RESUMO
This study aimed to investigate the failure behavior of 3 mol.% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) prosthetic crowns air-abraded with aluminum oxide (AO) particles of different sizes. Ninety ceramic premolar crowns were produced with 3Y-TZP frameworks veneered with porcelain. Crowns were randomly divided into three groups, according to the size of the air abrasion AO particles (n = 30): (GC) untreated (control); (G53) 53 µm; (G125) 125 µm. Air abrasion was performed with 0.25 mpa pressure, 10-mm distance, for 10 s. Crowns were adhesively cemented to dentin analog abutments. Specimens were loaded in compression to failure, in 37oC distilled water, using a universal testing machine (n = 30). Fractographic analysis was performed using a stereomicroscope and SEM. The roughness of the crown's inner surface was evaluated using an optical profilometer (n = 10). Fracture load data were statistically analyzed with Weibull analysis and roughness data with Kruskal-Wallis (α = 0.05). GC had the lowest characteristic fracture load (L0), while G53 and G125 had higher and statistically similar L0 values. The Weibull modulus (m) was similar among groups. The failure modes observed were catastrophic failure and porcelain chipping. There were no differences between the roughness parameters for the experimental groups (p > 0.05). The size of the AO particles did not affect the fracture load and failure mode of 3Y-TZP crowns. Air abrasion with 53 µm and 125 µm particles resulted in a higher fracture load of ceramic crowns than the untreated group while maintaining their reliability and surface characteristics.
Assuntos
Abrasão Dental por Ar , Porcelana Dentária , Óxido de Alumínio/química , Cerâmica/química , Coroas , Porcelana Dentária/química , Análise do Estresse Dentário , Teste de Materiais , Tamanho da Partícula , Reprodutibilidade dos Testes , Propriedades de Superfície , Zircônio/químicaRESUMO
OBJECTIVE: To evaluate the influence of photodynamic therapy (PDT), different final irrigants, and ultrasonic activation (US) on the bond strength of glass fiber posts (GFP) to root dentin. METHODS: One hundred twenty bovine roots were divided into 12 groups according to PDT application, the type of final endodontic irrigant, and US. The samples were divided into 12 groups (n = 10): G1-DW(distilled water); G2-DW+US; G3-17% EDTA; G4-17% EDTA+US; G5-17% GA (glycolic acid); G6-17% GA+US; G7-PDT+DW; G8-PDT+DW+US; G9-PDT+17% EDTA; G10-PDT+17% EDTA+US; G11-PDT+17% GA; G12-PDT+17% GA+US. After cementing the glass fiber posts with resin cement, roots were sectioned into 2-mm-thick slices. One slice from the cervical third and another from the middle third were used for the push out test (PO), and the other two for the diametral compression test (DC). Thus, 10 samples were obtained per third for each mechanical test (n = 10). Kruskal-Wallis and Student-Newman-Keuls tests were used to analyze PO and DC data, and Pearson's correlation test was used to verify the relationship between the variables. Failure patterns were analyzed with chi-square test. RESULTS: Significant differences were found in the PO test among the experimental groups (p < 0.001; power=1.00). PDT improved bond strength when using EDTA. PDT and US increased bond strength when using GA. Favorable failure patterns occurred more frequently in Group GA+US. There was no correlation between data obtained with PO and DC tests (r = 0.112; p = 0.729). CONCLUSION: PDT provided the highest bond strength values of GFP to root dentin when associated with GA and US or when associated only with EDTA.
Assuntos
Fotoquimioterapia , Técnica para Retentor Intrarradicular , Humanos , Bovinos , Animais , Dentina , Ácido Edético , Fotoquimioterapia/métodos , Teste de Materiais , Cavidade PulparRESUMO
OBJECTIVE: To evaluate the effect of two aging methods (mechanical cycling and autoclave) on the mechanical behavior of veneer and framework ceramic specimens with different configurations (monolithic, two and three-layers). METHODS: Three ceramics used as framework for fixed dental prostheses (YZ-Vita In-Ceram YZ; IZ-Vita In-Ceram Zirconia; AL-Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs: monolithic, two layers (porcelain-framework) and three layers (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. Three different experimental conditions were evaluated (n=10): control; mechanical cycling (2Hz, 37°C artificial saliva); and autoclave aging (134°C, 2 bars, 5h). Bi-layered specimens were tested in both conditions: with porcelain or framework ceramic under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy. Results were statistically analyzed using Kruskal-Wallis and Student-Newman-Keuls tests. RESULTS: Only for AL group, mechanical cycling and autoclave aging significantly decreased the flexural strength values in comparison to the control (p<0.01). YZ, AL, VM7 and VM9 monolithic groups showed no strength degradation. For multi-layered specimens, when the porcelain layer was tested in tension (bi and tri-layers), the aging methods evaluated also had no effect on strength (p≥0.05). Total and partial failure modes were identified. SIGNIFICANCE: Mechanical cycling and autoclave aging protocols had no effect on the flexural strength values and failure behavior of YZ and IZ ceramic structures. Yet, AL monolithic structures showed a significant decrease in flexural strength with any of the aging methods.
