evaluated using a universal test machine (n = 8). Bond strength data underwent Kruskal-Wallis test, followed by Dunn test for comparison between treatments, and Friedman test for comparison between thirds (α = 0.05). Illustrative scanning electron microscopy images were obtained to qualify the failure mode. RESULTS: Curcumin at higher concentration, activated or not by blue LED, decreased the bond strength values in the apical region when compared with the control group (P < 0.05). There was no difference between two photodynamic therapy sessions using methylene blue photosensitizer (activated or not) and the control group regardless of concentrations and root canal depth evaluated (P > 0.05). Regarding intraradicular depth, the different thirds showed no statistical difference on bond strength values (P > 0.05). All experimental groups presented predominance of mixed-type failure, excepting the methylene blue group at higher concentration activated by red laser, and the curcumin photosensitizer at both concentrations activated by blue LED. CONCLUSIONS: Methylene blue at a 50 mg/L concentration can be applied in two PDT sessions, after biomechanical preparation and before glass-fiber post luting, as it presents no influence on root dentin bond strength in in vitro conditions.

Caries temprana de la infancia: rehabilitación estética, funcional e integral en paciente preescolar. Caso clínico / Early childhood caries: esthetic, functional and comprehensive rehabilitation in preschool patient. A clinical case

La American Academy of Pediatric Dentistry (2020) define a la caries temprana de la infancia (CTI) como una forma severa de caries de etiología multifactorial que compromete la dentición primaria de niños pre-escolares. Afecta principalmente a los incisivos primarios superiores seguidos de los primeros molares primarios, pudiendo promover el desarrollo de hábitos parafuncionales, reducción de la eficacia masticatoria, pérdida de la dimensión vertical, alteraciones en la fonación y defectos estéticos que causan repercusiones emocionales e impacto psicosocial. La insuficiente cantidad y calidad de estructura coronaria remanente, luego de la eliminación del tejido cariado, puede comprometer la adhesión de los materiales de restauración. El objetivo de este trabajo es presentar la atención y el seguimiento a dos años de un paciente preescolar que presenta CTI, que concurrió para su atención a la Cátedra de Odontología Integral Niños de la Facultad de Odontología de la Universidad de Buenos Aires (AU)

Treatment of severely decayed anterior primary teeth with short-post technique (Mushroom Restorations) under general anesthesia.

AIMS: The aim of this study was to evaluation the treatment success of the short post technique (mushroom restoration) using a composite resin in severely decayed primary anterior teeth after 6, 12, and 18 months after treatment. METHODS: Eighteen children aged 3-5 years with severely decayed primary maxillary anterior teeth (60 anterior maxillary primary teeth in total) were included. Patients were treated under general anesthesia (GA). After pulpectomy, a "mushroom shape" was formed in the root canals for the purpose of retention, and the root canals were filled with zinc oxide-eugenol (ZOE), and the teeth were restored with composite resin. The status of treatment was evaluated clinically and radiographically for periapical radiolucency, pathological root resorption, marginal fracture, and loss of restoration for each treated tooth. All findings were recorded. RESULTS: As a result of the evaluation criteria, the success rates at 6, 12 and 18 months were 86%, 80%, and 71%, respectively. None of the teeth showed apical radiolucency or pathological root resorption at the end of the 18th month period. CONCLUSION: The short-post (mushroom restorations) technique is a clinically acceptable alternative method for restoration of severely decayed primary teeth. This study supports the feasibility of treatment with this technique for pediatric patients treated under GA.

The Effect of Cold Atmospheric Plasma (CAP) Treatment at the Adhesive-Root Dentin Interface.

PURPOSE: To investigate the use of a cold atmospheric plasma (CAP) source in a clinically realistic endodontic procedure to enhance the bond strength of a dental adhesive in root canal restoration. MATERIALS AND METHODS: CAP was generated by a handheld DBD-jet prototype specifically designed for biomedical applications. Extracted monoradicular teeth were standardized through crown sectioning and root canal shaping before being embedded in epoxy resin cylinders using a custom molding procedure designed to ensure the accurate alignment of the specimens. Afterwards, the dentin surface was conditioned according to different protocols including (or not, in controls) chelating agents (EDTA or IP6) and CAP treatment (180 s). Then a self-etch adhesive was applied, followed by a luting material to seal the root canal. Both materials were light cured. Tooth sections were obtained from coronal and middle portions of the root canal, and the push-out test was used to evaluate the bond strength between the adhesive and dentin. RESULTS: Push-out results demonstrated that plasma treatment greatly improved (> twofold) the mechanical properties of the adhesive-dentin interface along the whole length of the root canal. Contact angle measurements and SEM analyses showed that plasma treatment facilitated adhesive permeation into dentinal tubules, hence enhancing the effects of the bonding procedure. CONCLUSIONS: Although investigations on long-term bond stability after CAP treatment and clinical studies are required, the present study indicates that CAP devices may be useful in clinical endodontic treatment.

