RESUMO
BACKGROUND: Oral care products containing bioactive agents obtained from extracts of plant drugs were launched. This in vitro study investigated the effects of herbal-containing toothpastes associated or not with fluoride to remineralize the enamel after cariogenic challenge with pH cycling. The chemical and physical factors of toothpastes and the enamel surface roughness after brushing were also analyzed. MATERIAL AND METHODS: Sixty bovine enamel blocks were obtained and divided into 3 thirds: intact (untreated), demineralized (artificial caries lesion), and treated (caries lesion, pH cycling, and brushing with toothpastes). Toothpastes containing herbal compounds contained no fluoride [Galla chinensis (GCH)], low-F concentration [D'Or (DOR); Herbal Bliss (HBL)], or a different fluoride type [Elmex Anticaries (EAC)]. The results were compared to NaF-containing toothpastes: 1450 and 5000 ppm. Enamel blocks were brushed with the toothpastes using a pH-cycling model (7 days). The Knoop hardness (25g/10s) of the surface and the longitudinal sections were then evaluated. The percentage of surface hardness recovery (%SHR) was calculated. The enamel surface roughness, pH, particle size, zeta potential, and polydispersity index of toothpaste slurries were also evaluated. Data were statistically analyzed (α=5%). RESULTS: No significance was observed when %SHR was compared (p>0.05). DOR, GCH, and HBL were more effective in remineralizing the enamel subsurface. Significantly higher surface roughness was observed when treated with EAC and GCH (p<0.05). CONCLUSIONS: All toothpastes were able to remineralize the enamel, especially the subsurface, with results equal or better than that of standard toothpastes. Key words:Enamel, hardness, roughness, toothpaste, tooth remineralization.
RESUMO
OBJECTIVE: This in vitro study evaluated the influence of bioactive plant extracts as dentin biomodifying agents to improve the longevity of bonded restorations. For that, plant extracts were applied to the dentin surface prior to the adhesive system. MATERIALS AND METHODS: Bovine incisors were ground flat to obtain 2 mm thick slices in which conical preparations were made (N = 10). Tannin-containing plant extracts were applied to dentin before the application of the restorative system, as follows: control group (untreated, CTL), chlorhexidine 0.12% (CHX), mastruz (Dysphania ambrosioides, MTZ), cat's claw (Uncaria tomentosa, CTC), guarana (Paullinia cupana, GUA), galla chinensis (Rhus chinensis, GCH), and tannic acid (extracted from Acacia decurrens, TNA). The push-out bond strength test was conducted (0.5 mm/min). Dentin biomodification was assessed by the modulus of elasticity and mass change in bovine tooth sections (0.5 × 1.7 × 7.0 mm). The dentin staining after extract treatments of dentin slices was compared. The dentin surface wettability was also evaluated by means of the contact angles of the adhesive system with the dentin surface and compared with the untreated control group. Data were subjected to ANOVA/Tukey's test (α = 0.05). RESULTS: The bond strength of the restoratives to dentin was not significantly improved by the plant extracts, irrespective of the evaluation time (p > 0.05). Except for TNA, the elastic modulus of demineralized dentin significantly reduced after treatment with the plant extracts (p < 0.05). The dentin staining correlated with the tannin content of the extracts. The contact angle was significantly reduced when treated with CTC, GCH, and TNA. CONCLUSIONS: The tannin-containing extracts had a questionable effect on the longevity of bonded restorations. The dentin modulus was negatively affected by the extract treatments. Although some of the extracts changed the contact angle, which seems to improve the adhesive monomer permeation, the tannin-rich plant extract application prior to adhesive application was proven to be clinically unfeasible due to dentin staining.