Biosynthesis of nano bimetallic Ag/Pt alloy from Crocus sativus L. extract: Biological efficacy and catalytic activity.

In this project, silver­platinum (AgPt) nanoparticles were prepared by using the Crocus sativus L. plant ethanolic extract. The AgPt nanoparticles were characterized by applying the various method as ultraviolet-visible and infrared spectroscopy, electron microscopy, and X-ray diffraction analysis. The morphology structural indicated that the AgPt nanoparticles were spherical particles with diameter about 36.0 nm. The FTIR spectroscopy shows the efficient stabilization of the AgPt nanoparticles by phytoconstituents. The Ag and AgPt nanoparticles have polyphenolic content, lower than the flavonoids and proanthocyanins contents. The AgPt nanoparticles depicted the highest antioxidant properties compared to the Ag nanoparticles and ascorbic acid. The results showed that the AgPt nanoparticles had a high antioxidant properties. In addition, the AgPt nanoparticles demonstrated the substantial antimicrobial and cytotoxic activities against pathogenic microbes and MCF-7 breast cancer cell line. The environmental chemistry analysis depicts that methyl orange can be degraded from water by catalytic degradation process with sodium borohydride. The AgPt nanoparticles were prosperous in catalytic degrading methyl orange following a first order kinetic model.

Inorganic Nanoshell-Stabilized Liquid Metal for Targeted Photonanomedicine in NIR-II Biowindow.

Gallium and gallium-based alloys, typical types of liquid metals with unique physiochemical properties, are emerging as a next generation of functional materials in versatile biomedical applications. However, the exploration of their biomedical performance is currently insufficient, and their intrinsic low oxidative resistance is a key factor blocking their further clinical translation. Herein, we report on the surface engineering of liquid metal-based nanoplatforms by an inorganic silica nanoshell based on a novel but facile sonochemical synthesis for highly efficient, targeted, and near-infrared (NIR)-triggered photothermal tumor hyperthermia in the NIR-II biowindow. The inorganic silica-shell engineering of liquid metal significantly enhances the photothermal performance of the liquid metal core as reflected by enhanced NIR absorption, improved photothermal stability by oxidation protection, and abundant surface chemistry for surface-targeted engineering to achieve enhanced tumor accumulation. Systematic in vitro cell-level evaluation and in vivo tumor xenograft assessment demonstrate that (Arg-Gly-Asp) RGD-targeted and silica-coated nanoscale liquid metal substantially induces phototriggered cancer-cell death and photothermal tumor eradication, accompanied by high in vivo biocompatibility and easy excretion out of the body. This work provides the first paradigm for surface-inorganic engineering of liquid metal-based nanoplatforms for achieving multiple desirable therapeutic performances, especially for combating cancer.

In vitro biocompatibility and electrical stability of thick-film platinum/gold alloy electrodes printed on alumina.

OBJECTIVE: High-density electrode arrays are a powerful tool in both clinical neuroscience and basic research. However, current manufacturing techniques require the use of specialised techniques and equipment, which are available to few labs. We have developed a high-density electrode array with customisable design, manufactured using simple printing techniques and with commercially available materials. APPROACH: Electrode arrays were manufactured by thick-film printing a platinum-gold alloy (Pt/Au) and an insulating dielectric on 96% alumina ceramic plates. Arrays were conditioned in serum and serum-free conditions, with and without 1 kHz, 200 µA, charge balanced stimulation for up to 21 d. Array biocompatibility was assessed using an extract assay and a PC-12 cell contact assay. Electrode impedance, charge storage capacity and charge injection capacity were before and after array conditioning. MAIN RESULTS: The manufactured Pt/Au electrodes have a highly porous surface and exhibit electrical properties comparable to arrays manufactured using alternative techniques. Materials used in array manufacture were found to be non-toxic to L929 fibroblasts by extract assay, and neuronal-like PC-12 cells adhered and extended neurites on the array surfaces. Arrays remained functional after long-term delivery of electrical pulses while exposed to protein-rich environments. Charge storage capacities and charge injection capacities increased following stimulation accounted for by an increase in surface index (real surface area) observed by vertical scanning interferometry. Further, we observed accumulation of proteins at the electrode sites following conditioning in the presence of serum. SIGNIFICANCE: This study demonstrates the in vitro biocompatibility of commercially available thick-film printing materials. The printing technique is both simple and versatile, with layouts readily modified to produce customized electrode arrays. Thick-film electrode arrays are an attractive tool that may be implemented for general tissue engineering and neuroscience research.