Influence of final irrigation protocols and type of resin cement on bond strength of glass fiber posts in root dentin previously treated with photodynamic therapy.

INTRODUCTION: This study aimed to evaluate the influence of final irrigation protocols and type of resin cement on the bond strength of glass fiber posts (GFPs) in root dentin previously treated with photodynamic therapy (PDT). METHODS: One hundred root canals were prepared up to #4 Gates Glidden drill to receive the GFPs. All samples were subjected to PDT, and randomly divided into five groups (n = 20) according to final irrigation protocol: distilled water + ultrasonic activation [US]; 17% EDTA; QMix; 17% EDTA + US; and QMix + US. Each group was randomly divided into 2 subgroups (n = 10) according to the type of resin cement used for cementation of GFPs: Rely-X ARC dual-resin; or Rely-X U200 (#M, St Paul, MN, USA) self-adhesive resin cement. Bond strength was evaluated using the push-out test. Failure patterns were observed under an optical microscope. Bond strengths were compared using two-way ANOVA, followed by the Tukey post-hoc test; failure modes were compared using the chi-squared test (α = 5%). RESULTS: The use of US over final irrigants improved the bond strength of GFPs, regardless of resin cement used (p < 0.05). The type of resin cement did not influence the bond strength of GFPs (p < 0.05). There was a higher predominance of cohesive failure in all groups, regardless of resin cement tested (p < 0.05). CONCLUSIONS: The use of US on final irrigation improved the bond strength of GFPs, while the type of resin cement (dual or self-adhesive) did not influence the bond strength of GFPs in root dentin previously treated with PDT.

Effect of photodynamic therapy on the mechanical properties and bond strength of glass-fiber posts to endodontically treated intraradicular dentin.

STATEMENT OF PROBLEM: The use of photosensitizers in photodynamic therapy promotes intraradicular microbial reduction during nonsurgical endodontic therapy. However, studies are lacking on the consequences of the application of these agents on the mechanical properties of intraradicular dentin and on the bond strength of glass-fiber posts. PURPOSE: The purpose of this in vitro study was to evaluate the influence of photodynamic therapy on the bond strength of glass-fiber posts using a push-out test and, additionally, to measure the Martens hardness (MH) and elastic indentation modulus (Eit) of intraradicular dentin when different photosensitizers are used. MATERIAL AND METHODS: Eighty bovine teeth were used to simulate experimental endodontic treatments. Biomechanical instrumentation was performed for all root canals, and the teeth were distributed into 5 groups: control-deionized water; methylene blue 50 mg/L + red laser; methylene blue 100 mg/L + red laser; curcumin 500 mg/L + blue LED; and curcumin 1000 mg/L + blue LED. The MH and Eit of intraradicular dentin were measured using an ultramicrohardness tester under a load of 3 mN (n=8). The push-out bond strength of glass-fiber posts to dentin was measured using a universal testing machine (n=8). Mechanical properties and bond strength data were subjected to the Kruskal-Wallis test, ANOVA, and Fisher least significant difference test (α=.05). Images of representative specimens were obtained using a scanning electron microscope. RESULTS: The MH, Eit, and bond strength of intraradicular dentin were influenced by the photosensitizer used. In general, curcumin promoted lower mechanical properties values but higher bond strength values. CONCLUSIONS: Photosensitizers influenced the mechanical properties of intraradicular dentin and the bond strength of glass-fiber posts, and methylene blue at 50 mg/L had no marked effect on the mechanical properties of the dentin or the bond strength values.

Effects of Postsurface Treatments Including Femtosecond Laser and Aluminum-oxide Airborne-particle Abrasion on the Bond Strength of the Fiber Posts.