Assuntos
Óxido de Alumínio , Cerâmica , Porcelana Dentária , Facetas Dentárias , Análise do Estresse Dentário , Teste de Materiais , Microscopia Eletrônica de Varredura , Estresse Mecânico , Propriedades de Superfície , ZircônioRESUMO
OBJECTIVES: The effect of the ceramic infrastructure (IS) on the failure behavior and stress distribution of fixed partial dentures (FPDs) was evaluated. METHODS: Twenty FPDs with a connector cross-section of 16 mm(2) were produced for each IS and veneered with porcelain: (YZ) Vita In-Ceram YZ/Vita VM9 porcelain; (IZ) Vita In-Ceram Zirconia/Vita VM7 porcelain; (AL) Vita In-Ceram AL/Vita VM7 porcelain. Two experimental conditions were evaluated (n = 10). For control specimens, load was applied in the center of the pontic at 0.5 mm/min until failure, using a universal testing machine, in 37°C deionized water. For mechanical cycling (MC) specimens, FPDs were subjected to MC (2 Hz, 140 N, 10(6) cycles) and subsequently tested as described for the control group. For YZ, an extra group of 10 FPDs were built with a connector cross-section of 9 mm(2) and tested until failure. Fractography and FEA were performed. Data were analyzed by ANOVA and Tukey's test (α = 0.05). RESULTS: YZ16 showed the greatest fracture load mean value, followed by YZ16-MC. Specimens from groups YZ9, IZ16, IZ16-MC, AL16 and AL16-MC showed no significant difference for the fracture load. SIGNIFICANCE: The failure behavior and stress distribution of FPDs was influenced by the type of IS. AL and IZ FPDs showed similar fracture load values but different failure modes and stress distribution. YZ showed the best mechanical behavior and may be considered the material of choice to produce posterior FPDs as it was possible to obtain a good mechanical performance even with a smaller connector dimension (9 mm(2)).
Assuntos
Óxido de Alumínio/química , Porcelana Dentária/química , Falha de Restauração Dentária , Planejamento de Dentadura , Prótese Parcial Fixa , Ligas Metalo-Cerâmicas/química , Análise do Estresse Dentário , Análise de Elementos Finitos , Teste de Materiais , Ítrio/químicaRESUMO
OBJECTIVE: To evaluate the effect of the specimen design on the flexural strength (σ(f)) and failure mode of ceramic structures, testing the hypothesis that the ceramic material under tension controls the mechanical performance of the structure. METHODS: Three ceramics used as framework materials for fixed partial dentures (YZ--Vita In-Ceram YZ; IZ--Vita In-Ceram Zirconia; AL--Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs (n=10): monolithic, two layers (porcelain-framework) and three layers (TRI) (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. For bi-layered design, the specimens were tested in both conditions: with porcelain (PT) or framework ceramic (FT) layer under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy (SEM). Young's modulus (E) and Poisson's ratio (ν) were determined using ultrasonic pulse-echo method. Results were statistically analyzed by Kruskal-Wallis and Student-Newman-Keuls tests. RESULTS: Except for VM7 and VM9, significant differences were observed for E values among the materials. YZ showed the highest ν value followed by IZ and AL. YZ presented the highest σ(f). There was no statistical difference in the σ(f) value between IZ and IZ-FT and between AL and AL-FT. σ(f) values for YZ-PT, IZ-PT, IZ-TRI, AL-PT, AL-TRI were similar to the results obtained for VM7 and VM9. Two types of fracture mode were identified: total and partial failure. SIGNIFICANCE: The mechanical performance of the specimens was determined by the material under tension during testing, confirming the study hypothesis.
Assuntos
Cerâmica/química , Porcelana Dentária/química , Algoritmos , Óxido de Alumínio/química , Silicatos de Alumínio/química , Polimento Dentário , Análise do Estresse Dentário/instrumentação , Facetas Dentárias , Módulo de Elasticidade , Temperatura Alta , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Maleabilidade , Compostos de Potássio/química , Saliva Artificial/química , Estresse Mecânico , Propriedades de Superfície , Temperatura , Ultrassom , Vácuo , Ítrio/química , Zircônio/químicaRESUMO
OBJECTIVES: To evaluate the effect of the microstructure on the Weibull and slow crack growth (SCG) parameters and on the lifetime of three ceramics used as framework materials for fixed partial dentures (FPDs) (YZ - Vita In-Ceram YZ; IZ - Vita In-Ceram Zirconia; AL - Vita In-Ceram AL) and of two veneering porcelains (VM7 and VM9). METHODS: Bar-shaped specimens were fabricated according to the manufacturer's instructions. Specimens were tested in three-point flexure in 37°C artificial saliva. Weibull analysis (n=30) and a constant stress-rate test (n=10) were used to determine the Weibull modulus (m) and SCG coefficient (n), respectively. Microstructural and fractographic analyzes were performed using SEM. ANOVA and Tukey's test (α=0.05) were used to statistically analyze data obtained with both microstructural and fractographic analyzes. RESULTS: YZ and AL presented high crystalline content and low porosity (0.1-0.2%). YZ had the highest characteristic strength (σ(0)) value (911MPa) followed by AL (488MPa) and IZ (423MPa). Lower σ(0) values were observed for the porcelains (68-75MPa). Except for IZ and VM7, m values were similar among the ceramic materials. Higher n values were found for YZ (76) and AL (72), followed by IZ (54) and the veneering materials (36-44). Lifetime predictions showed that YZ was the material with the best mechanical performance. The size of the critical flaw was similar among the framework materials (34-48µm) and among the porcelains (75-86µm). SIGNIFICANCE: The microstructure influenced the mechanical and SCG behavior of the studied materials and, consequently, the lifetime predictions.