RESUMO
The present study aimed to assess the effects of low-level laser therapy (GaAlAs) on the bone repair process within titanium scaffolds in the femurs of healthy and osteoporotic rats. Fifty-six rats were divided into four groups: group Sh: SHAM animals that received scaffolds; group LSh: SHAM animals that received scaffolds and were subjected to laser therapy; group OV: ovarietomized (OVX) animals that received scaffolds; and group LOV: OVX animals that received scaffolds and were subjected to laser therapy. Thirty days following ovariectomy or sham surgery, scaffolds were implanted in the left femurs of all animals in the study. Immediately after opening the surgical site, the inner part of the surgical cavity was stimulated with low-level laser (GaAlAs). In addition to this procedure, the laser group was also subjected to sessions of low-level laser therapy (LLLT) at 48-h intervals, with the first session performed immediately after surgery. The rats were sacrificed at 2 and 6 weeks, time in which femur fragments were submitted for histological and histomorphometric examination, and skin tissue above the scaffold was submitted to histological analysis. At the end of the study, greater bone formation was observed in the animals submitted to LLLT. At 2 and 6 weeks, statistically significant differences were observed between LSh and Sh groups (p = 0.009 and 0.0001) and LOV and OV (p = 0.0001 and 0.0001), respectively. No statistical difference was observed when assessing the estrogen variable. On the basis of our methodology and results, we conclude that LLLT improves and accelerates bone repair within titanium scaffolds in both ovariectomized and healthy rats, when compared to animals not subjected to radiation.
Assuntos
Terapia com Luz de Baixa Intensidade/métodos , Osteogênese/efeitos da radiação , Alicerces Teciduais/química , Titânio/química , Cicatrização/efeitos da radiação , Animais , Feminino , Fêmur , Ovariectomia , Distribuição Aleatória , Ratos , Ratos WistarRESUMO
The study investigates the influence of low-level laser therapy (LLLT) on bone healing in the femur of osteopenic and normal rats with titanium implants. Ovariectomy and control group were randomly submitted to LLLT, which was applied by gallium-aluminum-arsenium (GaAlAs) laser at the surgical site before and after placing the implant, for seven times. Histomorphometric and statistical analysis were performed. Most irradiated groups showed higher values than the nonirradiated groups. The GaAlAs infrared diode laser may improve the osseointegration process in osteopenic and normal bone, particularly based on its effects in the initial phase of bone formation.
Assuntos
Doenças Ósseas Metabólicas/fisiopatologia , Doenças Ósseas Metabólicas/radioterapia , Fêmur/efeitos da radiação , Terapia com Luz de Baixa Intensidade/métodos , Osteogênese/efeitos da radiação , Titânio , Animais , Substitutos Ósseos , Feminino , Lasers Semicondutores/uso terapêutico , Terapia com Luz de Baixa Intensidade/instrumentação , Osseointegração , Ovariectomia , Ratos , Cicatrização/efeitos da radiaçãoRESUMO
PURPOSE: To evaluate the effect of the opaque layer firing temperature and mechanical and thermal cycling on the flexural strength of a ceramic fused to commercial cobalt-chromium alloy (Co-Cr). The hypotheses were that higher opaque layer temperatures increase the metal/ceramic bond strength and that aging reduces the bond strength. MATERIALS AND METHODS: Metallic frameworks (25 x 3 x 0.5 mm(3); ISO 9693) (N = 60) were cast in Co-Cr and airborne-particle abraded (Al(2)O(3): 150 mum) at the central area of the frameworks (8 x 3 mm(2)) and divided into three groups (N = 20), according to the opaque layer firing temperature: Gr1 (control)-900 degrees C; Gr2-950 degrees C; Gr3-1000 degrees C. The opaque ceramic (Opaque, Vita Zahnfabrick, Bad Säckingen, Germany) was applied, and the glass ceramic (Vita Omega 900, Vita Zahnfabrick) was fired onto it (thickness: 1 mm). While half the specimens from each group were randomly tested without aging (water storage: 37 degrees C/24 hours), the other half were mechanically loaded (20,000 cycles; 50 N load; distilled water at 37 degrees C) and thermocycled (3000 cycles; 5 degrees C to 55 degrees C, dwell time: 30 seconds). After the flexural strength test, failure types were noted. The data were analyzed using 2-way ANOVA and Tukey's test (alpha= 0.05). RESULTS: Gr2 (19.41 +/- 5.5 N) and Gr3 (20.6 +/- 5 N) presented higher values than Gr1 (13.3 +/- 1.6 N) (p= 0.001). Mechanical and thermal cycling did not significantly influence the mean flexural strength values (p > 0.05). Increasing the opaque layer firing temperature improved the flexural bond strength values (p < 0.05). The hypotheses were partially accepted. CONCLUSION: Increasing of the opaque layer firing temperature improved the flexural bond strength between ceramic fused to Co-Cr alloy.
Assuntos
Ligas de Cromo/química , Colagem Dentária , Porcelana Dentária/química , Ligas Metalo-Cerâmicas/química , Óxido de Alumínio/química , Cerâmica/química , Corrosão Dentária , Temperatura Alta , Humanos , Teste de Materiais , Maleabilidade , Estresse Mecânico , Propriedades de Superfície , Temperatura , Fatores de Tempo , Água/químicaRESUMO
The aim of this study was to investigate, by means of histological and histomorphometric analysis, the effects of 24% ethylenediaminetetraacetic acid (EDTA) gel in periodontal tissue when used in combination with conventional periodontal treatment. Periodontitis was induced in the 2nd upper left permanent molars of 45 male Wistar rats by means of ligature. After 5 weeks, this was removed and debridement was performed. The animals were then randomly divided into 3 groups; group 1: mechanical treatment, group 2: mechanical treatment and EDTA gel application for 2 min, and group 3: mechanical treatment and placebo gel application for 2 min. After the treatment, rinsing was done with 0.9% saline solution for 1 min in all cases, followed by root notching in the deepest part of the pocket. After 4, 10, and 28 days the animals were sacrificed. The averages obtained were evaluated by means of test two-way analysis of variance (ANOVA) and Tukey statistical tests (P < 0.05). The results showed that with respect to the type of treatment employed, there were no statistically significant differences in the vitality of the periodontal tissue. It was concluded that 24% EDTA gel did not interfere with periodontal tissue repair when used in combination with conventional periodontal treatment.