CONTEXT: Bond strength of fiber posts. AIMS: The purpose of this study was to evaluate the effect of different Post Surface treatment techniques on the push-out bond strength of the quartz fiber posts. SUBJECTS AND METHODS: A total of 30 maxillary central incisors were decoronated at cementoenamel junction. Root canals were filled and postspaces were prepared. The specimens were classified into three groups according to the surface treatment performed to the postsurface (n = 10) as no surface treatment (control group) (Group 1), A 50-µm aluminum-oxide airborne-particle abrasion group (Group 2), femtosecond laser (FS) group (Group 3). A self-curing adhesive cement was used for cementation of posts. Six sections (two coronal, two middle, and two apical) of 1-mm thickness specimens were prepared with a slow speed diamond saw. Specimens were stored in distilled water at 37°C for 24 h. Then, push-out test was performed on a universal testing machine. RESULTS: The data were analyzed by one-way ANOVA (α = 0.05). The test results indicated that push-out test values significantly different according to surface treatments among groups (P < 0.05). There were no significant differences between root sections of each group for bond strength (P > 0.05). All dislodged Group 3 posts were free of cement, indicating adhesive failure, Group 1 and 2 were partially coated with cement, indicating a mixed failure at the cement/postsurface. CONCLUSIONS: Based on the results, aluminum-oxide airborne-particle abrasion group showed higher and FS irradiation group showed lower bond strength values. Push-out bond strength values of the root segments were the same in all groups.

Can intra-radicular cleaning protocols increase the retention of fiberglass posts? A systematic review.

The presence of residues within the root canal after post-space preparation can influence the bond strength between resin cement and root dentin when using fiberglass posts (FGPs). Currently, there is no consensus in the literature regarding what is the best solution for the removal of debris after post-space preparation. This systematic review involved "in vitro" studies to investigate if cleaning methods of the root canal after post-space preparation can increase the retention of FGPs evaluated by the push-out test. Searches were carried out in PubMed (MEDLINE) and Scopus databases up to July2017. English language studies published from 2007 to July 2017 were selected. 475 studies were found, and 9 were included in this review. Information from the 9 studies were collected regarding the number of samples, storage method after extraction, root canal preparation, method of post-space preparation, endodontic sealer, resin cement, cleaning methods after post-space and presence of irrigant activation. Five studies presented the best results for the association of sodium hypochlorite (NaOCl) and ethylenediamine tetra-acetic acid (EDTA), while in the other 4 studies, the solutions that showed improved retention of FGPs were photon-induced photoacoustic streaming (PIPS), Qmix, Sikko and EDTA. The results showed heterogeneity in all comparisons due to a high variety of information about cleaning methods, different concentrations, application time, type of adhesive system and resin cements used. In conclusion, this review suggests that the use of NaOCl/EDTA results in the retention of FGPs and may thus be recommended as a post-space cleaning method influencing the luting procedure.

Influence of Zingiber officinale Extract on Push-Out Bond Strength of Glass-Fiber Post

Abstract The aim of this study was to evaluate in vitro the influence of 20% glycolic ginger extract on the bond strength of glass-fiber post cemented with etch-and-rinse or self-etching resin cement. Forty-eight bovine roots were standardized (17±0.5 mm) and randomly divided into two groups, according to irrigant used during biomechanical preparation: NaOCl: 1% sodium hypochlorite and GEN: 20% glycolic ginger extract. Root canal was prepared and randomly assigned to one of two subgroups (n=12), according to luting protocol: self-etching (RelyX U200) and etch-and-rinse (RelyX ARC). After 48 h, the roots were sectioned perpendicularly (4 in cervical third and 3 in middle third) and submitted to push-out bond strength test (50 kgf load cell, 1.0 mm/min). Failure mode was analyzed in SEM and stereomicroscopy. Data were analyzed by three-way ANOVA and Tukey tests (p<0.05). ANOVA revealed that there were no significant differences between U200 (2.01±0.17)B and ARC (1.93±0.12)B in GEN group, and at the cervical third for both irrigants, 2.69±0.16A and 2.54±0.17A, respectively. Middle third showed lower bond strength than cervical third, regardless the irrigant. Overall, the cervical third regardless the irrigant employed and the association between NaOCl and ARC, presented better adhesive performance.

