Enhanced permeability, selectivity, and antifouling ability of CNTs/Al2O3 membrane under electrochemical assistance.

Membrane filtration provides effective solutions for removing contaminants, but achieving high permeability, good selectivity, and antifouling ability remains a great challenge for existing membrane filtration technologies. In this work, membrane filtration coupled with electrochemistry has been developed to enhance the filtration performance of a CNTs/Al2O3 membrane. The as-prepared CNTs/Al2O3 membrane, obtained by coating interconnected CNTs on an Al2O3 substrate, presented good pore-size tunability, mechanical stability, and electroconductivity. For the removal of a target (silica spheres as a probe) with a size comparable to the membrane pore size, the removal efficiency and flux at +1.5 V were 1.1 and 1.5 times higher, respectively, than those without electrochemical assistance. Moreover, the membrane also exhibited a greatly enhanced removal efficiency for contaminants smaller than the membrane pores, providing enhancements of 4 orders of magnitude and a factor of 5.7 for latex particles and phenol, respectively. These results indicated that both the permeability and the selectivity of CNTs/Al2O3 membranes can be significantly improved by electrochemical assistance, which was further confirmed by the removal of natural organic matter (NOM). The permeate flux and NOM removal efficiency at +1.5 V were about 1.6 and 3.0 times higher, respectively, than those without electrochemical assistance. In addition, the lost flux of the fouled membrane was almost completely recovered by an electrochemically assisted backwashing process.

Performing a microfiltration integrated with photocatalysis using an Ag-TiO(2)/HAP/Al(2)O(3) composite membrane for water treatment: Evaluating effectiveness for humic acid removal and anti-fouling properties.

Membrane filtration has been increasingly used for water treatment and wastewater reclamation in recent years. To further improve the effectiveness of membrane process and reduce membrane fouling, a highly reactive photocatalytic membrane, Ag-TiO(2)/hydroxiapiate (HAP, Ca(10)(PO(4))(6)(OH)(2))/Al(2)O(3), was employed to realize microfiltration (MF) coupling photocatalysis for surface water treatment. The effectiveness on the potential of membrane was investigated by removing humic acid (HA) test under different feed total organic carbon (TOC), light intensity and transmembrane pressure (TMP). The HA removal and anti-fouling property of as-prepared membrane was improved under UV irradiation, likely due to photocatalytic degradation of foulants along with filtration simultaneously. Under given feed water composition, increasing the light intensity resulted in increased removal of HA from aqueous solution. However, a limiting TMP seems to exist beyond which the increased HA removal cannot be sustained. Fouling behavior analysis indicated that the transition in fouling mode from initial pore blocking to cake filtration occurred much slower as UV irradiated. Furthermore, a superior efficiency on removal of trace organic contaminants, as well as milder flux reduction, was presented from surface water treatment, which demonstrated that the integrated system with enhanced performance is foreseen as an emerging technique for water treatment.