Exploration of multifunctional properties of garlic skin derived cellulose nanocrystals and extracts incorporated chitosan biocomposite films for active packaging application.

For many years, garlic has been used as a condiment in food and traditional medicine. However, the garlic skin, which accounts for 25% of the garlic bulk, is considered agricultural waste. In this study, cellulose nanocrystals (CNCs) and garlic extract (GE) from garlic skin were isolated and used as fillers to manufacture biocomposite films. The films were characterized in terms of UV barrier, thermal, mechanical, biodegradability, and antimicrobial activity. The chitosan-containing films and CNCs have significantly improved the films' tensile strength, Young's modulus, and elongation but decreased the film transparency compared to chitosan films. The combination of the CNCs and GE, on the other hand, slightly reduced the mechanical properties. The addition of CNCs slightly decreased the film transparency, while the addition of GE significantly improved the UV barrier properties. Thermal studies revealed that the incorporation of CNC and GE had minimal effect on the thermal stability of the chitosan films. The degradability rate of the chitosan composite films was found to be higher than that of the neat chitosan films. The antimicrobial properties of films were studied against Escherichia coli, Streptomyces griseorubens, Streptomyces alboviridis, and Staphylococcus aureus, observing that their growth was considerably inhibited by the addition of GE in composite films. Films incorporating both CNCs and GE from garlic skin hold more promise for active food packaging applications due to a combination of enhanced physical characteristics and antibacterial activity.

Cellulose nanocrystals-filled poly (vinyl alcohol) nanocomposites as waterborne coating materials of NPK fertilizer with slow release and water retention properties.

Effective fertilizers management is essential for sustainable agricultural practices. One way to improve agronomic practices is by using slow-release fertilizers (SRF) that have shown interesting role in optimizing nutrients availability for plants growth. Considering the current ecological concerns, coated SRF using ecofriendly materials continue to attract great attention. In this context, novel waterborne and biodegradable coating nanocomposite formulations were elaborated from cellulose nanocrystals (CNC)-filled poly (vinyl alcohol) (PVA) for slow release NPK fertilizer with water retention property. CNC were extracted from hemp stalks using sulfuric acid hydrolysis process and their physico-chemical characteristics were investigated. CNC with various weight loadings (6, 10, 14.5 wt%) were incorporated into PVA polymer via solvent mixing method to produce viscous coating nanocomposite formulations with moderated shear viscosity. Uniform PVA@CNC coating microlayer was applied on the surface of NPK fertilizer granules in Wurster chamber of a fluidized bed dryer at controlled spraying and drying parameters. The nitrogen, phosphorus and potassium release profiles from coated NPK fertilizer were determined in water and soil. It was found that the coating materials extended the N-P-K nutrients release time from 3 days for uncoated fertilizer to 10 and 30 days for neat PVA- and CNC/PVA-coated fertilizer in soil medium, indicating the positive role of the presence of CNC in the PVA-based coatings. The morphology, coating rate and crushing strength of the as-prepared coated products were investigated in addition to their effect on water holding capacity and water retention of the soil. Enhanced crushing strength and water retention with a positive effect on the soil moisture were observed after coating NPK fertilizer, mainly with high CNC content (14.5 wt%). Therefore, these proposed nanocomposite coating materials showed a great potential for producing a new class of SRF with high nutrients use efficiency and water retention capacity, which could be beneficial to sustainable crop production.

Phosphoric acid-mediated green preparation of regenerated cellulose spheres and their use for all-cellulose cross-linked superabsorbent hydrogels.

With the growing environmental concerns and an emergent demand, a growing attention is turned to eco-friendly superabsorbent hydrogels instead of synthetic counterparts. Hydrogels based on cellulose derivatives can absorb and retain a huge amount of water in the interstitial sites of their structures, stimulating their uses in various useful industrial purposes. In this work, cross-linked superabsorbent composite hydrogel films (CHF) were designed, manufactured and characterized, by taking advantage of the combination of carboxymethyl cellulose (CMC), hydroxyethyl cellulose (HEC) and newly developed regenerated cellulose (RC) spheres. RC with sphere-like shape was successfully prepared using a green method based on cold phosphoric acid-mediated dissolution of microcrystalline cellulose (MCC) followed by regeneration process using water as anti-solvent. Prior to be used, the morphological and structural properties of RC spheres, with an average diameter of 477 ± 270 nm, were examined by SEM, AFM, XRD, FTIR and TGA techniques. CHF crosslinked with citric acid were, in fact, prepared by solvent casting method with different RC weight fractions (i.e. 0, 2.5, 5, 10 and 15 wt%), then the crosslinking reaction was triggered by thermal treatment at 80 °C during 8 h. Prepared CHF were then characterized in terms of their structural, thermal, tensile and transparency properties. Swelling tests were carried at three different aqueous media (i.e. with a pH = 3, 6.4 or 11) to evaluate the water retention capacity of hydrogel films, as well as, the pH effect on their swelling and hydrolytic degradation properties. Collected results reveal that CHF with low RC content (i.e. RC weight fraction of 2.5 or 5 wt%) have the best tensile and swelling properties, with a tensile strength and a swelling capacity (at pH = 6.4) up to 95 MPa and 4000%, respectively.

Sunflower oil cake-derived cellulose nanocrystals: Extraction, physico-chemical characteristics and potential application.

In this work, sunflower oil cake (SOC) was identified as bio-sourced material for cellulose nanocrystals (CNC) production using chemical treatments followed by sulfuric acid hydrolysis. The hydrolysis was performed at 64% acid concentration, a temperature of 50 °C and at two different hydrolysis times, 15 min (CNC15) and 30 min (CNC30). It was found that CNC exhibited a diameter of 9 ±â€¯3 nm and 5 ±â€¯2 nm, a length of 354 ±â€¯101 nm and 329 ±â€¯98 nm, a crystallinity of 75% and 87%, a surface charge density of ~1.57 and ~1.88 sulfate groups per 100 anhydroglucose units and a zeta potential value of -25.6 and -30.7 mV, for CNC15 and CNC30, respectively. The thermal degradation under nitrogen atmosphere started at 225 °C (CNC15), which is relatively higher than the temperature for sulfuric acid hydrolyzed CNC from other sources. Due to a high importance of CNC application in aqueous systems, the rheological behaviour of CNC suspensions at various concentrations was evaluated by the steady shear viscosity measurements and the oscillatory dynamic tests. The results showed that the CNC suspensions exhibited a gel-like behaviour at very low CNC concentrations (0.1-1%) wherein a strong CNC entangled network is formed. Polymer nanoreinforcing capability of the newly produced CNC was also investigated in this study. CNC filled PVA nanocomposite films were produced at various CNC contents (1, 3, 5 and 8 wt%) and their mechanical and transparency properties were investigated, resulting in transparent nanocomposite materials with strong mechanical properties. The study suggested other possibilities to utilize agricultural wastes from SOC for CNC production with potential application as reinforcement in polymer nanocomposites.