Resumo O objetivo deste estudo foi avaliar in vitro a influência do extrato de gengibre 20% na resistência adesiva de pinos de fibra de vidro cimentados com cimentos resinosos convencional ou autocondicionantes. Quarenta e oito raízes bovinas foram padronizadas (17±0.5mm) e aleatoriamente divididas em dois grupos (n=24), de acordo com o irrigante utilizado durante o preparo biomecânico: NaOCl: hipoclorito de sódio 1%; e GEN: extrato glicólico de gengibre 20%. Os canais radiculares foram preparados e aleatoriamente distribuídos em dois subgrupos (n=12), conforme o protocolo de cimentação: autocondicionante (RelyX U200) e convencional (RelyX ARC). Após 48 h, as raízes foram seccionadas perpendicularmente (4 no terço cervical e 3 no terço médio) e submetidas ao teste de resistência adesiva push-out (50 kgf carga, 1.0 mm/min). O modo de falha foi analisado em MEV e estereomicroscopia. Os dados foram analisados pelos testes ANOVA 3-fatores e Tukey (p<0.05). ANOVA mostrou que não houve diferenças significativas entre U200 (2.01±0.17)B e ARC (1.93±0.12)B no grupo GEN, e no terço cervical para ambos os irrigantes (2.69±0.16A and 2.54±0.17A, respectivamente). O terço médio apresentou menor resistência adesiva que o terço cervical, independente do irrigante. Em geral, o terço cervical, independentemente do irrigante empregado, e a associação entre NaOCl e ARC apresentaram melhores desempenhos adesivos.

Influence of Zingiber officinale Extract on Push-Out Bond Strength of Glass-Fiber Post.

The aim of this study was to evaluate in vitro the influence of 20% glycolic ginger extract on the bond strength of glass-fiber post cemented with etch-and-rinse or self-etching resin cement. Forty-eight bovine roots were standardized (17±0.5 mm) and randomly divided into two groups, according to irrigant used during biomechanical preparation: NaOCl: 1% sodium hypochlorite and GEN: 20% glycolic ginger extract. Root canal was prepared and randomly assigned to one of two subgroups (n=12), according to luting protocol: self-etching (RelyX U200) and etch-and-rinse (RelyX ARC). After 48 h, the roots were sectioned perpendicularly (4 in cervical third and 3 in middle third) and submitted to push-out bond strength test (50 kgf load cell, 1.0 mm/min). Failure mode was analyzed in SEM and stereomicroscopy. Data were analyzed by three-way ANOVA and Tukey tests (p<0.05). ANOVA revealed that there were no significant differences between U200 (2.01±0.17)B and ARC (1.93±0.12)B in GEN group, and at the cervical third for both irrigants, 2.69±0.16A and 2.54±0.17A, respectively. Middle third showed lower bond strength than cervical third, regardless the irrigant. Overall, the cervical third regardless the irrigant employed and the association between NaOCl and ARC, presented better adhesive performance.

Effect of Laser Etching on Glass Fiber Posts Cemented with Different Adhesive Systems.

BACKGROUND: Glass fiber-reinforced posts have been preferred frequently because of some physical properties similar to the dentin, chemically bonding to dentin, biocompatibility, and esthetics. OBJECTIVE: This study aimed to evaluate the microleakage and bond strength of glass fiber posts cemented with various adhesive systems on laser-etched root canal walls. METHODS: Roots of 120 human mandibular premolars were divided into two groups for push-out bond strength test and the microleakage test (n = 60). Erbium-doped yttrium-aluminum-garnet (Er:YAG) laser etching of the root canal walls was carried out on half of the specimens in both test groups. The laser-treated and laser-nontreated groups were divided again into three subgroups (n = 10). Glass fiber posts (everStick Post) were luted using three different resin cements: total-etch (Variolink N), self-etch (Panavia F 2.0), and self-adhesive (Rely X Unicem). Three dentin discs were obtained from each root, and the bond strength of the glass fiber posts was measured by push-out tests. The dye penetration method was used to investigate coronal microleakage. In addition, surface treatments and the bonding interfaces were observed using scanning electron microscope. RESULTS: The highest bond strengths were observed for the total-etch and self-adhesive resin cement groups with laser etching (p < 0.05), and the lowest bond strength was obtained for the self-etch resin cement group (p < 0.05). There were no statistically significant differences in terms of microleakage (p > 0.05), except for the self-adhesive resin cement group (p < 0.05). CONCLUSIONS: Er:YAG laser etching enhances the bonding strength of glass fiber posts. In addition, laser etching can reduce microleakage of self-adhesive resin cement.

