Effect of Polymerization Unit, Polishing, and Coffee Thermocycling on the Color and Translucency of Additively Manufactured Resins Used for Definitive Prostheses.

PURPOSE: To evaluate the effect of polymerization unit, polishing, and coffee thermocycling on the color and translucency of additively manufactured polyurethane-based resins with different viscosities. In addition, their color behavior was compared with the color of the shade tab throughout the fabrication steps and aging. MATERIALS AND METHODS: Disk-shaped specimens (Ø10 × 2 mm) were fabricated from polyurethane-based resins with different viscosities (Tera Harz TC-80DP and C&B permanent; n = 30 per material). Baseline color coordinates were measured after cleaning. The specimens in each resin group were divided into three subgroups (n = 10 per subgroup) to be polymerized with different polymerization units (Otoflash G171 [FLN], Wash and Cure 2.0 [CLED1], and P Cure [CLED2]), polished, and subjected to coffee thermocycling. Color coordinates were remeasured after each process. Color differences (ΔE00) and relative translucency parameter (RTP) values were calculated. Data were statistically analyzed (α = .05). RESULTS: Time points and polymerization units affected the ΔE00 for each material (P ≤ .049). ΔE00 of each polymerization unit pair had significant differences within and among different time points within each material (P ≤ .024). ΔE00 (when compared with the shade tab) and RTP were mostly affected by polymerization units and time points within both materials (P ≤ .042). CONCLUSIONS: Tested polymerization units, polishing, and coffee thermocycling affected the color difference and translucency of tested resins. Color differences ranged from moderately unacceptable to extremely unacceptable, and the differences in translucency values mostly ranged from perceptible to unacceptable, according to previous thresholds. In addition, tested resin-polymerization unit pairs had unacceptable color differences when compared to the shade tab. CLED1 may enable higher color stability for tested resins.

Effect of coffee thermocycling on the surface roughness and stainability of denture base materials with different chemical compositions manufactured with additive and subtractive technologies.

OBJECTIVE: To evaluate the effect of coffee thermocycling (CTC) on the surface roughness (Ra ) and stainability of denture base materials with different chemical compositions fabricated by using additive and subtractive manufacturing. MATERIALS AND METHODS: Disk-shaped specimens were additively (FREEPRINT denture, AM) or subtractively (G-CAM, GSM and M-PM, SM) fabricated from three pink denture base materials in different chemical compositions (n = 10). Ra was measured before and after polishing, while color coordinates were measured after polishing. Specimens were subjected to CTC (5000 cycles) and measurements were repeated. Color differences (ΔE00 ) after CTC were calculated. Ra among different time intervals within materials was evaluated by using repeated measures analysis of variance (ANOVA), while 1-way ANOVA was used to evaluate the Ra of different materials within each time interval and the ΔE00 values. Color coordinates within each material were compared by using paired samples t-tests (α = 0.05). RESULTS: Ra before polishing was the highest for all materials (p < 0.001), while SM had its lowest Ra after CTC and AM had its lowest Ra after polishing (p ≤ 0.008). Before polishing, AM had the highest Ra among the materials (p < 0.001). After polishing, SM had higher Ra than AM (p < 0.001). After CTC, GSM had the lowest Ra (p ≤ 0.048). SM had the lowest (p ≤ 0.031) and AM had the highest (p < 0.001) ΔE00 . CTC decreased the a* and b* values of SM and AM (p ≤ 0.017), and increased the L* values of AM (p < 0.001). CONCLUSIONS: Polishing significantly reduced the surface roughness of all materials. CTC did not increase the surface roughness of materials above the clinically acceptable threshold. Only AM had perceptible color change when previously reported threshold values for denture base materials were considered. CLINICAL SIGNIFICANCE: Tested denture base materials may have similar surface stability after coffee thermocycling. However, subtractively manufactured denture base materials may have improved color stability when subjected to long-term coffee consumption.

Stainability and translucency of potassium aluminum sulfate applied computer-aided design and computer-aided manufacturing materials after coffee thermocycling.

OBJECTIVE: The purpose of this in vitro study was to evaluate the effect of potassium aluminum sulfate (alum) application on the stainability and translucency of computer-aided design and computer-aided manufacturing (CAD-CAM) materials after coffee thermocycling (CTC). MATERIALS AND METHODS: Disk-shaped specimens (Ø10 × 1 mm; N = 200) were fabricated by using additively (Crowntec [CT] and Varseo Smile Crown Plus [VS]) and subtractively manufactured (Brilliant Crios [RCR], CEREC Block [FC], and Vita Enamic [VE]) CAD-CAM materials and polished. All specimens were randomly divided into two groups as alum applied and control (n = 10). All specimens were then subjected to CTC (10,000 cycles at 5-55°C) and color coordinates were measured at each time interval. Color differences (ΔE00 ) and relative translucency parameters (RTPs) were calculated and the data were statistically analyzed (a = 0.05). RESULTS: Among tested time intervals, alum applied specimens had their lowest ΔE00 after alum application (p ≤ 0.006), except for FC (p = 0.177). In addition, alum applied RCR had lower ΔE00 values than its control specimens (p = 0.029). Alum applied specimens had their lowest RTP after CTC (p < 0.001) and alum application decreased the RTP of CT (p = 0.010). CTC reduced the RTP of all materials in control groups (p < 0.001). Alum applied CT had higher RTP than its control specimens (p = 0.049). CONCLUSIONS: Alum application's effect on color change varied depending on the material and alum mostly resulted in clinically acceptable changes in translucency. CTC led to unacceptable color and translucency changes based on previously reported threshold values. CLINICAL SIGNIFICANCE: Optical properties of CAD-CAM materials and the sustainability of these properties over time is critical for longevity. Alum may improve the color stability of reinforced composite resin when subjected to long-term coffee consumption.

Effect of coffee thermocycling on the surface roughness and stainability of nanographene-reinforced polymethyl methacrylate used for fixed definitive prostheses.

STATEMENT OF PROBLEM: A nanographene-reinforced polymethyl methacrylate (PMMA) has been introduced for definitive prostheses. However, knowledge on the surface roughness and stainability of this material is lacking. PURPOSE: The purpose of this in vitro study was to compare the surface roughness and stainability of nanographene-reinforced PMMA with those of a prepolymerized PMMA and a reinforced composite resin after coffee thermocycling. MATERIAL AND METHODS: Disk-shaped specimens (Ø10×1.5-mm) were prepared from 3 different A1-shade millable resins (prepolymerized PMMA [M-PM; PMMA]; nanographene-reinforced PMMA [G-CAM; G-PMMA]; reinforced composite resin [Brilliant Crios; RCR]). Surface roughness (Ra) values were measured before and after conventional polishing by using a noncontact profilometer. Initial color coordinates were measured over a gray background with a spectrophotometer after polishing. Specimens were then thermocycled in coffee for 5000 cycles. Measurements were repeated after coffee thermocycling, and color differences (ΔE00) were calculated. Ra values among different time intervals were analyzed by using either the Friedman and Dunn tests (RCR) or repeated measures analysis of variance (ANOVA) and Bonferroni corrected paired samples t tests (PMMA and G-PMMA), while Ra values within a time interval were analyzed by using either the Kruskal-Wallis and Dunn tests (before polishing) or 1-way ANOVA and Tukey HSD (after polishing) or Tamhane T2 tests (after coffee thermocycling). ΔE00 values were analyzed by using 1-way ANOVA and Tukey HSD tests, while color coordinates of the specimens after polishing and after coffee thermocycling were compared by using paired samples t tests (α=.05). RESULTS: All materials had their highest Ra values before polishing (P≤.011), while differences after polishing and after coffee thermocycling values were nonsignificant (P≥.140). PMMA had higher Ra than RCR before polishing (P=.002), and RCR had higher values than G-PMMA after polishing and after coffee thermocycling (P≤.023). RCR had the highest ΔE00 (P<.001). Polishing increased the b∗ values of PMMA, and coffee thermocycling increased the a∗ values of G-PMMA and all values of RCR (P≤.012). CONCLUSIONS: The tested materials had similar and acceptable surface roughness after polishing. The surface roughness of materials was not affected by coffee thermocycling. Considering the reported color thresholds, all materials had acceptable color change, but the computer-aided design and computer-aided manufacturing composite resin had perceptible color change after coffee thermocycling.

Translucency, color stability, and biaxial flexural strength of advanced lithium disilicate ceramic after coffee thermocycling.

OBJECTIVE: To compare the color stability, translucency, and biaxial flexural strength (BFS) of differently glazed advanced lithium disilicate (ALDS) with those of lithium disilicate (LDS) and zirconia-reinforced lithium silicate (ZLS) after coffee thermocycling. MATERIALS AND METHODS: Forty disk-shaped specimens were prepared from three lithium silicate based materials (CEREC Tessera, ALDS; IPS e.max CAD, LDS; Vita Suprinity, ZLS). ALDS specimens were divided into two subgroups according to glazing procedures (reduced glaze duration, ALDS-S and normal glaze duration, ALDS-N), while LDS and ZLS specimens were crystallized and glazed. Color coordinate measurements were performed before and after coffee thermocycling. Color differences (ΔE00 ) and relative translucency parameters (RTP) were calculated. Specimens were then subjected to BFS test. Statistical analysis was performed by using 1- (ΔE00 and BFS) and 2-way (RTP) ANOVA tests (α = 0.05). RESULTS: ΔE00 values of tested materials were similar (df = 3, F = 0.150, p = 0.929). Two-way ANOVA showed the significant effect of material type, coffee thermocycling, and the interaction between these parameters on RTP values (p < 0.001). Both before and after thermocycling, LDS had the highest (p ≤ 0.001) and ZLS had the lowest (p < 0.001) RTP values, while ALDS-N had higher RTP than ALDS-S (p ≤ 0.001). Among tested materials, only LDS had similar RTP values before and after thermocycling (p = 0.865) as the other materials had lower RTP values after thermocycling (p < 0.001). ALDS-N had higher BFS values than ALDS-S (p = 0.005), while LDS had similar values to ALDS specimens (p ≥ 0.201). ZLS had the highest BFS (p ≤ 0.007). CONCLUSIONS: ALDS had comparable values to those of other materials. However, reduced glazing duration resulted in decreased translucency and BFS of ALDS. CLINICAL SIGNIFICANCE: ALDS may be an appropriate restorative material for those patients with increased coffee consumption considering its color stability and ability to maintain translucency, particularly when glazed by using a conventional porcelain furnace.

Effect of Potassium Aluminum Sulfate Application on the Viability of Fibroblasts on a CAD-CAM Feldspathic Ceramic before and after Thermocycling.

Potassium aluminum sulfate (alum) is a known adjuvant, which has been used as a mordant in textile industry for color fixation. This material has potential to be incorporated into dentistry for color stability, yet its toxicity first needs to be evaluated. The present study aimed to evaluate the cytotoxic potential of potassium aluminum sulfate (alum) on fibroblasts when applied onto feldspathic ceramic before and after thermocycling. Forty-eight feldspathic ceramic specimens were divided into four groups (FC: no alum application or thermocycling; FCT: thermocycling without alum application; FA: alum application without thermocycling; FAT: alum application and thermocycling) (n = 12). Cell viability was assessed by using a tetrazolium salt 3-[4,5-dimethylthiazol-2-yl]-2,5-diphnyltetrazolium bromide assay at 24 and 72 h, and cell cultures without any ceramic specimens served as control (C). One sample from each material group was further analyzed with energy dispersive X-ray spectroscopy (EDX). Cell viability at different time intervals within each group was analyzed with Friedman tests, while Kruskal−Wallis tests were used to compare the test groups within each time interval. Pairwise comparisons were further resolved by using Wilcoxon tests (a = 0.05). C had lower (p = 0.01) and FA had higher (p = 0.019) cell viability after 72 h. After 24 h, the highest cell viability was observed in C (p ≤ 0.036). After 72 h, the differences between C and FA, C and FAT, FC and FA, and FCT and FAT were nonsignificant (p > 0.05). Cell viability was not affected by alum application or thermocycling at any time interval (p ≥ 0.631). EDX analysis showed an increase in potassium concentration in FA and FAT when compared with FC and FCT. Regardless of the time interval, alum application onto feldspathic ceramic and thermocycling did not influence the cell viability.

Effect of thickness, cement shade, and coffee thermocycling on the optical properties of zirconia reinforced lithium silicate ceramic.

OBJECTIVE: To investigate the effect of thickness, cement shade, and coffee thermocycling (CTC) on the optical properties of zirconia reinforced lithium silicate (ZLS) paired with different shades of a resin cement. MATERIALS AND METHODS: Thirty ZLS specimens were prepared in two different thicknesses (0.8 and 1.5 mm) and three different resin cement shades (Tr, A2, and A3) were applied (n = 5). Color determinations were done before and after 5000 CTC by using a noncontact spectroradiometer. Color change due to CTC and relative translucency parameter (RTP) before and after CTC were calculated by using CIEDE2000. Data were analyzed using ANOVA and Bonferroni-corrected t-tests(α = 0.05). RESULTS: Material thickness and resin cement shade (P < 0.001) affected baseline color. Material thickness affected color difference (P = 0.025). Thickness, resin cement shade, and CTC (P ≤ 0.0001) affected RTP. The difference between the color changes of the 0.8- and 1.5-mm specimens combined with A2 shade cement after CTC was significant (P = 0.01). RTPs of all pairs decreased after CTC (P < 0.001). CONCLUSIONS: Cement shade and material thickness affected the baseline color. The thickness of ZLS affected the color change after CTC only with A2 resin cement and the color change was less when the ZLS was thicker. CTC reduced the translucency of all pairs. CLINICAL SIGNIFICANCE: Clinicians and patients should be aware of a potential color change after long-term coffee consumption when zirconia reinforced lithium silicate is used particularly for laminate veneers with A2 shade of the tested resin cement.