Green synthesis of silver and copper nanoparticles using ascorbic acid and chitosan for antimicrobial applications.

Silver and copper nanoparticles were produced by chemical reduction of their respective nitrates by ascorbic acid in the presence of chitosan using microwave heating. Particle size was shown to increase by increasing the concentration of nitrate and reducing the chitosan concentration. Surface zeta potentials were positive for all nanoparticles produced and these varied from 27.8 to 33.8 mV. Antibacterial activities of Ag, Cu, mixtures of Ag and Cu, and Ag/Cu bimetallic nanoparticles were tested using Bacillus subtilis and Escherichia coli. Of the two, B. subtilis proved more susceptible under all conditions investigated. Silver nanoparticles displayed higher activity than copper nanoparticles and mixtures of nanoparticles of the same mean particle size. However when compared on an equal concentration basis Cu nanoparticles proved more lethal to the bacteria due to a higher surface area. The highest antibacterial activity was obtained with bimetallic Ag/Cu nanoparticles with minimum inhibitory concentrations (MIC) of 0.054 and 0.076 mg/L against B. subtilis and E. coli, respectively.

Facile synthesis of pentacle gold-copper alloy nanocrystals and their plasmonic and catalytic properties.

The combination of gold and copper is a good way to pull down the cost of gold and ameliorate the instability of copper. Through shape control, the synergy of these two metals can be better exploited. Here, we report an aqueous phase route to the synthesis of pentacle gold-copper alloy nanocrystals with fivefold twinning, the size of which can be tuned in the range from 45 to 200 nm. The growth is found to start from a decahedral core, followed by protrusion of branches along twinning planes. Pentacle products display strong localized surface plasmon resonance peaks in the near-infrared region. Under irradiation by an 808-nm laser, 70-nm pentacle nanocrystals exhibit a notable photothermal effect to kill 4T1 murine breast tumours established on BALB/c mice. In addition, 70-nm pentacle nanocrystals show better catalytic activity than conventional citrate-coated 5-nm Au nanoparticles towards the reduction of p-nitrophenol to p-aminophenol by sodium borohydride.

Rapid efficient synthesis and characterization of silver, gold, and bimetallic nanoparticles from the medicinal plant Plumbago zeylanica and their application in biofilm control.