Can intra-radicular cleaning protocols increase the retention of fiberglass posts? A systematic review

Abstract The presence of residues within the root canal after post-space preparation can influence the bond strength between resin cement and root dentin when using fiberglass posts (FGPs). Currently, there is no consensus in the literature regarding what is the best solution for the removal of debris after post-space preparation. This systematic review involved "in vitro" studies to investigate if cleaning methods of the root canal after post-space preparation can increase the retention of FGPs evaluated by the push-out test. Searches were carried out in PubMed (MEDLINE) and Scopus databases up to July2017. English language studies published from 2007 to July 2017 were selected. 475 studies were found, and 9 were included in this review. Information from the 9 studies were collected regarding the number of samples, storage method after extraction, root canal preparation, method of post-space preparation, endodontic sealer, resin cement, cleaning methods after post-space and presence of irrigant activation. Five studies presented the best results for the association of sodium hypochlorite (NaOCl) and ethylenediamine tetra-acetic acid (EDTA), while in the other 4 studies, the solutions that showed improved retention of FGPs were photon-induced photoacoustic streaming (PIPS), Qmix, Sikko and EDTA. The results showed heterogeneity in all comparisons due to a high variety of information about cleaning methods, different concentrations, application time, type of adhesive system and resin cements used. In conclusion, this review suggests that the use of NaOCl/EDTA results in the retention of FGPs and may thus be recommended as a post-space cleaning method influencing the luting procedure.

Morphology of root canal surface: A reflection on the process of cementation of the composite relined glass fiber post.

BACKGROUND: The present study was conducted to evaluate the bond strength in the different root thirds (premolars and maxillary central incisors) of composite relined glass fiber posts compared to untreated glass fiber posts cemented with dual- or chemical-cure cements. MATERIALS AND METHODS: Sixty human single-rooted premolars (flat canal) (n = 15) and 12 maxillary central incisors were used (round canal) (n = 3). The teeth were sectioned, and the roots received endodontic treatment. The standardized preparation of the canals was carried out, and the roots were randomly divided into four groups according to the cementation systems: G1: cemented posts (dual: Ambar/Allcem); G2: relined posts (dual: Ambar/Allcem); G3: cemented posts (chemical: Fusion Duralink/Cement Post); and G4: relined posts (chemical: Fusion Duralink/Cement Post). The roots were cut to give two slices of each third of the root canal per specimen. Push-out test was conducted at a speed of 0.5 mm/min. Data were analyzed by analysis of variance and Tukey's post hoc test (α = 0.05). RESULTS: There was no statistically significant difference between groups for the premolars (flat canal) (P = 0.959). There was a significant difference in the central incisors between the middle and apical thirds in the cemented group when using the dual system (P = 0.04) and between the middle and apical thirds (P = 0.003) and cervical and apical thirds (P = 0.033) when using the chemical system. CONCLUSION: Due to the anatomy of the root canal, flat canal of the premolars does not require relining, but round canal of the maxillary central incisors demands it for more secure in the bond strength.

Influence of root dentin treatment on the push-out bond strength of fibre-reinforced posts

This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols.

Influence of root dentin treatment on the push-out bond strength of fiber posts.

The aim of the present study was to assess whether different dentin conditioning protocols with different acids [phosphoric acid, ethylene diamine tetra acetic acid (EDTA), and polyacrylic acid (PAA)] influence the bond strength of fiber posts along the radicular depth when luted with self-adhesive resin cement. Twenty single-rooted teeth were randomly divided into four experimental groups (n = 5) according to dentin treatment: Group 1: no treatment; Group 2: etching with 35 % phosphoric acid for 10 s; Group 3: 17 % EDTA application for 60 s; and Group 4: conditioning with 25 % PAA for 30 s. RelyX Fiber Posts were luted with the self-adhesive resin cement RelyX Unicem 2 Automix (3M ESPE). Roots were transversally sectioned into nine 1-mm thick specimens, three corresponding to each root third and a push-out test was performed. Data were analyzed by two-way ANOVA and Tukey test (p < 0.05). Failure mode was determined and specimens with representative failures for each group were observed under scanning electron microscopy. According to the results, dentin treatment influenced the bond strength (p < 0.001), whereas the root third did not (p > 0.05). Fiber posts luted after treating dentin with phosphoric acid, and PAA exhibited the highest push-out bond strength values, while the lowest were obtained after EDTA application. Intermediate results were obtained when dentin was not conditioned. In conclusion, the bond strength of the self-adhesive resin cement RelyX Unicem 2 improves when root dentin is treated with 35 % phosphoric acid or 25 % PAA, before fiber posts luting irrespective of the root depth.

Influence of root dentin treatment on the push-out bond strength of fibre-reinforced posts

Abstract This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols.