Anti-Inflammatory and Protective Effects of Juncus effusus L. Water Extract on Oral Keratinocytes.

Periodontitis is a chronic inflammatory disease caused by periodontopathogenic bacteria that form biofilms in periodontal pockets. The gingival epithelium acts as the first physical barrier in fighting attacks by periodontopathogenic pathogens, such as the primary etiological agent Porphyromonas gingivalis, and various exogenous chemicals, as well as regulates the local innate immune responses. Therefore, the development of novel oral care products to inhibit inflammatory reactions caused by bacterial infection and protect the gingival epithelium is necessary. Juncus effusus L. has generally been used as an indigenous medicine, such as a diuretic, an antipyretic, and an analgesic, in ancient practice. In this study, we examined the effects of a water extract from J. effusus L. on the inhibition of the inflammatory reaction elicited by bacterial infection and protection of the oral epithelium by chemical irritation. Pretreatment of oral epithelial cells with the water extract from J. effusus L. significantly reduced P. gingivalis or its lipopolysaccharide- (LPS-) mediated production of chemokines (interleukin-8 and C-C-chemokine ligand20) in a concentration-dependent manner with comparable to or greater effects than epigallocatechin gallate and protected oral epithelial cells from injury by chemical irritants, cetylpyridinium chloride, and benzethonium chloride. Moreover, the water extract from J. effusus L. in the presence of antimicrobial agents or antifibrinolytics already used as ingredients in mouthwash could significantly reduce the production of chemokines from P. gingivalis LPS-stimulated oral epithelial cells in a concentration-dependent manner. These findings suggest that the water extract from J. effusus L. is potentially useful for oral care to prevent oral infections, such as periodontal infections, and maintain oral epithelial function.

Effect of single-liquid acidic primers on bonding of a composite luting agent joined to a prefabricated alumina coping material.

PURPOSE: The aim of this study was to assess the effect of acidic primers on adhesive bonding to prefabricated alumina material designed for fixed restorations. METHODS: High-purity alumina disks (Procera AllCeram) were primed with one of the following materials: Acryl Bond, All Bond II Primer B, Alloy Primer, Estenia Opaque Primer, M.L. Primer, MR. Bond, and Super- Bond Liquid. The specimens were bonded with a dualpolymerizing luting composite (Variolink II). Unprimed specimen was prepared as the control. Bond strengths were determined both before and after thermocycling. RESULTS: Average bond strength before thermocycling ranged from 12.0 to 39.1 MPa, whereas average bond strength after thermocycling varied from 0.0 to 26.9 MPa. The statistically highest post-thermocycling bond strength was obtained with the use of the Alloy Primer, Estenia Opaque Primer, and M.L. Primer agents. CONCLUSION: It can be concluded that the use of either the Estenia or Alloy Primer material, which contain 10- methacryloyloxydecyl dihydrogen phosphate (MDP), or the M.L. Primer, which contains 6-methacryloyloxyhexyl phosphonoacetate (6-MHPA), is recommended for bonding the Procera alumina copings with the Variolink II composite.

Effects of alumina air-abrasion and acidic priming agents on bonding between SUS XM27 steel and auto-polymerizing acrylic resin.

The purpose of this study was to evaluate the effects of functional monomers contained in the primers, as well as alumina particle abrasion on bonding between stainless steel and acrylic resin. SUS XM27 steel was primed with one of the following materials; Alloy Primer, Estenia Opaque Primer, M. L. Primer, and Super-Bond Liquid. Steel disks were either ground flat or alumina-blasted, primed with one of the four agents, and bonded with an acrylic resin (Unifast Trad). Bond strength was determined both before and after thermocycling (2,000 or 20,000 cycles). Among the four priming agents, the Alloy Primer and Estenia Opaque Primer, both of which contain 10-methacryloyloxydecyl dihydrogen phosphate (MDP), exhibited better bonding performance than the others. Alumina air-borne particle abrasion considerably improved the durability of bonding between the steel and the resin material. It can be concluded that alumina blasting followed by priming with an MDP agent is recommended for bonding the resin and SUS XM27 steel.

Effect of single-liquid priming agents on adhesive bonding to aluminum oxide of a methacrylic resin.

The purpose of this study was to evaluate the effects of acidic primers on adhesive bonding to sintered aluminum oxide (alumina). Alumina disks were primed with one of the following materials: Acryl Bond, All Bond 2 Primer B, Alloy Primer, Estenia Opaque Primer, Eye Sight Opaque Primer, M.L. Primer, MR. Bond, and Super-Bond Liquid. Specimens were then bonded with an acrylic resin initiated with partially oxidized tri-n-butylborane (TBBO), and bond strengths were determined. Unprimed specimen was employed as the control. Average bond strength before thermocycling ranged from 20.5 to 41.9 MPa, whereas post-thermocycling bond strength ranged from 0.0 to 40.0 MPa. Of the eight primers, Estenia Opaque Primer and Alloy Primer showed better adhesive performance than the other materials. It could thus be concluded that either Estenia Opaque Primer or Alloy Primer--which contained an adhesive monomer, 10-methacryloyloxydecyl dihydrogen phosphate (MDP)--was recommended for bonding alumina with TBBO-initiated resin.