BACKGROUND: Nanoparticles (NPs) have gained significance in medical fields due to their high surface-area-to-volume ratio. In this study, we synthesized NPs from a medicinally important plant - Plumbago zeylanica. MATERIALS AND METHODS: Aqueous root extract of P. zeylanica (PZRE) was analyzed for the presence of flavonoids, sugars, and organic acids using high-performance thin-layer chromatography (HPTLC), gas chromatography-time of flight-mass spectrometry (GC-TOF-MS), and biochemical methods. The silver NPs (AgNPs), gold NPs (AuNPs), and bimetallic NPs (AgAuNPs) were synthesized from root extract and characterized using ultraviolet-visible spectra, X-ray diffraction (XRD), energy-dispersive spectrometry (EDS), transmission electron microscopy (TEM), and dynamic light scattering (DLS). The effects of these NPs on Acinetobacter baumannii, Staphylococcus aureus, and Escherichia coli biofilms were studied using quantitative biofilm inhibition and disruption assays, as well as using fluorescence, scanning electron microscopy, and atomic force microscopy. RESULTS: PZRE showed the presence of phenolics, such as plumbagin, and flavonoids, in addition to citric acid, sucrose, glucose, fructose, and starch, using HPTLC, GC-TOF-MS, and quantitative analysis. Bioreduction of silver nitrate (AgNO3) and chloroauric acid (HAuCl4) were confirmed at absorbances of 440 nm (AgNPs), 570 nm (AuNPs), and 540 nm (AgAuNPs), respectively. The maximum rate of synthesis at 50°C was achieved with 5 mM AgNO3 within 4.5 hours for AgNPs; and with 0.7 mM HAuCl4 within 5 hours for AuNPs. The synthesis of AgAuNPs, which completed within 90 minutes with 0.7 mM AgNO3 and HAuCl4, was found to be the fastest. Fourier-transform infrared spectroscopy confirmed bioreduction, while EDS and XRD patterns confirmed purity and the crystalline nature of the NPs, respectively. TEM micrographs and DLS showed about 60 nm monodispersed Ag nanospheres, 20-30 nm Au nanospheres adhering to form Au nanotriangles, and about 90 nm hexagonal blunt-ended AgAuNPs. These NPs also showed antimicrobial and antibiofilm activity against E. coli, A. baumannii, S. aureus, and a mixed culture of A. baumannii and S. aureus. AgNPs inhibited biofilm in the range of 96%-99% and AgAuNPs from 93% to 98% in single-culture biofilms. AuNPs also showed biofilm inhibition, with the highest of 98% in S. aureus. AgNPs also showed good biofilm disruption, with the highest of 88% in A. baumannii. CONCLUSION: This is the first report on rapid and efficient synthesis of AgNPs, AuNPs and AgAuNPs from P. zeylanica and their effect on quantitative inhibition and disruption of bacterial biofilms.

Optical properties and exciton dynamics of alloyed core/shell/shell Cd(1-x)Zn(x)Se/ZnSe/ZnS quantum dots.

In this study we introduce a new method for the one-pot synthesis of core/shell/shell alloyed Cd1-xZnxSe/ZnSe/ZnS QDs and examine the effect of the shell coating on the optical properties and exciton dynamics of the alloy core. The photoluminescence (PL) quantum yield is greatly enhanced after shell growth, from 9.6% to 63%. The exciton dynamics were studied by time correlated single photon counting (TCSPC) and fit using integrated singular value decomposition global fitting (i-SVD-GF), which showed the biexponential observed lifetimes on the nanosecond time scale remain the same after shell growth. Using ultrafast transient absorption (TA) spectroscopy and SVD-GF, we have determined that surface passivation by ZnSe and ZnSe/ZnS shells reduces nonradiative recombination primarily on the picosecond time scale. These findings are helpful in directing the development of the next generation of QDs for biological labeling and other applications.

Synthesis of PbSeTe single ternary alloy and core/shell heterostructured nanocubes.

We report a robust method for synthesis of monodisperse PbSeTe single ternary alloy and core/shell heterostructured nanocubes, respectively. The key synthetic strategy to produce such different classes of nanocubes is to precisely control the time of reaction and successive growth. The crystallinity, shape/size distributions, structural characteristics, and compositions of as-prepared nanocubes, both ternary alloy and core/shell, were carefully studied. A plausible growth mechanism for developing each type of lead chalcogenide nanocubes is proposed. These delicately designed PbSeTe nanoscale architectures offer tunable compositions in PbSeTe ternary alloy and nano-interfaces in core/shell nanocubes, which are the critical factors in controlling thermal conductivity for applications in thermoelectrics.

Large scale synthesis of stable tricolor Zn(1-x)Cd(x)Se core/multishell nanocrystals via a facile phosphine-free colloidal method.

Here we report a new "green" method to synthesize Zn(1-x)Cd(x)Se (x = 0-1) and stable red-green-blue tricolor Zn(1-x)Cd(x)Se core/shell nanocrystals using only low cost, phosphine-free and environmentally friendly reagents. The first excitonic absorption peak and photoluminescence (PL) position of the Zn(1-x)Cd(x)Se nanocrystals (the value of x is in the range 0.005-0.2) can be fixed to any position in the range 456-540 nm. There is no red or blue shift in the entire reaction process. Three similar sizes of alloyed Zn(1-x)Cd(x)Se nanocrystals with blue, green, and yellow emissions were successfully selected as cores to synthesize high quality blue, green, and red core/shell nanocrystal emitters. For the synthesis of core/shell nanocrystals with a high quantum yield (QY) and stability, the selection of shell materials has been proven to be very important. Therefore, alternative protocols have been used to optimize thick shell growth. ZnSe/ZnSe(x)S(1-x) and CdS/Zn(1-x)Cd(x)S have been found as an excellent middle multishell to overcoat between the alloyed Zn(1-x)Cd(x)Se core and ZnS outshell. The QYs of the as-synthesized core/shell alloyed Zn(1-x)Cd(x)Se nanocrystals can reach 40-75%. The Cd content is reduced to less than 0.1% for Zn(1 -x)Cd(x)Se core/shell nanocrystals with emissions in the range 456-540 nm. More than 15 g of high quality Zn(1-x)Cd(x)Se core/shell nanocrystals were prepared successfully in a large scale, one-pot reaction. Importantly, the emissions of such thick multishell nanocrystals are not susceptible to ligand loss and stability in various physiological conditions.

Preparation and bioapplication of high-quality, water-soluble, biocompatible, and near-infrared-emitting CdSeTe alloyed quantum dots.

A facile method is developed for the preparation of high-quality, water-soluble, and near-infrared (NIR)-emitting CdSeTe alloyed quantum dots (AQdots) with L-cysteine as the capping agent. By changing the size and the composition of AQdots the photoluminescent quantum yield (QY) can reach as high as 53% and the emission color can be tuned between visible and NIR regions (580-814 nm). Furthermore, the prepared NIR-emitting AQdots have been successfully applied for HL-60 cell imaging and glucose and cholesterol assay, which demonstrates the great potential of the AQdots for biological applications.

Synthesis of nanocrystalline (Co, Ni)Al2O4 spinel powder by mechanical milling of quasicrystalline materials.

In the present study, attempts have been made to synthesize the nano-crystalline (Co, Ni)Al2O4 spinel powders by ball milling and subsequent annealing. An alloy of Al70Co15Ni15, exhibiting the formation of a complex intermetallic compound known as decagonal quasicrystal is selected as the starting material for mechanical milling. It is interesting to note that this alloy is close to the stoichiometry of aluminum and transition metal atoms required to form the aluminate spinel. The milling was carried out in an attritor mill at 400 rpm for 40 hours with ball to powder ratio of 20 : 1 in hexane medium. Subsequent to this annealing was performed in an air ambience for 10, 20, and 40 h at 600 degrees C in side the furnace in order to oxidize the decagonal phase and finally to form the spinel structure. The X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the formation of nano-sized decagonal phase after milling and then (Co, Ni)Al2O4 spinel type phase after annealing. The XRD studies reveal the lattice parameter to be 8.075 angstroms and the lattice strain as 0.6%. The XRD and TEM explorations of spinel phase indicate the average grain size to be approximately 40 nm.

Structural study of Cu(2-x)Se alloys produced by mechanical alloying.

The crystalline structures of the superionic high-temperature copper selenides Cu(2-x)Se (0 < x < 0.25) produced using mechanical alloying were investigated using X-ray diffraction (XRD). The measured XRD patterns showed the presence of peaks corresponding to the crystalline superionic high-temperature alpha-Cu(2)Se phase in the as-milled sample, and its structural data were determined by means of a Rietveld refinement procedure. After heat treatment in argon at 473 K for 90 h, this phase transforms to the superionic high-temperature alpha-Cu(1.8)Se phase, whose structural data were also determined by Rietveld refinement. In this phase, a very low occupation of the trigonal 32(f) sites ( approximately 3%) by Cu ions is found. In order to explain the evolution of the phases in the samples, two possible mechanisms are suggested: (i). the high mobility of Cu ions in superionic phases and (ii). the important diffusive processes in the interfacial component of samples produced by mechanical alloying.